In vitro wear, hardness, and conversion of diacetyl-containing and propanal-containing resin materials.
OBJECTIVE
This study was conducted to determine the effect of diacetyl or propanal activities: 1) on the in vitro wear of 22 experimental resin composites; and 2) on the Wallace indentation hardness of the unfilled resins. The objective was to examine the correlation between wear, hardness, and quantity of remaining double bonds (determined previously).


METHODS
Diacetyl or propanal agents were added in varying concentrations to monomer mixtures. The resins were made light-curing and those used for measurement of wear were loaded with filter. The results were analyzed by ANOVA and Newman-Keuls' multiple range tests.


RESULTS
In the composite systems, adding diacetyl or propanal resulted in decreased in vitro wear. The quantity of remaining double bonds in the dental polymers with these additives was also reduced. Their effect on Wallace indentation depth was less clear-cut. Low concentrations of additives decreased indentation depth of the unfilled materials, whereas high concentrations increased indentation depth. If it assumed that differences in the polymer have a major influence on the wear when the filter content and particle matrix interface are kept constant, then the hardness data on the unfilled resin can be used to correlate property changes of the polymer in the composite. A three-dimensional regression analysis found that in vitro wear decreased with decreasing Wallace indentation depth and decreasing quantity of remaining double bonds.


CONCLUSIONS
Addition of diketone or monoaldehyde to resin monomers may provide a means of increasing wear resistance of composites and allow their use in stress-bearing areas.
Peutzfeldt
A
A
Department of Dental Materials, School of Dentistry, Faculty of Health Sciences, University of Copenhagen, Denmark.
Asmussen
E
E
D000447:Aldehydes / Q000737:chemistry*; D000704:Analysis of Variance; D017438:Bisphenol A-Glycidyl Methacrylate / Q000737:chemistry; D003188:Composite Resins / Q000737:chemistry*; D019554:Dental Restoration Wear; D003931:Diacetyl / Q000737:chemistry*; D004339:Drug Compounding; D006244:Hardness; D008422:Materials Testing; D008689:Methacrylates / Q000737:chemistry; D011092:Polyethylene Glycols / Q000737:chemistry; D011109:Polymethacrylic Acids / Q000737:chemistry; D011140:Polyurethanes / Q000737:chemistry; D012044:Regression Analysis; D013499:Surface Properties
D000447:Aldehydes; D003188:Composite Resins; D008689:Methacrylates; D011109:Polymethacrylic Acids; D011140:Polyurethanes; C029824:urethane dimethacrylate luting resin; C020946:triethylene glycol dimethacrylate; D011092:Polyethylene Glycols; D017438:Bisphenol A-Glycidyl Methacrylate; C005044:hydroxyethyl methacrylate; C005556:propionaldehyde; D003931:Diacetyl