Use of carbon dioxide laser in improving knot security in polyester sutures.
Knot slippage continues to be a serious concern in surgery.  This study explored the possibility of improving knot performance by exposing it to radiation from a CO 2 laser. The specimens were mounted in a special device and exposed in a predetermined position for precisely controlled lengths of time.  In the first set of experiments, the welding of ends was examined in nylon and polyester sutures.  Although the welding was easily achieved, the joint was found brittle and its strength lower than that of a surgical knot. In the next set of experiments, the work was performed at a more fundamental level using oriented, high density, polyester films.  The results showed that up to a certain level of exposure the tensile properties did not change, but beyond it a rapid decay took place. Shear tests on polyester sutures twisted together and then exposed to various levels of energy indicated that a bond of maximum strength developed at this exposure.  Mersilene sutures of size 3/0 containing a two throw square knot when exposed to energy of this level produced optimal results.  The knot strength increased by about 16% (from 13.4 N unexposed to 15.6 N exposed) and the slippage often known to occur in a two-throw knot was completely absent.  This work performed under standard atmospheric conditions provided a direction for greatly enhancing the performance of a two-throw knot in terms of both the security and the strength.(ABSTRACT TRUNCATED AT 250 WORDS)
Department of Textile Engineering, Chemistry and Science, North Carolina State University, Raleigh 27695.
B S
BS
Gupta
B L
BL
Milam
R R
RR
Patty
D006801:Humans; D007834:Lasers; D008422:Materials Testing; D011091:Polyesters; D013536:Suture Techniques; D013537:Sutures; D013718:Tensile Strength