An evaluation of the transition temperature range of super-elastic orthodontic NiTi springs using differential scanning calorimetry.
Differential scanning calorimetry (DSC) was used to determine the transition temperature ranges (TTR) of four types of super-elastic orthodontic nickel-titanium coil springs (Sentalloy). A knowledge of the TTR provides information on the temperature at which a NiTi wire or spring can assume superelastic properties and when this quality disappears. The spring types in this study can be distinguished from each other by their characteristic TTR during cooling and heating. For each tested spring type a characteristic TTR during heating (austenite transformation) and cooling (martensite transformation) was evaluated. The hysteresis of the transition temperature, found between cooling and heating, was 3.4-5.2 K. Depending on the spring type the austenite transformation started (As) at 9.7-17.1 degrees C and finished (Af) at 29.2-37 degrees C. The martensite transformation starting temperature (Ms) was evaluated at 32.6-25.4 degrees C, while Mf (martensite transformation finishing temperature) was 12.7-6.5 degrees C. The results show that the springs become super-elastic when the temperature increases and As is reached. They undergo a loss of super-elastic properties and a rapid decrease in force delivery when they are cooled to Mf. For the tested springs, Mf and As were found to be below room temperature. Thus, at room temperature and some degrees lower, all the tested springs exert super-elastic properties. For orthodontic treatment this means the maintenance of super-elastic behaviour, even when mouth temperature decreases to about room temperature as can occur, for example, during meals.
Barwart
O
O
Institute of Pharmacognosy, University of Innsbruck, Austria.
Rollinger
J M
JM
Burger
A
A
D001831:Body Temperature; D002152:Calorimetry, Differential Scanning; D003080:Cold Temperature; D003722:Dental Alloys / Q000737:chemistry*; D004548:Elasticity; D005069:Evaluation Studies as Topic; D006358:Hot Temperature; D006801:Humans; D008422:Materials Testing; D009532:Nickel / Q000737:chemistry*; D009969:Orthodontic Wires; D013314:Stress, Mechanical; D013696:Temperature; D014025:Titanium / Q000737:chemistry*
D003722:Dental Alloys; C040654:titanium nickelide; C093824:Martensite; C093826:Austenite; D009532:Nickel; D014025:Titanium