Reactivity of fluoride-containing calcium aluminosilicate glasses used in dental glass-ionomer cements.
The glass component critically determines the properties of glass-ionomer cements (GIC). However, the exact relationship between the composition of the glass and these properties is not yet fully understood. To investigate this relationship, we studied the reactivity of glasses used in commercial GIC in acetic acid solutions, using a pH-stat method. Qualitative differences in the leaching behavior of these glasses can be explained by different pre-treatments. Acid-washing and silanization modify the surfaces of the glass particles, thus inducing a delay of the leaching process, whereas untreated glasses exhibit a fast initial leaching, but their acid reactivity slows very soon. Quantitative differences in acid reactivity can be correlated with the mean chemical composition of the glasses. In this respect, the leaching tends to increase with an increasing ratio of network-dwelling cations to Al3+ ions. These results provide a fundamental basis for the explanation, prediction, and control of cement properties as a function of glass characteristics.
De Maeyer
E A
EA
Department of Dental Materials Science, Dental School, Institute for Biomedical Technologies (IBITECH), University of Ghent, Belgium.
Verbeeck
R M
RM
Vercruysse
C W
CW
D019342:Acetic Acid / Q000737:chemistry; D000538:Aluminum Silicates / Q000032:analysis / Q000737:chemistry*; D017610:Calcium Compounds; D005459:Fluorides / Q000032:analysis / Q000737:chemistry*; D005898:Glass / Q000032:analysis / Q000737:chemistry*; D005899:Glass Ionomer Cements / Q000032:analysis / Q000737:chemistry*; D006863:Hydrogen-Ion Concentration; D012996:Solutions; D013997:Time Factors
D000538:Aluminum Silicates; D017610:Calcium Compounds; D005899:Glass Ionomer Cements; D012996:Solutions; C049037:aluminosilicate; D019342:Acetic Acid; D005459:Fluorides