Biomechanical and ultrastructural comparison of cryopreservation and a novel cellular extraction of porcine aortic valve leaflets.
Heart valve substitutes of biological origin often fail by degenerative mechanisms. Many authors have hypothesized that mechanical fatigue and structural degradation are instrumental to in vivo failure. Since the properties of the structural matrix at implantation may predetermine failure, we have examined the ultrastructure, fracture, mechanics, and uniaxial high-strain-rate viscoelastic properties of: (1) fresh, (2) cryopreserved, and (3) cellular extracted porcine aortic valve leaflets. The cellular extraction process is being developed in order to reduce immunological attack and calcification. Cryopreservation causes cellular disruption and necrotic changes throughout the tissue, whereas extraction removes all cells and lipid membranes. Both processes leave an intact collagen and elastin structural matrix and preserve the high-strain-rate viscoelastic characteristics of the fresh leaflets. Extraction does cause a 20% reduction in the fracture tension and increases tissue extensibility, with the percent strain at fracture rising to 45.3 +/- 4 (mean +/- SEM) from 31.5 +/- 3 for fresh leaflets. However, extraction does preserve matrix structure and mechanics over the physiological loading range. Glutaraldehyde fixation produces increased extensibility, increased elastic behavior, and, when applied to extracted leaflets, it causes a marked drop in fracture tension, to 50% of that for fresh leaflets. The combination of extraction and fixation may lead to early degenerative failure. The cellular extraction technique alone may be a useful alternative to glutaraldehyde fixation in preparing bioprosthetic heart valves.
Courtman
D W
DW
Centre for Biomaterials, University of Toronto, Ontario, Canada.
Pereira
C A
CA
Omar
S
S
Langdon
S E
SE
Lee
J M
JM
Wilson
G J
GJ
D000818:Animals; D001021:Aortic Valve / Q000737:chemistry / Q000502:physiology* / Q000648:ultrastructure; D001696:Biomechanical Phenomena; D001705:Bioprosthesis; D003432:Cross-Linking Reagents / Q000737:chemistry; D015925:Cryopreservation; D004548:Elasticity; D005109:Extracellular Matrix / Q000648:ultrastructure; D005976:Glutaral / Q000737:chemistry; D006350:Heart Valve Prosthesis; D008854:Microscopy, Electron; D011489:Protein Denaturation; D013552:Swine; D013718:Tensile Strength; D016707:Tissue Fixation; D014783:Viscosity
D003432:Cross-Linking Reagents; D005976:Glutaral