Microbiologically induced corrosion of aluminum alloys in fuel-oil/aqueous system.
To investigate the microbiologically induced corrosion of aluminum alloys in fuel-oil/aqueous system, aluminum alloys A356, AA 5052, AA 5083 and AA 6061 were chosen as the test alloys and Cladosporium and several fuel-oil contaminated microbes isolated in Taiwan were used as test organisms. Aluminum alloy AA 5083 in fuel-oil/aqueous system was the most susceptible material for microbial corrosion, then followed by aluminum alloys AA 5052 and A356, and AA 6061 was more resistant to microbial aggression. Mixed culture had high capability of corrosion, then followed by Penicillium sp. AM-F5, Fusarium sp. AM-F1, Pseudomonas aeruginosa AM-B5, Ps. fluorescens AM-B9, C. resinae ATCC 22712, Penicillium sp. AM-F2, Candida sp. AM-Y1 and Ps. aeruginosa AM-B11. From energy dispersive spectrometer analysis, aluminum and magnesium contents decreased in the corrosion area, while chlorine and sulfur contents increased. The major organic acid produced in fuel-oil/aqueous system was acetic acid, and the total organic acids content had a positive correlation with the degree of microbial corrosion.
Yang
S S
SS
Department of Agricultural Chemistry, National Taiwan University, Taipei, ROC.
Lin
J Y
JY
Lin
Y T
YT
D000497:Alloys / Q000737:chemistry*; D000535:Aluminum / Q000737:chemistry*; D001419:Bacteria / Q000254:growth & development*; D003343:Corrosion; D005648:Fuel Oils; D005658:Fungi / Q000254:growth & development*; D006863:Hydrogen-Ion Concentration; D008274:Magnesium / Q000494:pharmacology
D000497:Alloys; D005648:Fuel Oils; D000535:Aluminum; D008274:Magnesium