Microleakage in MOD resin composite with three dentin bonding agents.
The extent of microleakage under MOD composites was studied when an aluminum oxalate dentin bonding agent (Tenure), a phosphonated resin bonding agent (Bondlite), and a glass-ionomer cement (Ketac Silver) were used. Three groups of 10 extracted molars were prepared with MOD cavities; one box ended on enamel, the other on cementum. In Group 1, Bondlite was applied to dentin and etched enamel before the sample was restored with a light-cured hybrid composite. In Group 2, a 2-mm increment of Ketac Silver was placed in each box before Bondlite and composite. In Group 3, Tenure was applied to dentin before being restored. Teeth were thermal-cycled, stained in silver nitrate, sectioned, and scored for microleakage. Microleakage along the gingival floor was significantly less at enamel margins than at cementum margins in all three groups. All groups showed severe marginal microleakage on cementum.
Eakle
W S
WS
Nakamoto
D K
DK
D003188:Composite Resins; D001840:Dental Bonding / Q000379:methods*; D003763:Dental Leakage; D005899:Glass Ionomer Cements; D006801:Humans; D010070:Oxalates; D019815:Oxalic Acid; D012116:Resins, Plant
D003188:Composite Resins; D005899:Glass Ionomer Cements; D010070:Oxalates; D012116:Resins, Plant; D019815:Oxalic Acid