Crystallization of experimental bioactive glass compositions.
Crystallization kinetics studies for six experimental glass formulations in the system Na2O-CaO-SiO2-P2O5 synthesized by wet chemistry were conducted by means of differential thermal analysis. These glasses had CaO/P2O5 and SiO2/ (CaO + Na2O) ratios ranging from 8.74-3.38 and 0.92-3.03, respectively. Samples of each glass (n = 30 were heated from 23 to 1250 degrees C under N2 atmosphere at heating rates ranging from 10 to 50 degrees C/min. Glass-ceramics were obtained after heat treating the initial glasses at temperatures determined from their DTA exotherms. The activation energy of crystallization for each glass composition was calculated from an expression-relating log-heating rate and the reciprocal of the exothermic peak temperature. The compositions of the six glasses were significantly different (p = 0.05). The activation energy of crystallization (Q) values ranged from 196 to 782 kJ/mole. A correlation was obtained between Q and CaO/P2O5 and between Q and the Young's modulus (P < 0.001). Two of the six glasses exhibited bulk crystallization. X-ray diffraction studies showed that four of the six glasses exhibited different proportions of crystalline phases following heat treatment. These phases were wollastonite (CaSiO3), Na2CaSi3O9, combeite [Na4Ca3SI6O16(OH)2], and some unidentifiable phases. Two of the six bioceramic materials had a mixture of unknown crystalline phases.
Rizkalla
A S
AS
Division of Biomaterials Faculties of Medicine, Dalhousie University, Halifax, Nova Scotia, Canada.
Jones
D W
DW
Clarke
D B
DB
Hall
G C
GC
D001672:Biocompatible Materials; D005898:Glass
D001672:Biocompatible Materials