Wear-testing of a temporomandibular joint prosthesis: UHMWPE and PTFE against a metal ball, in water and in serum.
For a temporomandibular joint prosthesis, an estimation of the wear rate was needed, prior to patient application. Therefore, we determined the in vitro wear rate of the ball-socket articulation of this prosthesis, consisting of a metal head and an ultra-high molecular weight polyethylene (UHMWPE) cup. The basic testing configuration consisted of one 8-mm diameter stainless-steel ball, rotating between two conforming cups with a minimum thickness of 5 mm. For validation of the testing apparatus, two cup materials, in two lubricants, were tested. Both cup materials, UHMWPE and polytetrafluoroethylene (PTFE) were tested in deionized water, as well as in a serum-based solution. For UHMWPE in serum, eight samples were tested, for the other combinations four samples. For UHMWPE, the tests ran for 7 million cycles, for PTFE between 0.8 and 1.7 million cycles. For UHMWPE, the wear rate was 0.006 and 0.47 (mm3/10(6) cycles), in water and in serum, respectively. For PTFE, the wear rate was 2.8 and 47 (mm3/10(6) cycles), in water and in serum, respectively. For reason that testing in serum simulates the in vivo situation best, it was concluded that the wear rate of the TMJ prosthesis articulation is 0.47 (mm3/10(6) cycles), which is considered acceptable.
Van Loon
J P
JP
Department of Oral & Maxillofacial Surgery, University Hospital Groningen, The Netherlands. j.p.van.loon@kchir.azg.nl
Verkerke
G J
GJ
de Bont
L G
LG
Liem
R S
RS
D001672:Biocompatible Materials; D001696:Biomechanical Phenomena; D001769:Blood; D006801:Humans; D007595:Joint Prosthesis; D008422:Materials Testing; D008670:Metals; D008970:Molecular Weight; D055585:Physical Phenomena; D010825:Physics; D011095:Polyethylenes; D011138:Polytetrafluoroethylene; D011474:Prosthesis Design; D013704:Temporomandibular Joint; D014867:Water
D001672:Biocompatible Materials; D008670:Metals; D011095:Polyethylenes; D014867:Water; D011138:Polytetrafluoroethylene