Atomic Force Microscopy and Wettability Study of Oxidized Patterns at the Surface of Polystyrene.
The surface properties of patterned surfaces made by a combination of photolithography and oxygen plasma treatment of polystyrene (PS) were investigated. PS and plasma-treated PS (PSox) were first characterized using X-ray photoelectron spectroscopy and the study of wetting dynamics (Wilhelmy plate method) in water and in solutions of different pH. The results indicated that the PSox surface may be viewed as covered with a polyelectrolyte-like gel, which swells depending on pH. It was then shown, using atomic force microscopy (AFM), that the adhesion force measured on PS with a silicon tip in water was higher compared with that measured on PSox. This feature allowed imaging of the oxidation patterns using the adhesion mapping mode. The origin of the pulloff force contrast, which could not be explained by combining Johnson-Kendall-Roberts theory and thermodynamic considerations, was attributed to repulsion between the tip and hydrated polymer chains present on the oxidized surface. Imaging was also performed in the lateral force mode, a higher friction being recorded on PS than on PSox. Copyright 1999 Academic Press.
Dupont-Gillain
CC
Unité de chimie des interfaces, Unité de chimie et de physique des hauts polymères, Université Catholique de Louvain, Place Croix du Sud 2/18, Louvain-la-Neuve, B-1348, Belgium
Nysten
B
Hlady
V
Rouxhet
PG