title: Fabrication of porous calcium polyphosphate implants by solid freeform fabrication: a study of processing parameters and in vitro degradation characteristics.
abstract: Solid freeform fabrication (SFF) involves the creation of a solid 3-D object of desired shape by successively adding raw materials in particles or layers. Its use in fabricating surgical implants is being explored. The objective of this study was to determine the feasibility of using SFF to build porous parts of calcium polyphosphate (CPP), a linear condensed phosphate that has been suggested as a material for forming bioresorbable skeletal replacement implants. CPP powders (<25 microm in particle size) were added to an UV curable monomer (SOMOS 6110) at a solids loading of 25 vol %, with the addition of a commercial dispersant to prevent particle agglomeration and settling. Viscosity and cure depth measurements were performed to insure that CPP suspension met the requirements deemed necessary for use in SFF. The CPP suspension was bulk cured and sintered in molds in order to assess binder removal and sintering parameters. Using a three-point bend test, the ultimate bending strength and energy-to-fracture of sintered CPP samples simulating parts to be formed by this strategy were characterized. In vitro degradation studies using 0.1M of tris-buffered solution were performed to assess the effect of aging on mechanical properties of the samples as a function of the processing route and resulting structures. The polymer binder successfully was removed from the cured ceramic suspension by developing a procedure that combined slow heating rates with low temperature dwells. Sintering CPP at 585 degrees C for 1 h produced amorphous material samples with average porosity of 27.7 +/- 2.0%. Sintering CPP at 600 degrees C for 1 h produced a crystalline material with samples having an average porosity of 22.9 +/- 1.3%. Crystalline CPP was found to exhibit superior bend strength and toughness compared with amorphous CPP. Both samples experienced a decline in mechanical properties during in vitro degradation; however, the effects were more pronounced with the amorphous CPP samples. Amorphous CPP was found to degrade four times faster than crystalline CPP, as shown by high levels of phosphate present in the degradation solution and a noticeable increase in the porosity of the samples. Crystalline CPP was more resistant to attack as dissolution was limited to surface features of the sintered particles.
authors.affiliation: Institute of Biomaterials and Biomedical Engineering, University of Toronto, ON, Toronto, Canada M5S 3E3.
authors.forename: N L
authors.initials: NL
authors.lastname: Porter
authors.forename: R M
authors.initials: RM
authors.lastname: Pilliar
authors.forename: M D
authors.initials: MD
authors.lastname: Grynpas
mesh_terms: D001672:Biocompatible Materials; D002118:Calcium; D011122:Polyphosphates; D019736:Prostheses and Implants; D013499:Surface Properties
chemical_list: D001672:Biocompatible Materials; D011122:Polyphosphates; D002118:Calcium