An in vitro study of high-strength resin posterior denture tooth wear.
This in vitro study evaluated the wear resistance of a high-strength resin posterior denture tooth against eight opposing dental materials. The tooth specimen was cusp shaped and the opposing materials were formed as a 10 x 10 x 5 mm plate. All material combinations were tested using a machine designed to produce sliding contact 20 x 10(4) times at 60 cycles per minute and a 4-mm sliding distance per stroke in the buccolingual direction under a load of 1 kg. Wear analysis was measured as the total height loss of each material combination and the volume loss of each material. Wear against human enamel was evaluated as a control. The least loss was observed opposing a gold-silver-palladium-copper alloy, and the greatest loss was observed opposing porcelain. The volume loss of high-strength resin against gold-silver-palladium-copper alloy was as small as that against human enamel. High-strength resin wear was more significant against castable ceramics and porcelain. The volume losses of high-strength resin against high-strength resin, polycarbonate, or cobalt-chromium alloy were significantly larger than those against polyethersulfone, poly(methyl methacrylate), gold-silver-palladium-copper alloy, or human enamel. These findings suggest that the were resistance of high-strength resin is influenced considerably by opposing dental materials, and that the best combination was high-strength resin-gold-silver-palladium-copper alloy, and the poorest combination was high-strength resin-porcelain.
Abe
Y
Y
Department of Removable Prosthodontics, Hiroshima University School of Dentistry, Japan.
Sato
Y
Y
Akagawa
Y
Y
Ohkawa
S
S
D000704:Analysis of Variance; D001641:Bicuspid; D003188:Composite Resins / Q000737:chemistry*; D003432:Cross-Linking Reagents; D003743:Dental Enamel; D003764:Dental Materials; D019554:Dental Restoration Wear; D003779:Denture Design; D006244:Hardness; D008422:Materials Testing; D008689:Methacrylates / Q000737:chemistry; D008855:Microscopy, Electron, Scanning; D008963:Molar; D011092:Polyethylene Glycols / Q000737:chemistry; D011109:Polymethacrylic Acids / Q000737:chemistry; D011140:Polyurethanes / Q000737:chemistry; D014093:Tooth, Artificial
D003188:Composite Resins; D003432:Cross-Linking Reagents; D003764:Dental Materials; D008689:Methacrylates; D011109:Polymethacrylic Acids; D011140:Polyurethanes; C029824:urethane dimethacrylate luting resin; C020946:triethylene glycol dimethacrylate; D011092:Polyethylene Glycols