title: The evaluation of lyophilized polymer matrices for administering recombinant human bone morphogenetic protein-2.
abstract: Novel unitary devices, prepared by lyophilization of viscous solutions of sodium carboxymethylcellulose (CMC) and methylcellulose (MC), were evaluated as sustained-release delivery systems for recombinant human bone morphogenetic protein-2 (rhBMP-2). In vitro characterization of the unitary devices, which contained rhBMP-2-loaded poly (d,l lactide-co-glycolide) (PLGA) bioerodible particles (BEPs), was conducted over a 2-month period. Determinations included buffer uptake, mass and molecular weight loss and rhBMP-2 release from the unitary devices. CMC devices imbibed approximately 16 times their weight of buffer, while with MC, equilibrium uptake was approximately 6 times the dry weight of the devices. Overall mass loss percentages were approximately 55 and 35%, respectively, for CMC and MC devices. rhBMP-2 release from the devices was essentially a triphasic process: an initial phase during which "free" protein (rhBMP-2 present on the surface and within the pores of the PLGA BEPs) was released, a lag period during which no release was discerned, and then release of "bound" rhBMP-2 (protein adsorbed to the BEPs). The release of bound protein correlated with the mass loss of the polymer which began after 3 weeks. Release from the unitary devices was lower than that from the BEPs alone, due to a retardation effect of the gelled CMC/MC polymers. In rabbits in which full-thickness cranial bone defects were created, the implants were well tolerated and induced significant new bone growth during an 8-week evaluation period. The CMC devices appear to have induced bone earlier (at 2 weeks), but this did not affect eventual 8-week results. CMC devices without rhBMP-2 appeared to provide some bone conduction, in contrast to the blank MC devices.
authors.affiliation: Department of Surgery, University of Kentucky, Lexington 40536-0082, USA.
authors.forename: S S
authors.initials: SS
authors.lastname: Duggirala
authors.forename: J B
authors.initials: JB
authors.lastname: Rodgers
authors.forename: P P
authors.initials: PP
authors.lastname: DeLuca
mesh_terms: D000818:Animals; D001672:Biocompatible Materials; D055396:Bone Morphogenetic Protein 2; D019485:Bone Morphogenetic Proteins / Q000008:administration & dosage*; D002021:Buffers; D002266:Carboxymethylcellulose Sodium; D002851:Chromatography, High Pressure Liquid; D005079:Excipients; D005612:Freeze Drying; D006801:Humans; D019344:Lactic Acid; D008747:Methylcellulose; D008970:Molecular Weight; D011100:Polyglycolic Acid; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011108:Polymers; D011817:Rabbits; D011994:Recombinant Proteins / Q000008:administration & dosage; D016212:Transforming Growth Factor beta
chemical_list: C525718:BMP2 protein, human; D001672:Biocompatible Materials; D055396:Bone Morphogenetic Protein 2; D019485:Bone Morphogenetic Proteins; D002021:Buffers; D005079:Excipients; D011108:Polymers; D011994:Recombinant Proteins; D016212:Transforming Growth Factor beta; C499469:recombinant human bone morphogenetic protein-2; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011100:Polyglycolic Acid; D019344:Lactic Acid; D008747:Methylcellulose; D002266:Carboxymethylcellulose Sodium