Histological and ultrastructural observations at the interface of expanded polytetrafluorethylene anterior cruciate ligament implants.
Anterior cruciate ligament (ACL) grafts made from expanded polytetrafluorethylene (ePTFE) were examined after failure (n = 7; 3 instabilities, 2 partial ruptures, and 2 complete ruptures) to provide information about secondary fixation mechanisms via ingrowth of the different tissues. The ultrastructural evaluation clearly evidenced the existence of two main interface areas of ePTFE ACL-replacement:  First, in areas without a dense cellular infiltrate there was interdigitating collagen producing a dense ePTFE-collagen network.  Additionally, in a few areas of the graft/bone-tunnel interface a fibrous cartilage or bone regenerate could be demonstrated to be in contact with the prosthesis.  Second, there was a dense infiltration of macrophages and multinuclear giant cells, partially containing birefringent material of implant origin, with and without a neosynovia-like reaction product, indicating a disturbance of tissue integration of the prosthesis.  In areas of inflammation there was no bone development and only few collagen interdigitation with the graft material.  This study provides further knowledge about mechanisms of secondary graft fixation due to tissue ingrowth.  The interdigitation of collagen fibers and ePTFE filaments provides interfaces which should be at least partially resistant against load.
Müller-Mai
C M
CM
Institute of Pathology, Free University of Berlin, Germany.
Gross
U M
UM
D000293:Adolescent; D000328:Adult; D016118:Anterior Cruciate Ligament / Q000473:pathology / Q000601:surgery / Q000648:ultrastructure*; D000070598:Anterior Cruciate Ligament Injuries; D001672:Biocompatible Materials; D005260:Female; D006801:Humans; D007720:Knee Prosthesis; D008297:Male; D011138:Polytetrafluoroethylene; D011475:Prosthesis Failure