Formation Mechanism of Monodispersed alpha-Fe2O3 Particles in Dilute FeCl3 Solutions
Some ambiguity is still involved in the interpretation of the growth mechanism of monodispersed hematite (alpha-Fe2O3) particles in dilute FeCl3 solutions. Namely, there are two entirely different proposals on this issue, viz. aggregation of preformed primary particles of alpha-Fe2O3 itself and reprecipitation of the ionic species through dissolution of the preformed beta-FeOOH particles. In order to resolve this problem, the formation process was followed in detail through TEM, Electron Diffraction, XRD, FT-IR, and ICP spectrometry along with quantitative analyses on seed effects. As a result, it has been concluded that the nuclei of the hematite particles are initially generated with the formation of beta-FeOOH particles and that they are grown by deposition of the solute originally present in the solution phase and indirectly furnished from the beta-FeOOH by dissolution. As the concentration of the solute is lowered by the growth of the hematite particles, they continue to grow with the solute provided mainly from the beta-FeOOH in a steady-state of the dissolution of beta-FeOOH and growth of alpha-Fe2O3. The basic formation mechanism is common to the ellipsoidal particles grown in the presence of phosphate ions and spherical particles in their absence.
Sugimoto
T
Institute for Advanced Materials Processing, Tohoku University, Katahira 2-1-1, Aoba-ku, Sendai, 980-77, Japan
Muramatsu
A