title: Comparison of the tensile bond strength of high-noble, noble, and base metal alloys bonded to enamel.
abstract: BACKGROUND
  Although the bond strengths of various resin composite luting materials have been reported in the literature, the evaluation of these systems with various cast alloys of different compositions has not been completely clarified.
  
  
  OBJECTIVE
  To evaluate the tensile bond strength of sandblasted high-noble, noble, and base metal alloys bonded to etched enamel by 2 different bonding agents of different chemical composition: Panavia-Ex (BIS-GMA) and Super-Bond (4-META acrylic).
  
  
  METHODS
  Flat enamel surfaces were prepared on buccal surfaces of 60 extracted noncarious human incisors. Teeth were divided into 3 groups of 20 each. Twenty circular disks of 5 mm diameter were prepared for casting for each group. Group I was cast with a high-noble, group II with a noble, and group III with a base metal alloy. The surfaces of the disks were sandblasted with 250 microm Al(2)O(3). Ten disks of each group were bonded to exposed enamel surfaces with Super-Bond and 10 disks with Panavia-Ex as recommended by the manufacturer. The tensile bond strength was measured with an Instron universal testing machine with a crosshead speed of 0.5 mm/min until failure occurred.
  
  
  RESULTS
  Two-way ANOVA was used to evaluate the results. The differences in bond strengths of Super-Bond and Panavia-Ex with different alloys were not significant. The highest bond strengths were obtained in base metal alloys, followed by noble and high-noble alloys. These results were significant.
  
  
  CONCLUSIONS
  Panavia-Ex and Super-Bond exhibited comparable tensile bond strengths. For both luting agents, the highest bond strengths were achieved with base metal alloys and the lowest with high-noble alloys.
authors: Department of Prosthodontics, Instanbul University, Instanbul, Turkey. dsen@istanbul.edu.tr
authors: D
authors: D
authors: Sen
authors: E
authors: E
authors: Nayir
authors: S
authors: S
authors: Pamuk
mesh_terms: D000704:Analysis of Variance; D017438:Bisphenol A-Glycidyl Methacrylate; D001896:Boron Compounds; D003722:Dental Alloys / Q000737:chemistry*; D001840:Dental Bonding / Q000379:methods / Q000706:statistics & numerical data; D017005:Dental Debonding; D003743:Dental Enamel / Q000187:drug effects*; D006801:Humans; D066298:In Vitro Techniques; D007180:Incisor; D008689:Methacrylates; D008768:Methylmethacrylates; D008855:Microscopy, Electron, Scanning; D019279:Resin Cements; D013499:Surface Properties; D013718:Tensile Strength / Q000187:drug effects
chemical_list: D001896:Boron Compounds; D003722:Dental Alloys; D008689:Methacrylates; D008768:Methylmethacrylates; D019279:Resin Cements; D017438:Bisphenol A-Glycidyl Methacrylate; C049495:Super-bond