Crosslinking characteristics of an injectable poly(propylene fumarate)/beta-tricalcium phosphate paste and mechanical properties of the crosslinked composite for use as a biodegradable bone cement.
We investigated the crosslinking characteristics of an injectable composite paste of poly(propylene fumarate) (PPF), N-vinyl pyrrolidinone (N-VP), benzoyl peroxide (BP), sodium chloride (NaCl), and beta-tricalcium phosphate (beta-TCP). We examined the effects of PPF molecular weight, N-VP/PPF ratio, BP/PPF ratio, and NaCl weight percent on the crosslinking temperature, heat release upon crosslinking, gel point, and the composite compressive strength and modulus. The maximum crosslinking temperature did not vary widely among formulations, with the absolute values falling between 38 degrees and 48 degrees C, which was much lower than that of 94 degrees C for poly(methyl methacrylate) bone cement controls tested under the same conditions. The total heat released upon crosslinking was decreased by an increase in PPF molecular weight and a decrease in N-VP/PPF ratio. The gel point was affected strongly by the PPF molecular weight, with a decrease in PPF molecular weight more rapidly leading to a gel point. An increase in initiator concentration had the same effect to a lesser degree. The time frame for curing was varied from 1-121 min, allowing the composite to be tailored to specific applications. The compressive strength and compressive modulus values increased with decreasing N-VP/PPF, increasing NaCl content, and increasing BP/PPF ratio. For all formulations, the compressive strength values fell between 1 and 12 MPa, and the compressive modulus values fell between 23 and 265 MPa. These data suggest that injectable PPF/beta-TCP pastes can be prepared with handling characteristics appropriate for clinical orthopedic applications and that the mechanical properties of the cured composites are suitable for trabecular bone replacement.
Cox Laboratory for Biomedical Engineering, Institute of Biosciences and Bioengineering and Department of Chemical Engineering, Rice University, Houston, Texas 77251-1892, USA.
S J
SJ
Peter
P
P
Kim
A W
AW
Yasko
M J
MJ
Yaszemski
A G
AG
Mikos
D001673:Biodegradation, Environmental; D001843:Bone Cements / Q000737:chemistry*; D002130:Calcium Phosphates / Q000737:chemistry*; D002152:Calorimetry, Differential Scanning; D055598:Chemical Phenomena; D002627:Chemistry, Physical; D019245:Compressive Strength; D003432:Cross-Linking Reagents; D005650:Fumarates / Q000737:chemistry*; D005782:Gels; D008422:Materials Testing; D008970:Molecular Weight; D009824:Ointments; D011126:Polypropylenes / Q000737:chemistry*; D013696:Temperature
D001843:Bone Cements; D002130:Calcium Phosphates; D003432:Cross-Linking Reagents; D005650:Fumarates; D005782:Gels; D009824:Ointments; D011126:Polypropylenes; C485828:alpha-tricalcium phosphate; C097850:poly(propylene fumarate); C485830:tetracalcium phosphate; C485838:calcium phosphate, monobasic, anhydrous; C020243:calcium phosphate; C485829:calcium phosphate, dibasic, anhydrous