Viscoelasticity and aging of dental composites.
Effects of aging on several dental composites were studied using a torsion creep apparatus. A constant torque was applied from 1 second to 3 hours, and recovery was observed from 10 seconds to 2 days, for specimens aged from 3 hours to 8 weeks following polymerization. Specimens aged for shorter times exhibited more creep and less complete recovery than specimens aged for longer times. Modulus and creep results were qualitatively consistent with a composite model for particulate inclusions.