Effects of digestion protocols on the isolation and characterization of metal-metal wear particles. II. Analysis of ion release and particle composition.
The isolation of metal wear particles from hip simulator lubricants is important for understanding wear mechanisms and the tissue response to particulate material. Part I of this study demonstrated that isolation protocols involving digestion reagents can chemically attack metal-metal wear particles, reducing their size and changing their shape. In part II of this study, Co and Cr ion concentrations in solution after each digestion protocol were measured by flame atomic absorption spectrometry, and wear particle composition was determined by X-ray analysis spectra. The exposure of wear particles in water to alkaline solutions caused an increasing release of Cr ions in solution with alkaline concentration and time, and a corresponding decrease in particle Cr peak intensity on X-ray spectra. As a result, particles exposed to 12N KOH for 48 h displayed Co peaks and no Cr. In contrast, enzymatic protocols caused a release of Co ions in solution and a corresponding decrease in particle Co peak intensity on X-ray spectra, especially with sodium phosphate as a buffer. However, when isolating particles from 95% serum, there was an initial protective effect of serum proteins, presumably because of their binding to Co and Cr. As a result, the extent of Cr ion release from metal wear particles in 95% serum after alkaline treatments was diminished, although still present, whereas both enzymatic protocols resulted in a negligible release of Co and Cr ions into solution. Particle composition analysis after enzymatic treatments revealed the presence of chromium oxide particles and CoCrMo particles with variable Co/Cr ratios. After alkaline treatments, the chromium oxide particles increasingly disappeared with time and alkaline concentration, demonstrating a change in particle composition after these treatments. This study demonstrated that digestion reagents can induce chemical changes that affect particle composition. Of all the protocols tested, the enzymatic protocols were the least damaging to the particles and appeared to be the best compromise for isolation and characterization of metal particles, especially in 95% serum. Special care on the choice of buffers should be taken when isolating particles from a lower concentration of serum.
Department of Biomedical Engineering, McGill University, Duff Medical Building, 3775 University Street, Montreal, Quebec, Canada, H3A 2B4.
I
I
Catelas
J D
JD
Bobyn
J J
JJ
Medley
D J
DJ
Zukor
A
A
Petit
O L
OL
Huk
D000818:Animals; D001672:Biocompatible Materials / Q000737:chemistry; D001769:Blood; D002417:Cattle; D006622:Hip Prosthesis; D006801:Humans; D066298:In Vitro Techniques; D007477:Ions; D008422:Materials Testing; D008670:Metals / Q000737:chemistry; D010316:Particle Size; D011475:Prosthesis Failure; D013052:Spectrometry, X-Ray Emission; D014867:Water
D001672:Biocompatible Materials; D007477:Ions; D008670:Metals; D014867:Water