The effect on the fatigue strength of bone cement of adding sodium fluoride.
New bone cements that include several additives are currently being investigated and tested. One such additive is sodium fluoride (NaF), which promotes bone formation, facilitating implant integration and success. The influence of NaF on the fatigue performance of the cement as used in biomedical applications was tested in this paper. In fact fatigue failure of the cement mantle is a major factor limiting the longevity of a cemented implant. An experimental bone cement with added NaF (12 wt%) was investigated. The fatigue strength of the novel bone cement was evaluated in comparison with the cement without additives; fatigue tests were conducted according to current standards. The load levels were arranged based on a validated, statistically based optimization algorithm. The curve of stress against number of load cycles and the endurance limit were obtained and compared for both formulations. The results showed that the addition of NaF (12 wt%) to polymethylmethacrylate (PMMA) bone cement does not affect the fatigue resistance of the material. Sodium fluoride can safely be added to the bone cement without altering the fatigue performance of the PMMA bone cement.
Minari
C
C
Laboratorio di Tecnologia Medica, Istituti Ortopedici Rizzoli, Via Di Barbiano 1/10, 40136 Bologna, Italy.
Baleani
M
M
Cristofolini
L
L
Baruffaldi
F
F
D019245:Compressive Strength; D019544:Equipment Failure Analysis; D007558:Italy; D008422:Materials Testing; D019904:Polymethyl Methacrylate / Q000032:analysis*; D012969:Sodium Fluoride / Q000737:chemistry*; D013314:Stress, Mechanical
D012969:Sodium Fluoride; D019904:Polymethyl Methacrylate