Effect of the addition of poly(methyl methacrylate) beads on some properties of acrylic resin.
OBJECTIVE
There have been numerous attempts to improve the mechanical properties of acrylic resin. However, the fracture of dentures is still an unresolved problem. The potential advantage of self-reinforcement should be improved mechanical properties over the amorphous random polymer. This study investigated the addition of poly(methyl methacrylate) (PMMA) beads in a variety of percentages on a range of mechanical properties of PMMA denture base acrylic resin.


METHODS
The transverse and impact strengths and hardness of acrylic resin specimens stored in water for periods of 1 week and 6 months prior to testing were investigated.


RESULTS
The results showed that for specimens stored for 1 week, the addition of up to 25% beads produced a significant increase in the modulus of elasticity. Addition of 5% beads produced a slight but nonsignificant increase in the modulus of rupture, although additions of increasing percentages produced a decrease in the modulus of rupture. The impact strength was increased for 5% to 25% beads and decreased for 40% beads. The hardness showed only small changes. For specimens stored in water for 6 months, the modulus of rupture decreased with increasing percentages of beads. The addition of beads up to 10% significantly increased the modulus of elasticity. There was no significant increase in impact strength but a significant increase in hardness for 5% beads.


CONCLUSIONS
The addition of PMMA beads to acrylic resin did not produce a substantial improvement in the mechanical properties and cannot be recommended as a method of reinforcement in its present form.
Jagger
D C
DC
Department of Oral and Dental Science, Division of Restorative Dentistry (Prosthodontics), Bristol Dental School and Hospital, Lower Maudlin Street, Bristol BSI 2LY, United Kingdom. D.C.Jagger@bris.ac.uk
Harrison
A
A
al-Marzoug
K
K
D000180:Acrylic Resins / Q000737:chemistry*; D000704:Analysis of Variance; D003819:Denture Bases; D004548:Elasticity; D019544:Equipment Failure Analysis; D006244:Hardness; D008422:Materials Testing; D019904:Polymethyl Methacrylate / Q000737:chemistry*; D013314:Stress, Mechanical
D000180:Acrylic Resins; D019904:Polymethyl Methacrylate