Fabrication and characterization of an asymmetric polyurethane membrane for use as a wound dressing.
To prevent wound dehydration and bacterial penetration, a wound dressing should be occlusive, but on the other hand it should also be permeable for wound exudate to prevent bullae formation.  To meet these requirements a new type of polyurethane wound dressing which consists of a microporous top layer (pore size less than 0.7 mum) supported by a sublayer with a highly porous sponge-like structure containing micropores (pore size less than 10 mum) as well as macropores (pore size: 50-100 mum) was designed.  The pores of both layers are interconnected and form a continuous structure in the membrane. Membranes according to this design were prepared either by means of a two-step or by means of a one-step casting process.  Both fabrication methods are based on phase inversion techniques.  Asymmetric polyurethane Biomer membranes prepared by the two-step casting process were tested in vivo as full thickness skin substitutes using guinea pigs.  Neither wound dehydration nor infections were observed while the drainage capacity of the wound dressing was effective in preventing bullae formation.  Furthermore the wound dressing remained firmly adhered to the wound surface during the whole process of wound healing.  In contrast to all other commercial wound dressings currently available the polyurethane wound dressing applied on excised clean wounds did not need to be replaced during healing but could be left on the wound until full regeneration of the skin had taken place after which it was spontaneously repelled.
Department of Chemical Technology, University of Twente, The Netherlands.
W L
WL
Hinrichs
E J
EJ
Lommen
C R
CR
Wildevuur
J
J
Feijen
D000818:Animals; D001424:Bacterial Infections / Q000517:prevention & control; D003681:Dehydration / Q000517:prevention & control; D006168:Guinea Pigs; D008297:Male; D008422:Materials Testing; D008567:Membranes, Artificial; D008855:Microscopy, Electron, Scanning; D009779:Occlusive Dressings; D011140:Polyurethanes; D014945:Wound Healing