Elastohydrodynamic lubrication analysis of ultra-high molecular weight polyethylene hip joint replacements under squeeze-film motion.
Elastohydrodynamic lubrication was analysed under squeeze-film or normal approach motion for artificial hip joint replacements consisting of an ultra-high molecular weight polyethylene (UHMWPE) acetabular cup and a metallic or ceramic femoral head. A simple ball-in-socket configuration was adopted to represent the hip prosthesis for the lubrication analysis. Both the Reynolds equation and the elasticity equations were solved simultaneously for the lubricant film thickness and hydrodynamic pressure distribution as a function of the squeeze-film time was solved using the Newton-Raphson method. The elastic deformation of the UHMWPE cup was calculated by both the finite element method and a simple equation based upon the constrained column model. Good agreement of the predicted film thickness and pressure distribution was found between these two methods. A simple analytical method based upon the Grubin-Ertel-type approximation developed by Higginson in 1978 [1] was also applied to the present squeeze-film lubrication problem. The predicted squeeze-film thickness from this simple method was found to be remarkably close to that from the full numerical solution. The main design parameters were the femoral head radius, the radial clearance between the femoral head and the acetabular cup, and the thickness and elastic modulus for the UHMWPE cup; the effects of these parameters on the squeeze-film thickness generated in current hip prostheses were investigated.
Jagatia
M
M
Department of Mechanical and Medical Engineering, University of Bradford, West Yorkshire BD7 1DP, UK.
Jalali-Vahid
D
D
Jin
Z M
ZM
D019644:Arthroplasty, Replacement, Hip; D006622:Hip Prosthesis / Q000009:adverse effects*; D006801:Humans; D008153:Lubrication; D008422:Materials Testing; D008962:Models, Theoretical; D009038:Motion; D011095:Polyethylenes / Q000032:analysis*; D014481:United States
D011095:Polyethylenes; C111601:ultra-high molecular weight polyethylene