Anodic oxidation and hydrothermal treatment of titanium results in a surface that causes increased attachment and altered cytoskeletal morphology of rat bone marrow stromal cells in vitro.
Previous studies have suggested the usefulness of a new coating method-namely, the forming of a thin hydroxyapatite (HA) layer on commercially pure titanium (cpTi) by anodization and hydrothermal treatment-for use as a dental root implant material. In vivo and in vitro studies confirmed that an HA layer on cpTi (HA/cpTi) implants showed good compatibility with bone tissue, rat bone marrow stromal (RBM) cells, and immune cells. The aim of the present investigation was to further characterize the in vitro early cellular behavior of RBM cells on HA/cpTi implants. Therefore, in this study we performed surface analysis, analysis of cell initial attachment, and analysis of cell morphology and the cytoskeleton. Drops of distilled water or cell culture medium showed smaller contact angles with HA/cpTi than with cpTi. RBM cells were cultured for 30, 60, and 120 min on HA/cpTi and cpTi, and the level of cell adhesion was shown to increase with time on both substrates. However, cell adhesion on HA/cpTi was significantly higher than on cpTi at 60 and 120 min. Especially at 120 min, when compared with cpTi, the cell morphology on the surface of HA/cpTi not only adopted a flattened and spreading form, but also extended filopodium-like processes with irregular edges that were intimately adapted to the surface of the HA microcrystals. The cytoskeleton on HA/cpTi showed well-formed actin filaments that were parallel to each other and the long axis of RBM cells. The actin filaments of RBM cells on the HA/cpTi surface were localized to the periphery (corresponding to the edge of the filopodium-like processes) well after 120 min. This suggests that actin filaments of RBM cells need to be anchored at the HA/cpTi surface and the numerous HA microcrystals precipitated on the HA/cpTi surface. These findings were similar to the scanning electron microscopic morphology. The peripheral anchorage provide sufficient strength of attachment to allow recognization of actin filaments upon HA/cpTi. The surface of HA/cpTi was more hydrophilic and exhibited markedly improved wettability compared to untreated cpTi, and higher levels of early cell attachment were observed on surfaces after anodization and hydrothermal treatment than on surfaces with untreated cpTi. The results of in vitro experiments suggest that this new method for forming a thin HA layer on the surface of cpTi could be useful to ensure excellent cellular behavior on implant surfaces. The characterization of cell morphology on the thin HA layer formed by anodization and hydrothermal treatment on cpTi implant material suggests that physicochemical or biological conditioning of the implant surface involves implant surface topography.
Takebe
J
J
Department of Fixed Prosthodontics, School of Dentistry, Iwate Medical University, 1-3-27 Chuodori, Morioka-shi, Iwate 020-8505, Japan. takebej@iwate-med.ac.jp
Itoh
S
S
Okada
J
J
Ishibashi
K
K
D000818:Animals; D001672:Biocompatible Materials; D001854:Bone Marrow Cells / Q000166:cytology*; D002448:Cell Adhesion; D003599:Cytoskeleton / Q000648:ultrastructure; D017886:Durapatite; D066298:In Vitro Techniques; D008297:Male; D008422:Materials Testing; D018613:Microscopy, Confocal; D008855:Microscopy, Electron, Scanning; D010084:Oxidation-Reduction; D051381:Rats; D017208:Rats, Wistar; D017154:Stromal Cells / Q000166:cytology; D013499:Surface Properties; D014025:Titanium
D001672:Biocompatible Materials; D017886:Durapatite; D014025:Titanium