The yellow-orange oxonitridosilicate oxide Ce4[Si4O4N6]O was obtained by the reaction of cerium metal with Si(NH)2 and SiO2 in a radiofrequency furnace at 1560 degrees C. The crystal structure was determined by single-crystal X-ray diffraction (a = 1033.67(6) pm, P2,3, Z = 4, R1 = 0.0412, wR2 = 0.0678) and powder neutron diffraction. In the solid there are complex cations [Ce4O]10+ that are enveloped by a hyperbolical layer structure [Si4O4N6]10-. The layer is built up by corner-sharing SiON3 tetrahedra of Q3 type. The oxygen atoms of the SiON3 tetrahedra are terminally bound to Si, while all nitrogen atoms bridge two neighboring Si centres. The crystallographic differentiation of O and N was unequivocally possible by a careful evaluation of the single-crystal X-ray diffraction data combined with lattice-energy calculations by using the MAPLE concept (Madelung part of lattice energy). Furthermore the results were confirmed by the chemical analyses. Subsequently, the determined N/O distribution and their crystallographic ordering was proved by neutron powder diffraction. In accordance with the molar ratio Si:(O,N) = 2:5 the [Si4O4N6]10- network may be classified as a layer silicate. In this specific case a hyperbolically corrugated topology of the layers is observed; this is correlated to periodic nodal surface (PNS) representatives.
Irran
E
Department of Chemistry, University of Munich (LMU), Germany.
Kollisch
K
Leoni
S
Nesper
R
Henry
PF
Weller
MT
Schnick
W