Adherence of Candida albicans to the surface of polymethylmethacrylate--E glass fiber composite used in dentures.
OBJECTIVE
The use of reinforcing fibers in dentures has raised concerns about possible increased adherence of yeasts to the surface. The aim of this in vitro study was to compare the adherence of Candida albicans to the surface of denture-base polymer and to E-glass fibers.


METHODS
Test specimens were made from an autopolymerized denture-base resin (Palapress) reinforced with preimpregnated unidirectional E-glass fibers, which were exposed at the surface. The test specimens were pretreated with parotid saliva and incubated without agitation in standardized yeast suspensions (10(8) colony-forming units per mL) in phosphate-buffered saline at 37 degrees C for 1 hour. The test specimens were then washed to remove nonadherent cells. After being air dried, they were sputter coated with gold-palladium for scanning electron microscopy (SEM). To compare the adherence to different surfaces, the number of yeast cells found either on the polymer matrix or on the glass fibers was counted from SEM fields (170 microns x 120 microns, 600 x) of randomly selected areas.


RESULTS
The mean density of yeast cell found on the surface of the polymer matrix was significantly higher (P < 0.001) than that on the surface of glass fibers. The number of adherent yeast cells found at the interface between the fibers and polymer matrix was high.


CONCLUSIONS
The adherence of C albicans to E-glass fibers was lower than to polymer matrix in the denture composite. If fibers are exposed only during polishing of the composite, the reinforcing material appears not to increase the adherence of this common oral yeast. However, areas with permanently exposed fibers may provide mechanical retention for yeast cells at the interface of the components.
Waltimo
T
T
Scandinavian Institute of Dental Materials, Haslum, Norway. Tuomas.Waltimo@Helsinki.fi
Tanner
J
J
Vallittu
P
P
Haapasalo
M
M
D000180:Acrylic Resins; D000704:Analysis of Variance; D002176:Candida albicans / Q000502:physiology*; D002448:Cell Adhesion; D003775:Dental Polishing; D003819:Denture Bases / Q000382:microbiology*; D005898:Glass
D000180:Acrylic Resins; C009753:fiberglass