[Restoration of composite on etched stainless steel crowns. (1)].
Object of investigation The retention of composite resin to etched stainless steel crowns was tested as a possible method for restoring primary anterior teeth. Method employed 1) SEM observation Stainless steel crowns (Sankin Manufacture Co.) were etched with an aqua resia to create surface roughness and undercut to retain the composite resin to the crowns. Etching times were 1, 2, 3, 5, 8, 10 and 20 minutes, then washed in a 70% alcohol solution using an ultrasonic washer and dried. A total of 96 etched samples and non etched control samples were observed through the scanning electron microscope (Hitachi 520). 2) Shear bond strength test Stainless steel crowns were etched in an aqua resia from 1 to 20 minutes, then washed and dried. Composite resin (Photo Clearfil A, Kuraray Co.) with the bonding agent was placed on the crowns and the shear bond strength was tested in 56 samples using an Autograph (DCS-500, Shimazu). Results 1) SEM observation showed that the etching surface of stainless steel crowns created surface roughness and undercut. The most desirable surface was obtained in the 3 to 5 minute etching time specimens. 2) The highest bond strength was obtained in a 3 minute etching specimen. It was 42.12 MPa, although 29.26 MPa in mean value. Conclusion Etching with an aqua resia increased the adherence of composite resin to the surface of stainless steel crowns.
Goto
G
G
Department of Pediatric Dentistry, Nagasaki University School of Dentistry.
Zang
Y
Y
Hosoya
Y
Y
D003188:Composite Resins; D003442:Crowns; D001840:Dental Bonding; D006851:Hydrochloric Acid; D009566:Nitrates; D017942:Nitric Acid; D013193:Stainless Steel; D013499:Surface Properties
D003188:Composite Resins; D009566:Nitrates; D013193:Stainless Steel; D017942:Nitric Acid; D006851:Hydrochloric Acid; C022102:aqua regia