A new peptide-based urethane polymer: synthesis, biodegradation, and potential to support cell growth in vitro.
A novel non-toxic biodegradable lysine-di-isocyanate (LDI)-based urethane polymer was developed for use in tissue engineering applications. This matrix was synthesized with highly purified LDI made from the lysine diethylester. The ethyl ester of LDI was polymerized with glycerol to form a prepolymer. LDI-glycerol prepolymer when reacted with water foamed with the liberation of CO2 to provide a pliable spongy urethane polymer. The LDI-glycerol matrix degraded in aqueous solutions at 100, 37, 22, and 4 degrees C at a rate of 27.7, 1.8, 0.8, and 0.1 mM per 10 days, respectively. Its thermal stability in water allowed its sterilization by autoclaving. The degradation of the LDI-glycerol polymer yielded lysine, ethanol, and glycerol as breakdown products. The degradation products of LDI-glycerol polymer did not significantly affect the pH of the solution. The glass transition temperature (Tg) of this polymer was found to be 103.4 degrees C. The physical properties of the polymer network were found to be adequate to support the cell growth in vitro, as evidenced by the fact that rabbit bone marrow stromal cells (BMSC) attached to the polymer matrix and remained viable on its surface. Culture of BMSC on LDI-glycerol matrix for long durations resulted in the formation of multilayered confluent cultures, a characteristic typical of bone cells. Furthermore, cells grown on LDI-glycerol matrix did not differ phenotypically from the cells grown on the tissue culture polystyrene plates as assessed by the cell growth, and expression of mRNA for collagen type I, and transforming growth factor-beta1 (TGF-beta1). The observations suggest that biodegradable peptide-based urethane polymers can be synthesized which may pave their way for possible use in tissue engineering applications.
Zhang
J Y
JY
Department of Chemical & Petroleum Engineering, University of Pittsburgh, PA 15261-1964, USA.
Beckman
E J
EJ
Piesco
N P
NP
Agarwal
S
S
D020341:Absorbable Implants; D000818:Animals; D001672:Biocompatible Materials / Q000138:chemical synthesis / Q000737:chemistry*; D001854:Bone Marrow Cells / Q000166:cytology* / Q000378:metabolism; D018786:Bone Substitutes / Q000737:chemistry*; D002448:Cell Adhesion; D002455:Cell Division; D002478:Cells, Cultured; D003094:Collagen / Q000096:biosynthesis; D008239:Lysine / Q000031:analogs & derivatives* / Q000138:chemical synthesis / Q000737:chemistry; D008422:Materials Testing; D011140:Polyurethanes / Q000138:chemical synthesis / Q000737:chemistry*; D012333:RNA, Messenger / Q000096:biosynthesis; D011817:Rabbits; D017154:Stromal Cells / Q000166:cytology / Q000378:metabolism; D016212:Transforming Growth Factor beta / Q000096:biosynthesis
D001672:Biocompatible Materials; D018786:Bone Substitutes; D011140:Polyurethanes; D012333:RNA, Messenger; D016212:Transforming Growth Factor beta; C412587:lysine diisocyanate-glycerol poly(urea-urethane); D003094:Collagen; D008239:Lysine