Tissue engineered cartilage repair using cryopreserved and noncryopreserved chondrocytes.
The objective of this study was to reconstruct full thickness cartilage defects in rabbit knees with in vitro engineered cartilage tissue based on noncryopreserved and cryopreserved chondrocytes in polymer fleece scaffolds. Osteochondral defects in rabbits were filled with polymer cylinders with noncryopreserved or cryopreserved allogeneic chondrocytes and compared with empty defects and defects filled with polymers alone. The defects were evaluated macroscopically and histologically 4 and 12 weeks after surgery. Transplant samples were graded using a semiquantitative score system. Successful healing was defined as complete integration of a hyalinelike and structurally intact cartilage into the defect and occurred in 71% of the group with noncryopreserved chondrocytes after 4 weeks and 100% of the rabbit knees after 12 weeks, whereas hyalinelike cartilage was seen in 71% of the group with cryopreserved chondrocytes after 4 weeks, and in 85% after 12 weeks. No newly formed cancellous bone was present in the subchondral bone. In the control groups, no cartilagelike tissue was seen. Transplantation of chondrocytes in polymer fleece constructs is a suitable approach for joint cartilage repair. Noncryopreserved chondrocytes are preferred to cryopreserved chondrocytes because of their regenerative potential. In vitro engineered cartilage offers broad opportunities for optimization of cartilage transplantation based on the controlled use of morphogenic and biologically active factors such as transforming growth factor-beta and bone morphogenetic proteins.
Perka
C
C
Department of Orthopaedics, Charité University Hospital, Humboldt University of Berlin, Germany.
Sittinger
M
M
Schultz
O
O
Spitzer
R S
RS
Schlenzka
D
D
Burmester
G R
GR
D000818:Animals; D002358:Cartilage, Articular / Q000473:pathology*; D019902:Chondrocytes / Q000637:transplantation*; D015925:Cryopreservation; D005069:Evaluation Studies as Topic; D005240:Feasibility Studies; D008297:Male; D011108:Polymers; D011817:Rabbits; D011897:Random Allocation
D011108:Polymers