title: Effect of surface penetrating sealant on surface texture and microhardness of composite resins.
abstract: The application of Fortify (Bisco, Lombard, IL), an unfilled resin, to the surface of composite resin restorations is intended to fill in defects in the surface that persist despite polishing, improve marginal integrity, and increase these materials' resistance to abrasion. The aim of this study was to observe the surface texture by scanning electron microscopy and measure the microhardness of the surface. For each sample of composite resin covered with glaze, 40 measurements were made of the thickness of the resin. Measurements of the Vickers microhardness included three samples of composite resin, three samples of glaze, and six samples of composite resin covered with glaze. A relationship was established between microhardness and thickness. Scanning electron microscopy showed a noticeable improvement in the surface texture. Nevertheless, areas were seen in which glaze seemed very thin or even completely absent. Measurements of the thickness ranged from 0-70 microm. The mean microhardness of composite resin was 65.8 +/- 0.7, while the mean hardness of glaze was 7.3 +/- 0.7. The microhardness of the double layer was reduced, depending on the thickness of the glazing resin. The capacity of glaze to mask surface defects of composite resin was shown, but it was difficult to obtain a regular surface with liquid resin. The application of this product caused a decrease of the microhardness of the composite resin's surface.
authors.affiliation: Laboratory of Dental Biomaterials and Experimental Odontology, University of Nice-Sophia Antipolis, Nice, France.
authors.forename: M F
authors.initials: MF
authors.lastname: Bertrand
authors.forename: E
authors.initials: E
authors.lastname: Leforestier
authors.forename: M
authors.initials: M
authors.lastname: Muller
authors.forename: L
authors.initials: L
authors.lastname: Lupi-Pégurier
authors.forename: M
authors.initials: M
authors.lastname: Bolla
mesh_terms: D003188:Composite Resins; D006245:Hardness Tests; D008855:Microscopy, Electron, Scanning; D010895:Pit and Fissure Sealants; D013499:Surface Properties
chemical_list: D003188:Composite Resins; D010895:Pit and Fissure Sealants