The Influence of Temperature on the Adsorption of Cadmium(II) and Cobalt(II) on Kaolinite.
The adsorption of Cd(II) and Co(II) onto kaolinite was investigated at five temperatures between 10 and 70 degreesC. Adsorption edges showed that both Cd(II) and Co(II) adsorbed onto kaolinite in two stages, separated by a plateau between pH 4 and 7. Initial adsorption commenced at about the same pH for both cations, but at each temperature the second-stage adsorption occurred at a slightly lower pH for Co(II) than for Cd(II). At higher temperatures adsorption was generally shifted to lower pH. Adsorption isotherms at pH 5.50 for both cations could be fitted closely by a simple Langmuir model at all temperatures. A two-site Langmuir model provided a substantially better fit for isotherms at pH 7.50 for Cd(II) and pH 7.00 for Co(II). At pH 5.50 the maximum adsorption density estimated from Langmuir modelling was approximately the same (1 µmol m-2) for both cations and at all temperatures. A similar value was found for one of the model sites at pH 7.50 for Cd(II) and at pH 7.00 for Co(II). Potentiometric titrations of kaolinite suspensions, in the presence and absence of added Cd(II) or Co(II), could be modeled accurately by a constant-capacitance surface complexation model. The data for adsorption of both cations could be fitted at all temperatures using a model that assumed ion exchange at permanent charge sites on silanol faces and complexation to hydroxyl edge groups. Thermodynamic parameters estimated from both the Langmuir and surface complexation models showed that adsorption of Cd(II) and Co(II) were endothermic. For the surface complexation model, enthalpies of adsorption on exchange sites were about 10 kJ mol-1, but at the variable-charge sites the enthalpy changes were about 70 kJ mol-1. For all these reactions the entropy changes were positive, with values of the order of 100 J K-1 mol-1. Trends for the Langmuir model were qualitatively similar. Copyright 1998 Academic Press.
Angove
MJ
Division of Physical Sciences and Engineering, La Trobe University, Bendigo, Bendigo, Victoria, 3552, Australia
Johnson
BB
Wells
JD