Influence of filler content on static properties of glass-reinforced bone cement.
A commercial acrylic bone cement was modified by the incorporation of different weight fractions of glass spheres. The influence of the filler proportion on the mechanical behavior was assessed. Composite cements were prepared by replacing part of the powder phase of the cement by an equivalent weight of glass particles, which resulted in an increase in the liquid-to-powder (L/P) ratio of the polymeric matrix. Dynamic mechanical analysis revealed an increase in residual monomer content with increasing filler proportion as a consequence of the increase in L/P. Flexural, compressive, and fracture properties of the cement with varying amounts of glass particles were measured. It was found that up to 50 wt% glass particles could be added with significant increases in flexural modulus and fracture toughness. The mechanical behavior was explained in terms of both the reinforcing effect of the filler and the plasticizing effect of the monomer. Glass-filled bone cements displayed superior workability compared with the standard cement, which was attributed to a decrease in the viscosity of the initial mix and the surface characteristics of the glass particles. The observed increase in fracture toughness could be rationalized through the application of proposed mechanisms for toughening of particle-reinforced polymers.
Vallo
C I
CI
Institute of Materials Science and Technology (INTEMA), Universidad Nacional de Mar del Plata-National Research Council (CONICET), Av. Juan B. Justo 4302, (7600) Mar del Plata, Argentina. civallo@fi.mdp.edu.ar
D000180:Acrylic Resins; D000465:Algorithms; D001843:Bone Cements; D002152:Calorimetry, Differential Scanning; D005898:Glass; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D011108:Polymers; D013314:Stress, Mechanical; D013499:Surface Properties; D013696:Temperature; D014783:Viscosity
D000180:Acrylic Resins; D001843:Bone Cements; D011108:Polymers