title: Mechanical properties of laser-welded cast titanium joints under different conditions.
abstract: BACKGROUND
  Data on optimal conditions for laser welding commercial pure cast titanium used in dental restorations are sparse and not well established.
  
  
  OBJECTIVE
  The mechanical properties of laser-welded cast commercially pure titanium under different laser welding conditions were evaluated to find the optimal parameters in terms of duration and voltage (energy level).
  
  
  METHODS
  Fifty-seven cast pure titanium specimens according to ISO specification 6871 were divided into nine experimental groups and one control group. The sectioned titanium bars were laser-welded under different duration (8, 10, and 12 ms) and energy (290, 300, and 310 V) levels and evaluated for ranges of ultimate tensile strength (374 to 562 MPa), 0.2% yield strength (206 to 338 MPa), and percentage elongation (2.49% to 10.58%).
  
  
  RESULTS
  Under a suitable laser-welding setting parameter the ultimate tensile strength and 0.2% yield strength of experimental groups were weaker than the unsectioned control specimens (control group ultimate tensile strength 540 +/- 11 MPa, 0.2% yield strength 258 +/- 49 MPa) or too brittle (control group percentage elongation 12.41% +/- 1.83%). Two-way ANOVA, nonparametric tests showed that voltage was the only significant factor for all parameters studied (p < 0.01). Optimal conditions were determined with three-dimensional response curves (305 V, 12 ms ultimate tensile strength; 310 V, 10 ms 0.2% yield strength; 300 V, 12 ms percentage elongation).
  
  
  CONCLUSIONS
  Optimal duration and voltage (energy level) used in laser welding for cast CP grade I titanium bar was superior to or comparable with and produced properties that were superior to or comparable with the unsectioned control specimens.
authors.affiliation: Department of Prosthodontics, School of Dentistry, National Taiwan University, Taipei.
authors.forename: T
authors.initials: T
authors.lastname: Chai
authors.forename: C K
authors.initials: CK
authors.lastname: Chou
mesh_terms: D000704:Analysis of Variance; D055598:Chemical Phenomena; D002627:Chemistry, Physical; D003764:Dental Materials / Q000737:chemistry*; D012994:Dental Soldering; D004548:Elasticity; D005069:Evaluation Studies as Topic; D006244:Hardness; D007834:Lasers; D016018:Least-Squares Analysis; D008422:Materials Testing; D013314:Stress, Mechanical; D013718:Tensile Strength; D013997:Time Factors; D014025:Titanium / Q000737:chemistry*
chemical_list: D003764:Dental Materials; D014025:Titanium