title: Scanning electron microscope appearances of Lightspeed instruments used clinically: a pilot study.
abstract: The cutting heads of the first 18 instruments in six sets of clinically used Lightspeed instruments (sizes 20-65) were examined in a scanning electron microscope (SEM). Three sets had been used by full-time faculty and discarded as follows: instrument sizes 20-32.5 after 18 treated root canals; instrument sizes 35-47.5 after 36 treated root canals; and instrument sizes 50-65 after 54 treated root canals. Three other sets had been used by a private clinician who discarded all Lightspeed instruments after preparing 20 root canals. The cutting heads of the 108 instruments were examined for the presence of surface debris, metal strips, metal flash, disrupted cutting edges, microfractures, tears, pitting and fretting and fatigue cracks. Fewer instruments ultrasonically cleaned before examination in the SEM had debris than those not cleaned before examination. The prevalence of metal strips and metal flash was similar for both groups. In contrast, microfractures and tears were more prevalent in instruments used by the full-time faculty group, who used their instruments more frequently before discarding them. Pitting and fretting occurred equally frequently in both groups whilst no fatigue cracks were noted in any of the 108 instruments. Overusage of Lightspeed instruments may predispose the flutes of the cutting heads to microfractures and clinicians should be aware of this possibility.
authors.affiliation: Department of Preventive Dentistry, School of Dentistry, University of Zurich, Switzerland.
authors.forename: M
authors.initials: M
authors.lastname: Marending
authors.forename: F
authors.initials: F
authors.lastname: Lutz
authors.forename: F
authors.initials: F
authors.lastname: Barbakow
mesh_terms: D000497:Alloys / Q000737:chemistry; D003762:Dental Instruments / Q000706:statistics & numerical data; D004867:Equipment Design; D004868:Equipment Failure; D005069:Evaluation Studies as Topic; D006801:Humans; D008855:Microscopy, Electron, Scanning; D010865:Pilot Projects; D018915:Root Canal Preparation / Q000295:instrumentation*; D013499:Surface Properties
chemical_list: D000497:Alloys; C013616:nitinol