Influence of the modification of P/L ratio on a new formulation of acrylic bone cement.
The use of smaller powder/liquid (P/L) ratio favours the handling and wetting of poly(methyl methacrylate) (PMMA) beads in bone cement formulations. In this paper a P/L ratio of 1.86 is tested to overcome adhesion problems found in hydroxypropyl methacrylate (HPMA) modified bone cements and the influence on bone cement characteristics was analysed. The reduction of the P/L ratio leads to higher temperature peaks and shorter setting times, whereas the residual monomer content increases slightly. Water uptake obeys the diffusion laws, and the introduction of a more hydrophilic monomer gives rise to an increase of this parameter, which does not present significant changes with modification of the P/L ratio. Polymerization shrinkage is slightly greater because of the introduction of higher proportions of monomer in the formulation. Mechanical properties are similar to those obtained with conventional P/L ratios. The analysis of scanning electron microscopy (SEM) reveals an improvement of the adhesion between phases with respect to P/L = 2 formulations.
Pascual
B
B
Dpto. Ciencia y Tecnología de Polímeros, Facultad de Química, UPV/EHU, San Sebastián, Spain.
Gurruchaga
M
M
Ginebra
M P
MP
Gil
F J
FJ
Planell
J A
JA
Goñi
I
I
D000180:Acrylic Resins / Q000737:chemistry; D000327:Adsorption; D001843:Bone Cements / Q000737:chemistry; D006801:Humans; D066298:In Vitro Techniques; D008422:Materials Testing; D008689:Methacrylates; D008855:Microscopy, Electron, Scanning; D019904:Polymethyl Methacrylate; D011208:Powders; D013314:Stress, Mechanical; D013718:Tensile Strength; D014867:Water
D000180:Acrylic Resins; D001843:Bone Cements; D008689:Methacrylates; D011208:Powders; D014867:Water; D019904:Polymethyl Methacrylate; C032802:hydroxypropyl methacrylate