Adhesion of denture tooth porcelain to heat-polymerized denture resin.
Use of porcelain denture teeth may be desirable in many clinical situations, including implant-supported prostheses. However, lack of space because of frameworks often precludes the use of conventional retention by diatorics and pins. Adhesion of porcelain denture teeth to denture resin could also stiffen and possibly strengthen dentures and decrease stain ingress between porcelain teeth and resin denture bases. Unlike previous studies that investigated the bond between conventional feldspathic metal-ceramic porcelain and bis-GMA based composite resin, this study investigated adhesion of denture tooth porcelain to polymethyl methacrylate (PMMA). High-energy air abrasion, hydrofluoric acid etching, and the use of a general purpose bonding agent resulted in an improved bond strength of heat-cured denture PMMA bonded to denture tooth porcelain. Silane coating did not improve bond strengths, and conventional air abrasion was no more effective than polishing with 600-grit silicon carbide. Storage in water and artificial aging substantially decreased bond strengths. The strongest bond strengths were achieved by a high-energy-abrasion + etching + multi-purpose bonding-agent treatment, but a simpler etching + multiple-purpose bonding-agent treatment also produced reliable results. A laboratory technique was suggested. The role of surface treatment in the mechanism of adhesion was examined with scanning electron microscopy. High-energy abrasion produced a slightly more detailed initial topography than conventional air abrasion, but after etching, the high-energy topography became much more detailed. Surface topography alone did not account for all differences found.
D000704:Analysis of Variance; D001840:Dental Bonding / Q000379:methods*; D003738:Dental Cements; D003775:Dental Polishing / Q000379:methods; D003776:Dental Porcelain; D003799:Dental Stress Analysis; D003819:Denture Bases; D004548:Elasticity; D008422:Materials Testing; D008689:Methacrylates; D008768:Methylmethacrylates / Q000737:chemistry*; D008855:Microscopy, Electron, Scanning; D012821:Silanes; D013499:Surface Properties; D013718:Tensile Strength; D014093:Tooth, Artificial
D003738:Dental Cements; D008689:Methacrylates; D008768:Methylmethacrylates; D012821:Silanes; D003776:Dental Porcelain; C074811:Tenure adhesive