Evaluation of the Structure and Acid-Base Properties of Bulk Wood by FT-Raman Spectroscopy.
The structure of pine wood (Pinus silvestris L.) has been analyzed by FT-Raman spectroscopy, taking birch wood and the wood components cellulose, hemicellulose (xylan), and lignin as well as previously characterized wood resins as references. The acid-base properties of bulk pine wood were evaluated by comparing the spectra recorded before and after the treatment with various solvents. After the treatment with the probe liquids having only a Lifshitz-van der Waals (LW) component, it was found that the LW interactions in pine wood take place without changing the main structure. After treatment with Lewis acid-base active probe liquids, the spectra indicate that, e.g., the intense peak located at approximately 2936 cm-1 (CH2 stretch) seems to disappear, suggesting that this peak may be related to Lewis acidity. In addition, after treatment with a Lewis acid, it was found that the intense peak located at approximately 1657 cm-1 (C&dbond;C) is shifted, relating to Lewis basicity. With the ratio approximately 2936/ approximately 1657 cm-1 as a measure of the acid-base properties of bulk wood, a value of about 2.00 indicates that the bulk pine wood is largely acidic. The pH determined supports the evaluation made by FT-Raman spectroscopy. Copyright 1998 Academic Press.
Department of Physical Chemistry, Åbo Akademi University, Porthansgatan 3, Turku, 20500, Finland
Q
Shen
H
Rahiala
JB
Rosenholm