Flexural properties and impact strength of denture base polymer reinforced with woven glass fibers.
OBJECTIVE
The present investigation was undertaken to determine the reinforcing effect of woven glass fibers on deflection, flexural strength, flexural modulus and impact strength of acrylic denture base polymer.


METHODS
Three silanized or unsilanized woven glass fibers were used. Specimens were made by heating the denture cure resin dough containing glass fibers, which were sheathed in the dough. Specimens with four different thicknesses and of five different types were made, incorporating the glass fiber. Three-point flexural test and flywheel type impact test were employed to determine the flexural properties and impact strength.


RESULTS
When specimens contained unsilanized glass fiber, the flexural strength in specimens of 1 and 2 mm thickness and the impact strength in specimens of 2 mm thickness were higher than those of specimens without glass fiber (p < 0.01). On the contrary, the flexural strength and deflection in specimens reinforced with silanized glass fiber of 1 mm thickness were significantly higher (p < 0.01, p < 0.05) than those of unreinforced specimens. Further, the impact strength in specimens reinforced with silanized glass fiber of 2 mm thickness was significantly higher (p < 0.01) than that of unreinforced specimens. Statistically significant differences were found in the flexural strength (p < 0.05) and in the impact strength (p < 0.01) when specimens of 4 mm thickness were reinforced with two or three unsilanized glass fibers.


CONCLUSIONS
The reinforcement with glass fiber was effective in thin specimens, and the reinforcing effect increased with the increase of the number of glass fibers in the case of thick specimens.
Kanie
T
T
Department of Biomaterials Science, Kagoshima University Dental School, 8-35-1 Sakuragaoka, Kagoshima 890-8544, Japan. einak@dentb.hal.kagoshima-u.ac.jp
Fujii
K
K
Arikawa
H
H
Inoue
K
K
D000180:Acrylic Resins / Q000737:chemistry*; D000465:Algorithms; D000704:Analysis of Variance; D003819:Denture Bases; D004548:Elasticity; D005663:Furans / Q000737:chemistry; D005898:Glass / Q000737:chemistry*; D006801:Humans; D008422:Materials Testing; D008689:Methacrylates / Q000737:chemistry; D020366:Methylmethacrylate / Q000737:chemistry; D008855:Microscopy, Electron, Scanning; D018583:Pliability; D019904:Polymethyl Methacrylate / Q000737:chemistry; D012821:Silanes / Q000737:chemistry; D012822:Silicon Dioxide / Q000737:chemistry; D012995:Solubility; D012997:Solvents / Q000737:chemistry; D013314:Stress, Mechanical; D013499:Surface Properties
D000180:Acrylic Resins; D005663:Furans; D008689:Methacrylates; D012821:Silanes; D012997:Solvents; C009753:fiberglass; D020366:Methylmethacrylate; C017492:methacryloxypropyltrimethoxysilane; C018674:tetrahydrofuran; D012822:Silicon Dioxide; D019904:Polymethyl Methacrylate