title: Bond strengths of nonrinsing adhesives.
abstract: OBJECTIVE
  The purpose of this study was to determine enamel and dentin bond strengths of a nonrinsing "all-in-one" adhesive and of a nonrinsing conditioner combined with a 1-bottle adhesive.
  
  
  METHODS
  Specimens were obtained from 240 bovine teeth ground to expose enamel or dentin surfaces. Ten enamel and 10 dentin specimens were randomly assigned to each of 12 different combinations of adhesive system (Prompt L-Pop; no etch + Prime & Bond NT; NRC + Prime & Bond NT; 36% phosphoric acid + Prime & Bond NT; no etch + Prime & Bond 2.1; 36% phosphoric acid + Prime & Bond 2.1) and restorative material (resin composite; polyacid-modified resin composite ["compomer"]). After the application of the adhesive system, a No. 5 gelatin capsule filled with the restorative material was seated against the enamel or dentin surface. After 24 hours in distilled water at 37 degrees C, the specimens were thermocycled and the shear bond strengths were measured.
  
  
  RESULTS
  For resin composite, etching with phosphoric acid resulted in the highest bond strengths to enamel. For compomer, the highest enamel bond strengths were achieved with both phosphoric acid and Prompt L-Pop. Treating dentin with Prime & Bond NT without etching provided the highest mean bond strength for composite. For compomer, treating dentin with Prime & Bond NT resulted in the highest mean bond strengths, regardless of the conditioner.
  
  
  CONCLUSIONS
  Compomer and resin composite exhibited statistically similar bond strengths. Bond strengths to dentin were significantly lower than those to enamel.
authors.affiliation: Department of Operative Dentistry, University of North Carolina at Chapel Hill, School of Dentistry, Chapel Hill, North Carolina, USA.
authors.forename: B T
authors.initials: BT
authors.lastname: Rosa
authors.forename: J
authors.initials: J
authors.lastname: Perdigão
mesh_terms: D000134:Acid Etching, Dental; D000269:Adhesives / Q000737:chemistry*; D000704:Analysis of Variance; D000818:Animals; D017438:Bisphenol A-Glycidyl Methacrylate / Q000737:chemistry; D002417:Cattle; D020770:Compomers / Q000737:chemistry; D003188:Composite Resins / Q000737:chemistry; D001840:Dental Bonding; D003743:Dental Enamel / Q000648:ultrastructure; D003804:Dentin / Q000648:ultrastructure; D017220:Dentin-Bonding Agents / Q000737:chemistry*; D008422:Materials Testing; D010756:Phosphoric Acids / Q000008:administration & dosage; D011109:Polymethacrylic Acids / Q000737:chemistry; D011897:Random Allocation; D019279:Resin Cements / Q000737:chemistry; D013314:Stress, Mechanical; D013499:Surface Properties; D013816:Thermodynamics
chemical_list: D000269:Adhesives; D020770:Compomers; D003188:Composite Resins; D017220:Dentin-Bonding Agents; D010756:Phosphoric Acids; D011109:Polymethacrylic Acids; C103500:Prime & Bond; C408584:Prompt L-Pop; D019279:Resin Cements; D017438:Bisphenol A-Glycidyl Methacrylate