A study of the corrosion products of mild steel in high ionic strength brines.
The corrosion layer on steel surfaces that formed after exposure to waste isolation pilot plant (WIPP) brines under anoxic conditions was characterized for chemical composition, thickness and phase composition. The chemical composition of the corrosion layer was determined both by X-ray photoelectron spectroscopy (XPS) and by chemical analysis of acid solutions used to remove the corrosion layer. Atomic force microscopic (AFM) images indicated that the brine-corroded surface layer shows extensive granulation along the contours of the steel surface that is characteristic of sharp polishing marks. The corrosion layer seemed to be porous and could be dissolved and detached in dilute hydrochloric acid. The corrosion layer appears to be composed of iron oxides with some ionic substitutions from the brines. The 77 K Mössbauer spectrum recorded for iron powder leached under similar conditions indicated the corrosion layer was comprised principally of green rust.
Wang
Z
Z
Pacific Northwest National Laboratory, Richland, WA 99352, USA. zheming.wang@pnl.gov
Moore
R C
RC
Felmy
A R
AR
Mason
M J
MJ
Kukkadapu
R K
RK
D003343:Corrosion; D005290:Ferric Compounds / Q000032:analysis* / Q000737:chemistry; D006851:Hydrochloric Acid / Q000737:chemistry; D008670:Metals / Q000032:analysis; D018625:Microscopy, Atomic Force; D011850:Radioactive Waste; D012037:Refuse Disposal / Q000295:instrumentation* / Q000379:methods; D012492:Salts / Q000737:chemistry*; D013057:Spectrum Analysis; D013232:Steel / Q000737:chemistry*
D005290:Ferric Compounds; D008670:Metals; D011850:Radioactive Waste; D012492:Salts; C017082:brine; D013232:Steel; C000499:ferric oxide; D006851:Hydrochloric Acid