The particle size distribution, density, and specific surface area of welding fumes from SMAW and GMAW mild and stainless steel consumables.
Particle size distributions were measured for fumes from mild steel (MS) and stainless steel (SS); shielded metal arc welding (SMAW) and gas metal arc welding (GMAW) consumables. Up to six samples of each type of fume were collected in a test chamber using a micro-orifice uniform deposit (cascade) impactor. Bulk samples were collected for bulk fume density and specific surface area analysis. Additional impactor samples were collected using polycarbonate substrates and analyzed for elemental content. The parameters of the underlying mass distributions were estimated using a nonlinear least squares analysis method that fits a smooth curve to the mass fraction distribution histograms of all samples for each type of fume. The mass distributions for all four consumables were unimodal and well described by a lognormal distribution; with the exception of the GMAW-MS and GMAW-SS comparison, they were statistically different. The estimated mass distribution geometric means for the SMAW-MS and SMAW-SS consumables were 0.59 and 0.46 micron aerodynamic equivalent diameter (AED), respectively, and 0.25 micron AED for both the GMAW-MS and GMAW-SS consumables. The bulk fume densities and specific surface areas were similar for the SMAW-MS and SMAW-SS consumables and for the GMAW-MS and GMAW-SS consumables, but differed between SMAW and GMAW. The distribution of metals was similar to the mass distributions. Particle size distributions and physical properties of the fumes were considerably different when categorized by welding method. Within each welding method there was little difference between MS and SS fumes.
National Institute for Occupational Safety and Health, Morgantown, WV 26505-2845.
P
P
Hewett
D000336:Aerosols; D000395:Air Pollutants, Occupational / Q000032:analysis*; D002118:Calcium / Q000032:analysis; D002857:Chromium / Q000032:analysis; D003300:Copper; D004784:Environmental Monitoring / Q000295:instrumentation; D005459:Fluorides / Q000032:analysis; D007501:Iron / Q000032:analysis; D008345:Manganese / Q000032:analysis; D008851:Micropore Filters; D009532:Nickel / Q000032:analysis; D010316:Particle Size; D011188:Potassium / Q000032:analysis; D012906:Smoke / Q000032:analysis*; D013057:Spectrum Analysis; D013193:Stainless Steel / Q000032:analysis* / Q000737:chemistry; D013232:Steel / Q000032:analysis* / Q000737:chemistry; D013499:Surface Properties; D014896:Welding / Q000379:methods*
D000336:Aerosols; D000395:Air Pollutants, Occupational; D012906:Smoke; D002857:Chromium; D013193:Stainless Steel; D013232:Steel; D008345:Manganese; D003300:Copper; D009532:Nickel; D007501:Iron; D005459:Fluorides; D011188:Potassium; D002118:Calcium