Mercury evaporation from amalgams with varied mercury contents.
This study examined the relationship between mercury content and mercury evaporation from amalgams during setting. Two different types of commercial high-copper amalgams (single composition and admixed types) were used. Cylindrical specimens of each amalgam were prepared with five different mercury contents according to ADA Specification No.1. Specimens were also prepared by hand condensation. Mercury evaporation from amalgam specimens maintained at 37 degrees C was measured using a gold film mercury analyzer from 10 min after the end of trituration until the mercury concentration in air reached an undetectable level. The mercury content more clearly influenced the mercury evaporation from the admixed type amalgam specimens when the mercury content decreased below the manufacturers' recommended trituration conditions. Triturating with less mercury than the manufacturers' recommended amount cannot lower the evaporation of mercury from freshly made amalgam. Proper condensing procedures can minimize the mercury evaporation from the amalgam surface.
Ohmoto
K
K
Department of Operative Dentistry, School of Dentistry, Hiroshima University, 1-2-3 Kasumi, Minami-ku, Hiroshima 734-8553, Japan.
Nakajima
H
H
Ferracane
J L
JL
Shintani
H
H
Okabe
T
T
D002626:Chemistry, Pharmaceutical; D003722:Dental Alloys / Q000737:chemistry; D003723:Dental Amalgam / Q000737:chemistry*; D008628:Mercury / Q000032:analysis*; D008669:Metallurgy; D014835:Volatilization
D003722:Dental Alloys; C033470:Dispersalloy; C036886:tytin; D003723:Dental Amalgam; D008628:Mercury