The effect of potential investment expansion and hot strength on the fit of full-crown castings made with a gypsum-bonded investment.
OBJECTIVE
It has been claimed that the strength of the investment mold at the casting temperature affects the dimensional accuracy of castings (e.g., Markley, 1953; Earnshaw, 1957; Asgar, 1972), but the relationship has not been studied quantitatively. In this investigation, the effects of both mold expansion and hot strength on the relative inaccuracy of full-crown castings have been measured and analyzed. The likelihood that a strong investment could cause distortion of the casting by non-uniform restriction of casting shrinkage (Earnshaw, 1969b) was also considered.


METHODS
Castings were made with a commercial gypsum-bonded inlay investment, used both as supplied and with modifications that increased its expansion and reduced its hot strength. In both series of tests, the investments were used over a wide range of liquid/powder (L/P) ratios in casting rings fitted with dry ceramic liners, and set under dry conditions.


RESULTS
Casting inaccuracy showed a significant linear correlation with total expansion and a highly significant linear correlation with the combination of total expansion and hot strength. The modified investment, with its low hot strength, gave less distortion of casting shape than did the much stronger unmodified material. However, it was found that to ensure sound castings, the hot compressive strength should not be less than 1.8MPa.


CONCLUSIONS
This investigation showed that while investment expansion is the major variable affecting casting inaccuracy, hot strength is an important modifying factor which also has to be considered when predicting casting inaccuracy from measured properties of the investment.
Morey
E F
EF
School of Dental Studies, Faculty of Dentistry, University of Sydney, New South Wales, Australia.
Earnshaw
R
R
D002133:Calcium Sulfate / Q000737:chemistry*; D003442:Crowns; D003734:Dental Casting Investment / Q000737:chemistry*; D003735:Dental Casting Technique; D005990:Glycerol / Q000737:chemistry; D006047:Gold Alloys; D006358:Hot Temperature; D016018:Least-Squares Analysis; D016014:Linear Models; D015203:Reproducibility of Results; D012822:Silicon Dioxide / Q000737:chemistry*; D012965:Sodium Chloride / Q000737:chemistry
D003734:Dental Casting Investment; D006047:Gold Alloys; D012965:Sodium Chloride; D012822:Silicon Dioxide; D005990:Glycerol; D002133:Calcium Sulfate