Apatite formation on/in hydrogel matrices using an alternate soaking process (III): effect of physico-chemical factors on apatite formation on/in poly(vinyl alcohol) hydrogel matrices.
The aim of this study is to clarify the physico-chemical factors which influence apatite formation on/in a hydrogel during a novel alternate soaking process. A poly(vinyl alcohol) (PVA) gel was used as a model matrix. The amount of apatite formed on/in PVA gels decreased with an increase in the reaction temperature during the same reaction cycles. This suggested that the equilibrium swelling ratios decreased with increasing reaction temperatures; that is, the diffusion of calcium and phosphate ions reduced at high reaction temperature. However, the crystallinity of apatite formed on/in PVA gels was greater at higher reaction temperatures. The amount of apatite formed on/in PVA gels increased with an increase in the calcium and phosphate solution concentrations, and increased by shaking at the first three reaction cycles. A few influences could be observed when the solution volume was changed, however, the soaking order was not effective in this study. These results indicate that the amount of apatite formation on/in PVA gels can be controlled by changing the reaction temperature and the Ca- and P-solution concentrations, and that the crystallinity of apatite can be also changed by controlling the reaction temperatures.
Taguchi
T
T
Department of Applied Chemistry and Chemical Engineering, Faculty of Engineering, Kagoshima University, Japan.
Kishida
A
A
Akashi
M
M
D001031:Apatites / Q000138:chemical synthesis*; D001672:Biocompatible Materials / Q000737:chemistry; D011142:Polyvinyl Alcohol / Q000737:chemistry*; D012996:Solutions / Q000737:chemistry; D013696:Temperature
D001031:Apatites; D001672:Biocompatible Materials; D012996:Solutions; C062364:polyvinyl alcohol hydrogel; D011142:Polyvinyl Alcohol