Chemical composition of individual aerosol particles in workplace air during production of manganese alloys.
Aerosol particle samples were collected at ELKEM ASA ferromanganese (FeMn) and silicomanganese (SiMn) smelters at Porsgrunn, Norway, during different production steps: raw material mixing, welding of protective steel casings, tapping of FeMn and slag, crane operation moving the ladles with molten metal, operation of the Metal Oxygen Refinement (MOR) reactor and casting of SiMn. Aerosol fractions were assessed for the analysis of the bulk elemental composition as well as for individual particle analysis. The bulk elemental composition was determined by inductively coupled plasma atomic emission spectrometry. For individual particle analysis, an electron microprobe was used in combination with wavelength-dispersive techniques. Most particles show a complex composition and cannot be attributed to a single phase. Therefore, the particles were divided into six groups according to their chemical composition: Group I, particles containing mainly metallic Fe and/or Mn; Group II, slag particles containing mainly Fe and/or Mn oxides; Group III, slag particles consisting predominantly of oxidized flux components such as Si, Al, Mg, Ca, Na and K; Group IV, particles consisting mainly of carbon; Group V, mixtures of particles from Groups II, III and IV; Group VI, mixtures of particles from Groups II and III. In raw material mixing, particles originating from the Mn ores were mostly found. In the welding of steel casings, most particles were assigned to Group II, Mn and Fe oxides. During the tapping of slag and metal, mostly slag particles from Group III were found (oxides of the flux components). During movement of the ladles, most particles came from Group II. At the MOR reactor, most of the particles belonged to the slag phase consisting of the flux components (Group III). The particles collected during the casting of SiMn were mainly attributed to the slag phase (Groups III and V). Due to the compositional complexity of the particles, toxicological investigations on the kinetics of pure compounds may not be easily associated with the results of this study.
Gunst
S
S
Material Science Department, Darmstadt University of Technology, Germany.
Weinbruch
S
S
Wentzel
M
M
Ortner
H M
HM
Skogstad
A
A
Hetland
S
S
Thomassen
Y
Y
D000336:Aerosols / Q000737:chemistry*; D016902:Air Pollution, Indoor / Q000032:analysis*; D000497:Alloys; D004784:Environmental Monitoring; D006801:Humans; D008345:Manganese / Q000737:chemistry*; D008420:Manufactured Materials; D008669:Metallurgy; D008670:Metals / Q000032:analysis; D016273:Occupational Exposure; D017132:Workplace
D000336:Aerosols; D000497:Alloys; D008670:Metals; D008345:Manganese