Thermoreversible copolymer gels for extracellular matrix.
To improve the properties of a reversible synthetic extracellular matrix based on a thermally reversible polymer, copolymers of N-isopropylacrylamide and acrylic acid were prepared in benzene with varying contents of acrylic acid (0 to 3%) and the thermal properties were evaluated. The poly(N-isopropylacrylamide) and copolymers made with acrylic acid had molecular weights from 0.8 to 1.7 x10(6) D. Differential scanning calorimetry (DSC) showed the high-molecular-weight acrylic acid copolymers had similar onset temperatures to the homopolymers, but the peak width was considerably increased with increasing acrylic acid content. DSC and cloud point measurements showed that polymers with 0 to 3% acrylic acid exhibit a lower critical solution temperature (LCST) transition between 30 degrees and 37 degrees C. In swelling studies, the homopolymer showed significant syneresis at temperatures above 31 degrees C. Copolymers with 1 and 1.5% showed syneresis beginning at 32 degrees and 37 degrees C, respectively. At 37 degrees C the copolymers with 1.5-3% acrylic acid showed little or no syneresis. Due to the high water content and a transition near physiologic conditions (below 37 degrees C), the polymers with 1.5-2.0% acrylic acid exhibited properties that would be useful in the development of a refillable synthetic extracellular matrix. Such a matrix could be applied to several cell types, including islets of Langerhans, for a biohybrid artificial pancreas.
Vernon
B
B
Department of Bioengineering, University of Utah, Salt Lake City, Utah 84112, USA.
Kim
S W
SW
Bae
Y H
YH
D000178:Acrylamides / Q000138:chemical synthesis; D000179:Acrylates / Q000032:analysis / Q000138:chemical synthesis; D002152:Calorimetry, Differential Scanning; D005109:Extracellular Matrix; D005782:Gels; D006358:Hot Temperature; D008970:Molecular Weight; D019397:Pancreas, Artificial; D011108:Polymers; D012996:Solutions; D013696:Temperature; D014867:Water / Q000032:analysis
D000178:Acrylamides; D000179:Acrylates; D005782:Gels; D011108:Polymers; D012996:Solutions; D014867:Water; C067295:N-isopropylacrylamide; C036658:acrylic acid