title: Laser welding of a cobalt-chromium removable partial denture alloy.
abstract: BACKGROUND
  The electric alloy brazed joints of removable partial denture alloys have failed frequently after routine usage.
  
  
  OBJECTIVE
  A technique providing higher joint strengths was investigated. This investigation compared the tensile strengths of electric-brazed and laser-welded joints for a cobalt-chromium removable partial denture alloy.
  
  
  METHODS
  Twenty-four cobalt-chromium standard tensile testing rods were prepared and divided into three groups of eight. All specimens in the control group (group 1) were left in the as-cast condition. Groups 2 and 3 were the test specimens, which were sectioned at the center of the rod. Eight specimens were joined by using electric brazing, and the remaining specimens were joined by using laser welding. After joining, each joint was ground to a uniform diameter, then tested to tensile failure on an Instron universal testing machine. Failure loads were recorded and fracture stress calculated. Statistical analysis was applied.
  
  
  RESULTS
  The student-Newman-Keuls test showed a highly significant difference between the joint strengths of the as-cast control specimens, the electric-brazed and laser-welded joints.
  
  
  CONCLUSIONS
  The tensile strengths of the as-cast joints were higher than those for the laser-welded joints, and both were higher than the electric-brazed joint strengths.
authors.affiliation: Department of Prosthodontics, University of Washington, Seattle, USA.
authors.forename: D P
authors.initials: DP
authors.lastname: NaBadalung
authors.forename: J I
authors.initials: JI
authors.lastname: Nicholls
mesh_terms: D000704:Analysis of Variance; D002858:Chromium Alloys; D003035:Cobalt; D012994:Dental Soldering / Q000295:instrumentation*; D003799:Dental Stress Analysis; D003779:Denture Design; D003832:Denture, Partial, Removable; D006801:Humans; D007834:Lasers; D008422:Materials Testing; D016062:Porosity; D018709:Statistics, Nonparametric; D013718:Tensile Strength; D014800:Vitallium; D014896:Welding / Q000295:instrumentation*
chemical_list: D002858:Chromium Alloys; D014800:Vitallium; D003035:Cobalt