Polymerization with the argon laser: curing time and shear bond strength.
The objective of this study was to determine the efficiency of an argon laser in polymerizing a light-cured orthodontic adhesive. Metal brackets were bonded to 185 premolars, divided into 5 different protocol groups of 37 each as follows: light 40-second buccal, light 40-second lingual, laser 5-second lingual, laser 10-second lingual, and laser 15-second lingual. All bonded specimens were placed in distilled water for 30 days at 37 degrees C followed by thermal cycling for 24 hours. Brackets were detached using a shearpeel load delivered by an Instron machine. The site of bond failure was examined under 10x magnification. The difference in the shear-peel bond strength between the light 40-second buccal (13.31 MPa) and the light 40-second lingual (11.95 MPa) groups was not statistically significant. The mean shear-peel bond strengths for the laser cured groups were quite similar for the 5-, 10- and 15-second laser groups (10.86, 11.32, and 10.80 MPa). The difference in mean lingual bond strength between the light 40-second and laser 5-second groups was not statistically significant (t = 1.26; P = .212). The adhesive remnant index analysis revealed principally cohesive bond failures. An increased frequency of enamel fractures at debond was noted in the lingual light-cured and 10-second laser-cured groups, at 35.1% (13/37) and 21.6% (8/ 37), respectively. All other groups displayed enamel fractures of 16.2% (6/37). A 5-second cure using an argon laser produced bond failure loads comparable to those obtained after 40 seconds of conventional light cure, with less than half the frequency of enamel fracture at debond.
Lalani
N
N
University of Western Ontario, London, Canada.
Foley
T F
TF
Voth
R
R
Banting
D
D
Mamandras
A
A
D000180:Acrylic Resins / Q000737:chemistry / Q000528:radiation effects*; D000704:Analysis of Variance; D001128:Argon; D001641:Bicuspid / Q000648:ultrastructure; D017438:Bisphenol A-Glycidyl Methacrylate / Q000737:chemistry / Q000528:radiation effects*; D001840:Dental Bonding; D003743:Dental Enamel / Q000293:injuries / Q000648:ultrastructure; D004868:Equipment Failure; D006801:Humans; D007834:Lasers; D008027:Light; D016910:Orthodontic Brackets; D011108:Polymers / Q000737:chemistry / Q000528:radiation effects*; D019279:Resin Cements / Q000737:chemistry / Q000528:radiation effects*; D013193:Stainless Steel; D013314:Stress, Mechanical; D013499:Surface Properties; D013816:Thermodynamics; D013997:Time Factors; D014867:Water
D000180:Acrylic Resins; D011108:Polymers; D019279:Resin Cements; D014867:Water; D013193:Stainless Steel; C065742:Transbond; D017438:Bisphenol A-Glycidyl Methacrylate; D001128:Argon