Towards a single crystal Raman spectrum of kaolinite at 77 K.
The Raman spectra at 77 K of the hydroxyl stretching of kaolinite were obtained along the three axes perpendicular to the crystal faces. Raman bands were observed at 3616, 3658 and 3677 cm(-1) together with a distinct band observed at 3691 cm(-1) and a broad profile between 3695 and 3715 cm(-1). The band at 3616 cm(-1) is assigned to the inner hydroxyl. The bands at 3658 and 3677 cm(-1) are attributed to the out-of-phase vibrations of the inner surface hydroxyls. The Raman spectra of the in-phase vibrations of the inner-surface hydroxyl-stretching region are described in terms of transverse and longitudinal optic splitting. The band at 3691 cm(-1) is assigned to the transverse optic and the broad profile to the longitudinal optic mode. This splitting remained even at liquid nitrogen temperature. The transverse optic vibration may be curve resolved into two or three bands, which are attributed to different types of hydroxyl groups in the kaolinite.
Frost
R L
RL
Centre for Instrumental and Developmental Chemistry, Queensland University of Technology, Brisbane, Australia. r.frost@qut.edu.au
Kloprogge
J T
JT
D003460:Crystallization; D007616:Kaolin / Q000737:chemistry*; D008958:Models, Molecular; D008968:Molecular Conformation; D013059:Spectrum Analysis, Raman; D013816:Thermodynamics
D007616:Kaolin