Evaluation of multiphase implants for repair of focal osteochondral defects in goats.
The use of biodegradable scaffolds for articular cartilage repair has been investigated by numerous researchers. The objective of this screening study was to examine how the mechanical and physical properties of four multiphase implants can affect the cartilage healing response. Multiphase implant prototypes were prepared using poly(D,L)lactide-co-glycolide as the base material. PGA fibers (FR), 45S5 Bioglass (BG) and medical grade calcium sulfate (MGCS) were used as additives to vary stiffness and chemical properties. Osteochondral defects (3 mm dia. and 4 mm in depth) were created bilaterally in the medial femoral condyle (high-weight bearing) and the distal medial portion of the patellar groove (low-weight bearing) of 16 Spanish goats. Half of the implants were loaded with autologous costochondral chondrocytes. Defect sites (total n = 64, 4 sites/treatment) were randomly treated and allowed to heal for 16 weeks, fully weight bearing. At euthanasia, gross evaluations and biomechanical testing were conducted. Histological sections of the defect sites were stained with H and E, Safranin O/Fast Green or processed to analyze collagen architecture. Sections were semi-quantitatively scored for repair tissue structure. Qualitative evaluations showed that all groups had a high percentage of hyaline cartilage and good bony restoration, with new tissue integrating well with the native cartilage. Gross and histology scoring indicated a significantly higher score for defect healing in the condyle than in the patellar groove, but no difference in healing for implant types or addition/omission of cells was found. This investigation demonstrates that focal, osteochondral defects in caprine distal femurs treated with various implant constructs were repaired with hyaline-like cartilage and good underlying bone. The multiphase implants show potential for treatment of osteochondral defects and long-term studies need to be undertaken to confirm the longevity of the regenerated tissue.
Niederauer
G G
GG
OsteoBiologics, Inc., San Antonio, TX 78249-3308, USA. gabi@obi.com
Slivka
M A
MA
Leatherbury
N C
NC
Korvick
D L
DL
Harroff
H H
HH
Ehler
W C
WC
Dunn
C J
CJ
Kieswetter
K
K
D000818:Animals; D001672:Biocompatible Materials; D001696:Biomechanical Phenomena; D002358:Cartilage, Articular / Q000254:growth & development*; D006041:Goats; D019344:Lactic Acid; D008297:Male; D011100:Polyglycolic Acid; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011108:Polymers
D001672:Biocompatible Materials; D011108:Polymers; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011100:Polyglycolic Acid; D019344:Lactic Acid