Reducing chemical vapour infiltration time for ceramic matrix composites.
Conventional routes to producing ceramic matrix composites (CMCs) require the use of high temperatures to sinter the individual ceramic particles of the matrix together. Sintering temperatures are typically much higher than the upper temperature limits of the fibres. This paper details preliminary work carried out on producing a CMC via chemical vapour infiltration (CVI), a process that involves lower processing temperatures, thus avoiding fibre degradation. The CVI process has been modified and supplemented in an attempt to reduce the CVI process time and to lower the cost of this typically expensive process. To this end microwave-enhanced CVI (MECVI) has been chosen, along with two alternative pre-infiltration steps: electrophoretic infiltration and vacuum bagging. The system under investigation is based on silicon carbide fibres within a silicon carbide matrix (SiCf/SiC). The results demonstrate that both approaches result in an enhanced initial density and a consequent significant reduction in the time required for the MECVI processing step. Dual energy X-ray absorptiometry was used as a non-destructive, density evaluation technique. Initial results indicate that the presence of the SiC powder in the pre-form changes the deposition profile during the MECVI process.
Timms
L. A.
LA
Mechanical Sciences Sector, Building A7, Room 2008, DERA Farnborough, Hampshire, GU14 0LX, U.K.; School of Mechanical, Materials, Manufacturing Engineering and Management, University of Nottingham, Nottinghamshire, NG7 2RD U.K.; Department of Materials Engineering, Brunel University, Middlesex, UB8 3PH, U.K.
Westby
W.
W
Prentice
C.
C
Jaglin
D.
D
Shatwell
R. A.
RA
Binner
J. G. P.
JG