Dentine chips produced by nickel-titanium rotary instruments.
This study aimed to compare the cross-sectional shape of two nickel-titanium rotary instruments, namely ProFile and Quantec files, both ISO 25, 0.06 taper, and sought to relate this to the chips produced by cutting dentine. A limited comparison was made with stainless steel engine reamers. First, five files of each type were sectioned transversely at 12 mm, 8 mm and 4 mm from the tip and examined by scanning electron microscopy. The cutting angles were assessed by a direct measurement technique which allowed for the inclination of a cutting edge to the root canal. Second, eight samples of cutting debris were collected from instrumentation by each type of nickel-titanium file and four samples from the engine reamers. The major and minor axis, area and roundness of the dentine chips in each sample were measured using computerized particle analysis. The results demonstrated that all files had a negative cutting angle which varied at the different levels (ProFiles range 69.4 degrees to 58.4 degrees and Quantec range 74.8 degrees to 56.8 degrees). The consistency within files of the same type was good as demonstrated by low standard deviations, except for Quantec files at the 4 mm level where higher standard deviations of 4.1 degrees and 5.5 degrees for the two blades were found. The chip analysis showed significant differences between chips produced by ProFile and Quantec files (P < 0.05). The latter were larger and rounder. The chips from the ProFile and the engine reamer chips were similar in dimension (P > 0.05). No simple relationship existed between file geometry and the dentine chips produced during instrumentation.
Guppy
D R
DR
Department of Conservative Dentistry, Guy's, King's and St Thomas' Dental Institute, Kings' College, London, UK.
Curtis
R V
RV
Ford
T R
TR
D003722:Dental Alloys; D003786:Dental Pulp Cavity / Q000648:ultrastructure; D003804:Dentin / Q000648:ultrastructure*; D004867:Equipment Design; D006801:Humans; D007091:Image Processing, Computer-Assisted; D008855:Microscopy, Electron, Scanning; D009532:Nickel; D018915:Root Canal Preparation / Q000295:instrumentation*; D012399:Rotation; D013193:Stainless Steel; D018709:Statistics, Nonparametric; D013499:Surface Properties; D014025:Titanium
D003722:Dental Alloys; C040654:titanium nickelide; D013193:Stainless Steel; D009532:Nickel; D014025:Titanium