Novel layered superstructures in mixed ultralong n-alkanes.
Two new types of layered structures were found in binary mixtures of n-alkanes ranging from C122H246 to C294H590. At high temperatures a semicrystalline form is the stable phase, having a regular structure of alternating crystalline and amorphous layers. The two long-chain compounds are mixed in the crystalline layers and the amorphous layers consist of the surplus length of the longer chains. At lower temperatures a reversible transition occurs to a triple layer superlattice structure with a periodicity of up to 50 nm. These two new phases allow the existence of binary solid solutions of chains with a length ratio of up to 1.7 and a chain length difference of 100 CH2 groups.