[Composition and morphology of oxides on porcelain fused to Ni-Cr alloys. Be containing alloys].
Bonding strength between porcelain and Ni-Cr alloy for the porcelain fused-to metal crown in which Be is contained in the alloy is known to be higher than those in which Be is not contained. Since, bonding between porcelain and alloy is the reaction of oxides and porcelain, the bonding is thought to be influenced by the quality the oxides film which forms on the alloy surface. The purpose of this study was to determine the composition and morphology of the oxides formed on both Be containing and non-Be contained Ni-Cr alloys. The oxides analysis was done using an EPMA and Auger analysis. Also, the Porcelain/Ni-Cr alloy interface was observed by a scanning electron microscope (SEM). The following results are indicated from this investigation: 1. The oxides from the alloys not containing Be are corundum type Cr2O3 and spinel type NiCr2O4. These oxide layers are uniform, thick and porous and the adhesion to alloy is poor. 2. The oxides from alloy containing Be is BeO only. The BeO is uniform, thin and condensed. The adhesion to the alloy is good. 3. The oxide layer formed when the porcelain is fused to alloy containing Be is thin (1 micron average) and has good adhesion to alloy. 4. Be is selectively oxidized and controlled the form of Cr2O3 and NiO.
Watanabe
T
T
D001608:Beryllium; D002858:Chromium Alloys; D001840:Dental Bonding; D003776:Dental Porcelain; D009532:Nickel
D002858:Chromium Alloys; D003776:Dental Porcelain; D009532:Nickel; D001608:Beryllium