Alarming wear of the first-generation polyethylene liner of the cementless porous-coated Biomet Universal cup: 107 hips followed for mean 6 years.
Wear of the socket liner and resulting osteolysis are the major causes of failure in cementless hip arthroplasties. We report alarming wear of the first-generation polyethylene liner of the cementless porous-coated Biomet Universal cup. Radiographs of 107 primary hip arthroplasties were analyzed retrospectively. The mean follow-up time was 74 (47-91) months. The linear wear of the polyethylene liners was assessed using a modification of the Livermore method. The median linear wear was 1.0 (0-6.2) and the median linear wear rate was 0.17 mm/year. There was a statistically significant difference between the 28 mm and 32 mm femoral head groups both in the volumetric wear and in the volumetric wear rate. The median linear wear was 0.28 mm/year and 0.14 mm/year for the 32 mm and 28 mm heads, respectively. So far, 14 revisions have been performed or have been scheduled because of excessive wear of the polyethylene liner. In regression analysis, the factors related to the wear rate were the 32 mm size of the femoral head and screw fixation of acetabular shell. We found that the cases with calcar rounding were associated with significantly greater wear. Possible reasons for increased wear of the Hexloc liner may be the cylindrical design, thin polyethylene, and poor quality of the polyethylene. Regular clinical and radiographic follow-ups are recommended especially for hips with 32 mm femoral heads or with screw fixation. If progressive wear of the liner is observed, revision must be considered.
Puolakka
T J
TJ
Department of Surgery, Tampere University Hospital, Finland. timo.puolakka@tays.fi
Laine
H J
HJ
Moilanen
T P
TP
Koivisto
A M
AM
Pajamäki
K J
KJ
D000328:Adult; D000368:Aged; D001172:Arthritis, Rheumatoid / Q000000981:diagnostic imaging / Q000601:surgery; D001863:Bone Screws / Q000009:adverse effects; D020099:Coated Materials, Biocompatible / Q000009:adverse effects* / Q000737:chemistry; D019544:Equipment Failure Analysis; D005260:Female; D005500:Follow-Up Studies; D006618:Hip Dislocation, Congenital / Q000000981:diagnostic imaging / Q000601:surgery; D006621:Hip Joint; D006622:Hip Prosthesis / Q000009:adverse effects*; D006801:Humans; D016015:Logistic Models; D008297:Male; D008875:Middle Aged; D015207:Osteoarthritis, Hip / Q000000981:diagnostic imaging / Q000601:surgery; D020959:Polyethylene / Q000009:adverse effects* / Q000737:chemistry; D011474:Prosthesis Design; D011475:Prosthesis Failure; D011859:Radiography; D012044:Regression Analysis; D012086:Reoperation; D012189:Retrospective Studies; D012307:Risk Factors; D016896:Treatment Outcome
D020099:Coated Materials, Biocompatible; D020959:Polyethylene