Evaluation of glass ionomer as an endodontic sealant: an in vitro study.
This study investigated the sealing ability of glass ionomer as a root canal sealer with and without lateral condensation of gutta percha cones. Ten gutta percha cones were embedded in Grossman's sealer and 10 in glass ionomer sealer. The sealers were mechanically separated from the gutta percha. The cone surfaces were examined using scanning electron microscopy (SEM). SEM revealed a characteristic etch pattern on the glass ionomer group and a hybrid layer on the cone surfaces of the Grossman's group. Additionally, 40 maxillary incisors were divided into four treatment groups: 1) glass ionomer sealer with lateral condensation, 2) glass ionomer sealer with only one master cone, 3) Grossman's sealer with condensation, and 4) Grossman's sealer with only one master cone. The average values for leakage (mm) in groups 1 through 4 were 0.81 +/- 0.75, 4.30 +/- 1.82, 0.67 +/- 0.80, and 1.10 +/- 1.68, respectively. Statistical analysis showed that group 2 leaked more than the other three groups.
Lee
C Q
CQ
Department of Oral Biology and Endodontics, School of Dentistry, University of Missouri-Kansas 64108, USA.
Harandi
L
L
Cobb
C M
CM
D000704:Analysis of Variance; D003763:Dental Leakage; D005069:Evaluation Studies as Topic; D005899:Glass Ionomer Cements / Q000737:chemistry; D006171:Gutta-Percha / Q000737:chemistry; D008855:Microscopy, Electron, Scanning; D012387:Root Canal Filling Materials / Q000737:chemistry; D012389:Root Canal Obturation; D013499:Surface Properties; D015035:Zinc Oxide-Eugenol Cement / Q000737:chemistry
D005899:Glass Ionomer Cements; C074934:Ketac Endo; D012387:Root Canal Filling Materials; D015035:Zinc Oxide-Eugenol Cement; C045432:Grossman's sealer; D006171:Gutta-Percha