Effect of three adhesive primers on the bond strengths of four light-activated opaque resins to noble alloy.
The effect of commercial adhesive primers for noble metals on the bond strength of light-activated opaque resin has not been determined. This study evaluated the effect of three adhesive primers on the shear bond strengths of each of the four light-activated opaque resins to silver--palladium--copper--gold (Ag--Pd--Cu--Au) alloy. The adhesive primers Alloy Primer (AP), Metal Primer II (MPII) and Metaltite(MT) were used. Four commercial light-activated opaque resins (Axis (AX), Cesead II (CEII), Dentacolor(DE) and Solidex (SO) were used to bond a light-activated resin-veneered composite to Ag--Pd--Cu--Au alloy. The specimens were stored in water at 37 degrees C for 24 h and then immersed alternatively in water baths at 4 and 60 degrees C for 1 min each for up to 20,000 thermal cycles before shear mode testing at a cross-head speed of 0.5 mm min(-1). All the primers examined improved the shear bond strength between opaque resin and Ag--Pd--Cu--Au alloy compared with non-primed specimens prior to thermal cycling. After 20,000 thermal cycles, the bond strengths of combined use of AP and DE and that of MT and each of AX, CE or DE were significantly greater than any other groups. Significant difference was observed between the bond strengths at thermal cycles 0 and 20,000, with the combined use of MT and DE. With the combination of appropriate adhesive metal primers and light-activated opaque resins, complicated surface preparations of metal frameworks of resin-veneered prostheses that are composed of casting Ag-Pd-Cu-Au alloy may be negligible.
Yoshida
K
K
Department of Fixed Prosthodontics, Nagasaki University School of Dentistry, Nagasaki, Japan. keiichi@net.nagasaki-u.ac.jp
Kamada
K
K
Taira
Y
Y
Atsuta
M
M
D000269:Adhesives / Q000737:chemistry*; D000704:Analysis of Variance; D003188:Composite Resins / Q000737:chemistry; D003300:Copper / Q000737:chemistry; D003722:Dental Alloys / Q000737:chemistry*; D001840:Dental Bonding; D003734:Dental Casting Investment / Q000737:chemistry; D003801:Dental Veneers; D006047:Gold Alloys / Q000737:chemistry*; D006801:Humans; D008027:Light; D008422:Materials Testing; D008689:Methacrylates / Q000737:chemistry; D010165:Palladium / Q000737:chemistry; D019279:Resin Cements / Q000737:chemistry; D012117:Resins, Synthetic / Q000737:chemistry*; D012821:Silanes / Q000737:chemistry; D012834:Silver / Q000737:chemistry; D013223:Statistics as Topic; D013314:Stress, Mechanical; D013499:Surface Properties; D013816:Thermodynamics
D000269:Adhesives; D003188:Composite Resins; D003722:Dental Alloys; D003734:Dental Casting Investment; D006047:Gold Alloys; D008689:Methacrylates; D019279:Resin Cements; D012117:Resins, Synthetic; D012821:Silanes; C113676:Solidex; C083620:cesead; C100646:Metal Primer; D012834:Silver; D010165:Palladium; D003300:Copper; C057365:Dentacolor