In vivo surface analysis of titanium and stainless steel miniplates and screws.
This study was undertaken to characterize the surfaces of Champy titanium and stainless steel miniplates and screws that had been used to stabilize fractures of the mandible in an animal model. Miniplates and screws were retrieved at 4, 12, and 24 weeks after surgery. Low-vacuum scanning electron microscopy (SEM) of autoclaved unused (control) and test miniplates from the same production batches was undertaken. Energy-dispersive X-ray (EDX) analysis was used to identify compositional variations of the miniplate surface, and Vickers hardness testing was performed. At autopsy, clinical healing of all fractures was noted. SEM analysis indicated no perceptible difference in the surface characteristics of the miniplates at all time intervals. Aluminium and silicon deposits were identified by EDX analysis over the flat surfaces. There was extensive damage to some screw heads. It is concluded that there were no significant changes in the surface characteristics of miniplates retrieved up to 24 weeks after implantation in comparison with controls. Damage to the screws during insertion due to softness of the materials may render their removal difficult. There was no evidence to support the routine removal of titanium or stainless steel miniplates because of surface corrosion up to 6 months after implantation.
Matthew
I R
IR
Unit of Oral Surgery, University of Birmingham, School of Dentistry, UK.
Frame
J W
JW
Browne
R M
RM
Millar
B G
BG
D000704:Analysis of Variance; D000818:Animals; D001672:Biocompatible Materials / Q000737:chemistry; D001860:Bone Plates; D001863:Bone Screws; D003343:Corrosion; D004285:Dogs; D005260:Female; D005593:Fracture Fixation, Internal / Q000295:instrumentation*; D006244:Hardness; D008337:Mandibular Fractures / Q000601:surgery*; D008854:Microscopy, Electron; D013193:Stainless Steel / Q000737:chemistry; D013499:Surface Properties; D014025:Titanium / Q000737:chemistry
D001672:Biocompatible Materials; D013193:Stainless Steel; D014025:Titanium