[The surface degradation of various light-cured composite resins by thermal cycling].
The durability of four commercially available light-cured composite resins was investigated by thermal cycling, GR containing inorganic fillers treated with the graft polymerization of acryl ester, LF inorganic fillers treated with a silane coupling agent, PC silanized inorganic fillers and organic composite fillers, and the MFR-type SI containing the organic composite fillers. These materials were given 10,000, 30,000 and 50,000 thermal cycles (4 degrees C-60 degrees C) and the deterioration of materials by thermal cycling was evaluated by the measurement of the mechanical properties and the SEM observations of the surface of the thermocycled materials. Compressive strength and bending elastic moduli for all materials did not change greatly by thermal cycling. However, bending strength, toothbrush abrasion resistance and surface hardness decreased with increasing number of thermal cycles between 0 and 30,000, and changed little after 30,000 cycles. The percentage of bending strength after 50,000 thermal cycles to that of the non-thermocycled sample was 75% for GR, 60% for LF, 50% for PC and 65% for SI, respectively. Deterioration of materials was observed as cracks on the surface, which generated at the interface of the filler and matrix. The cracks generated relatively earlier during thermal cycling for SI and PC which contained the organic composite filler, later for LF which contained the silanized inorganic fillers, and the number of cracks on LF were fewer than SI and PC. On the other hand, for GR, no cracks were observed even after 50,000 thermal cycles. From these results, it can be presumed that the pre-treatment of filler by the graft polymerization is more effective to improve the durability of composite resin.
Hirabayashi
S
S
Department of Dental Engineering, School of Dental Medicine, Tsurumi University.
Nomoto
R
R
Harashima
I
I
Hirasawa
T
T
D003188:Composite Resins / Q000737:chemistry*; D004548:Elasticity; D006244:Hardness; D006358:Hot Temperature; D008422:Materials Testing; D012821:Silanes; D013499:Surface Properties; D013718:Tensile Strength
D003188:Composite Resins; D012821:Silanes