Performance of retrieved Kuntscher intramedullary rods: improved corrosion resistance with contemporary material design.
Eighteen Kuntscher-type intramedullary rods were obtained after human implantation periods ranging from 1 to 23 years.  A clinical evaluation, metallurgical and chemical analyses of each implant were performed.  Idiopathic, implant-related pain was the most common reason for removal, but was not related to extent of implant corrosion.  When classified as early versus contemporary material compositions, a significant increase in surface corrosion, inclusion content and carbon content were demonstrated in rods made of the earlier composition of stainless steel.  Intergranular corrosion was associated with structural design, rather than material microcleanliness or composition.  While contemporary intramedullary fracture fixation provides excellent clinical results, the present investigation suggests that the performance of stainless steel implants may be improved through continued refinement of steel composition, careful consideration of structural design and fabrication techniques, and by routine removal of implants at the earliest opportunity.
Cook
S D
SD
Department of Orthopaedic Surgery, Tulane University School of Medicine, New Orleans, Louisiana 70112.
Brinker
M R
MR
Anderson
R C
RC
Tomlinson
R J
RJ
Butler
J C
JC
D001672:Biocompatible Materials; D003343:Corrosion; D005069:Evaluation Studies as Topic; D005594:Fracture Fixation, Intramedullary / Q000295:instrumentation*; D006244:Hardness; D006801:Humans; D011474:Prosthesis Design; D011475:Prosthesis Failure; D013193:Stainless Steel; D013314:Stress, Mechanical; D013499:Surface Properties; D013997:Time Factors