The effect of glaze on restorative glass-ionomer cements: evaluation of environmental durability in lactic acid solution.
The surface texture changes of three kinds of glass-ionomer cements were compared with glazed and polished cement surfaces after thermal cycling in a storage media [lactic acid solution (pH 4.0)]. The changes were measured with regard to the surface roughness, colour-change, gloss, hardness, toothbrush wear, and SEM (scanning electron microscope) observation in the laboratory. The glazed cement surface was not affected after thermal cycling in the lactic acid solution.
D000134:Acid Etching, Dental; D003116:Color; D003775:Dental Polishing; D003793:Dental Restoration, Permanent; D005069:Evaluation Studies as Topic; D005899:Glass Ionomer Cements / Q000737:chemistry*; D006244:Hardness; D006863:Hydrogen-Ion Concentration; D007773:Lactates / Q000737:chemistry*; D019344:Lactic Acid; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D010756:Phosphoric Acids / Q000737:chemistry; D016628:Replica Techniques; D013499:Surface Properties; D013696:Temperature; D014099:Toothbrushing / Q000295:instrumentation
D005899:Glass Ionomer Cements; D007773:Lactates; D010756:Phosphoric Acids; C054101:ChemFil II; C068076:Chelon Fil; D019344:Lactic Acid; C037885:Fuji-ionomer