Defining the heating characteristics of ferromagnetic implants using calorimetry.
The induction heating of small, cylindrical ferromagnetic implants for localized tumors is currently under investigation. These thermal rods are implanted within a lesion in 1 cm(2) arrays and subsequently exposed to an externally applied alternating magnetic field. Implants absorb energy from the field and transfer it as heat to the surrounding tissue. To achieve a uniform temperature rise throughout the tissue volume and to account for any field-rod misalignment, 400 mW of power per implant is used as the design specification. The temperature to necrose cells must be greater than 46 degrees C. A calorimeter was constructed to confirm that the rod power output specification is satisfied at temperatures adequate for inducing cell death. The rods were designed to undergo a ferromagnetic to paramagnetic transition at temperatures of 55 degrees C, 60 degrees C, 65 degrees C, and 70 degrees C; this transition produces rods that are temperature self-regulating. Calorimetric results demonstrated that 55 degrees C, 60 degrees C, 65 degrees C, and 70 degrees C rods provided 400 mW at 47-51 degrees C, 51-53.5 degrees C, 57 degrees C, and 62.5-63.5 degrees C, respectively. Thermal rods provide sufficient power output at the temperatures necessary to cause thermal ablation of tumors. The higher-temperature rods give a greater margin to ensure that necrotizing temperatures can be achieved throughout the rod array even with minor misalignment.
Case
J A
JA
Department of Biomedical Engineering, University of Iowa, IA City, Iowa 52242, USA.
Tucker
R D
RD
Park
J B
JB
D000465:Algorithms; D000497:Alloys; D002151:Calorimetry; D003035:Cobalt; D003625:Data Collection; D008280:Magnetics; D010165:Palladium; D019736:Prostheses and Implants; D013696:Temperature; D013816:Thermodynamics
D000497:Alloys; D003035:Cobalt; D010165:Palladium