Behavior of pure gallium in water and various saline solutions.
This study investigated the chemical stability of pure gallium in water and saline solutions in order to obtain fundamental knowledge about the corrosion mechanism of gallium-based alloys. A pure gallium plate (99.999%) was suspended in 50 mL of deionized water, 0.01%, 0.1% or 1% NaCl solution at 24 +/- 2 degrees C for 1, 7, or 28 days. The amounts of gallium released into the solutions were determined by atomic absorption spectrophotometry. The surfaces of the specimens were examined after immersion by x-ray diffractometry (XRD) and x-ray photoelectron spectroscopy (XPS). In the solutions containing 0.1% or more NaCl, the release of gallium ions into the solution was lowered when compared to deionized water after 28-day immersion. Gallium oxide monohydroxide was found by XRD on the specimens immersed in deionized water after 28-day immersion. XPS indicated the formation of gallium oxide/hydroxide on the specimens immersed in water or 0.01% NaCl solution. The chemical stability of pure solid gallium was strongly affected by the presence of Cl- ions in the aqueous solution.
Horasawa
N
N
Department of Dental Technology, Matsumoto Dental College, Nagano, Japan.
Nakajima
H
H
Takahashi
S
S
Okabe
T
T
D003722:Dental Alloys; D004577:Electron Probe Microanalysis; D005708:Gallium / Q000032:analysis / Q000737:chemistry*; D005709:Gallium Isotopes; D007101:Immersion; D012965:Sodium Chloride / Q000032:analysis / Q000737:chemistry*; D012996:Solutions; D013054:Spectrophotometry, Atomic; D013997:Time Factors; D014867:Water / Q000032:analysis / Q000737:chemistry*; D014961:X-Ray Diffraction
D003722:Dental Alloys; D005709:Gallium Isotopes; D012996:Solutions; D014867:Water; D012965:Sodium Chloride; D005708:Gallium