Type of motion and lubricant in wear simulation of polyethylene acetabular cup.
The wear of ultra-high molecular weight polyethylene, the most commonly used bearing material in prosthetic joints, is often substantial, posing a significant clinical problem. For a long time, there has been a need for simple but still realistic wear test devices for prosthetic joint materials. The wear factors produced by earlier reciprocating and unidirectionally rotating wear test devices for polyethylene are typically two orders of magnitude too low, both in water and in serum lubrication. Wear is negligible even under multidirectional motion in water. A twelve-station, circularly translating pin-on-disc (CTPOD) device and a modification of the established biaxial rocking motion hip joint simulator were built. With these simple and inexpensive devices, and with the established three-axis hip joint simulator, realistic wear simulation was achieved. This was due to serum lubrication and to the fact that the direction of sliding constantly changed relative to the polyethylene specimen. The type and magnitude of load was found to be less important. The CTPOD tests showed that the subsurface brittle region, which results from gamma irradiation sterilization of polyethylene in air, has poor wear resistance. Phospholipid and soy protein lubrication resulted in unrealistic wear. The introduction of devices like CTPOD may boost wear studies, rendering them feasible without heavy investment.
Saikko
V
V
Department of Mechanical Engineering, Helsinki University of Technology, Finland.
Ahlroos
T
T
D015060:1,2-Dipalmitoylphosphatidylcholine; D000077:Acetabulum / Q000502:physiology; D006622:Hip Prosthesis; D006801:Humans; D008153:Lubrication; D008422:Materials Testing; D008954:Models, Biological; D009068:Movement; D011095:Polyethylenes; D011474:Prosthesis Design / Q000295:instrumentation; D013314:Stress, Mechanical; D013499:Surface Properties
D011095:Polyethylenes; D015060:1,2-Dipalmitoylphosphatidylcholine