In vivo wear pattern of experimental composite resins containing different filler components.
Using a scanning electron microscope (SEM) and an electron probe surface roughness analyzer (ERA), we conducted the in vivo study of the effect of various filler components on the wear of composite resins. Experimental light-cured composite resins were prepared employing three different filler components; -(1) Silica type, (2) Strontium type, and (3) Barium type. The filler content for all three types was 80 wt%, with the mean particlesize being 2.6 microns in diameter. The resin monomers consisted of 40 wt% Bis-GMA, 40 wt% TEGDMA and 20 wt% UTMA. These materials were placed in 2 mm diameter cylindrical cavities located in the OCA (occlusal contact area) or the CFA (contact free area) of cast crowns temporarily set in a volunteer patient's mouth. The crowns were removed at monthly intervals for longitudinal SEM observation. After two months, worn surfaces were also analyzed by ERA. The result showed that the wear patterns of the composites were characterized by the filler components, especially in the OCA.
Department of Operative Dentistry and Endodontics, Niigata University School of Dentistry, Japan.
K
K
Sekiya
A
A
Okamoto
M
M
Fukushima
M
M
Iwaku
D000328:Adult; D001464:Barium / Q000737:chemistry; D017438:Bisphenol A-Glycidyl Methacrylate; D003188:Composite Resins / Q000737:chemistry*; D003442:Crowns; D004577:Electron Probe Microanalysis; D005898:Glass / Q000737:chemistry; D006801:Humans; D008689:Methacrylates; D008855:Microscopy, Electron, Scanning; D011092:Polyethylene Glycols; D011109:Polymethacrylic Acids; D011140:Polyurethanes; D012822:Silicon Dioxide / Q000737:chemistry; D013324:Strontium / Q000737:chemistry; D013499:Surface Properties
D003188:Composite Resins; D008689:Methacrylates; D011109:Polymethacrylic Acids; D011140:Polyurethanes; C091839:urethanetrimethacrylate; C020946:triethylene glycol dimethacrylate; D001464:Barium; D011092:Polyethylene Glycols; D017438:Bisphenol A-Glycidyl Methacrylate; D012822:Silicon Dioxide; D013324:Strontium