Cyclic voltammetry of dental amalgams.
OBJECTIVE
This study used cyclic voltammetry to examine the effect of the composition of dental amalgams on their electrochemical behavior, including reactions occurring outside of oral conditions.


METHODS
Amalgams (residual mercury 47.5%) were prepared using two low-copper (3 wt% Cu) powders and five high-copper powders (40-80 wt% Ag, 12-30 wt% Cu) with and without zinc (1.5 wt%). Cyclic voltammograms were obtained at 37 degrees C in 1.0% NaCl scanning at 2 mV/s in the potential range from -1.5 V to +0.8 V vs. Ag/AgCl.


RESULTS
During the anodic scans, AgCl and Hg2Cl2 films were formed on all amalgams except the one with only 40 wt% Ag. In all high-copper amalgams, a prominent Cu (oxidation) peak was found at -0.1 V, indicating the release of copper during corrosion. Zinc affected the oxidation process for both low- and high-copper amalgams. When zinc was absent, a peak for Sn2+ oxidation appeared at -0.4 V. When zinc was present, a Sn4+ oxidation peak was revealed at -0.6 V. In some amalgams, there was evidence of the selective corrosion (pitting corrosion) of tin and copper. In the lowest silver-content amalgam, no protective films were formed, which is indicative of its poor corrosion resistance. As expected, in all the low-copper amalgams, an extreme increase in current density was recorded immediately at 0 V, due to the release of tin from gamma 2.


CONCLUSIONS
Cyclic voltammetry is useful for the rapid examination (less than an hour) of the electrochemical behavior of amalgams, specifically to obtain information on the formation of compounds and the sequences of electrochemical reactions.
Horasawa
N
N
Department of Biomaterials Science, Baylor College of Dentistry, Dallas, Texas, USA.
Nakajima
H
H
Ferracane
J L
JL
Takahashi
S
S
Okabe
T
T
D000704:Analysis of Variance; D003300:Copper / Q000737:chemistry; D003343:Corrosion; D003723:Dental Amalgam / Q000737:chemistry*; D004339:Drug Compounding; D004563:Electrochemistry; D008422:Materials Testing; D008628:Mercury / Q000737:chemistry; D010084:Oxidation-Reduction; D012834:Silver / Q000737:chemistry; D018709:Statistics, Nonparametric; D013499:Surface Properties; D014001:Tin / Q000737:chemistry; D015032:Zinc / Q000737:chemistry
D012834:Silver; D014001:Tin; D003300:Copper; D003723:Dental Amalgam; D008628:Mercury; D015032:Zinc