Wear of enamel opposing low-fusing and conventional ceramic restorative materials.
OBJECTIVE
This study evaluated the wear area of human enamel opposing 2 conventional and 2 low-fusing dental porcelains, as well as abrasive wear, attrition, surface hardness, and fracture toughness for the 4 porcelain substrates.


METHODS
Two low-fusing and 2 conventional metal-ceramic porcelains were used to form 15-mm-diameter disks (n = 10), which were fired according to manufacturer's recommendations. Enamel cusps (n = 40) were formed from extracted third molars. All ceramic and enamel specimens were finished to a 1000-grit silicon carbide surface. The Oregon Health Sciences University (Portland, OR) oral wear simulator was used to deliver a 20-N load from the cusps to the ceramic substrates through a food-like slurry. The sliding action of the cusps over an 8-mm linear path produced abrasive wear. A static 70-N load was applied at the end of the path to create attrition. This sequence was repeated at 1.0 Hz for 50,000 cycles. Ceramic wear was measured with a profilometer (+/-2 micrometers), and enamel wear was evaluated using optical scanning methods. After wear testing, the hardness and fracture toughness of the ceramic surfaces were determined, and scanning electron photomicrographs were made using representative ceramic and enamel specimens from each group. Enamel wear areas, abrasion and attrition depths, hardness, and fracture toughness values were subjected to analysis of variance and Tukey-Kramer post hoc tests to determine significant differences.


RESULTS
Enamel wear was not significantly different for low-fusing and conventional porcelains (p =.29). The wear of conventional and low-fusing ceramic substrates was also not significantly different (p =.79). However, depth of porcelain wear caused by attrition was in general significantly greater than abrasive wear (p =.0004). Although no significant differences were found in the measured porcelain hardness values (p =.08), 1 conventional porcelain exhibited fracture toughness significantly greater than 1 low-fusing porcelain (p <.01).


CONCLUSIONS
No differences in wear patterns were noted among low-fusing compared with conventional metal-ceramic porcelains, but static loading resulted in significantly greater attrition compared with the observed sliding abrasive wear. J Prosthodont 2001;10:8-15.
Clelland
N L
NL
Ohio State University, College of Dentistry, 305 West 12th Avenue #191, Columbus, OH 43218-2357, USA. clelland.l@osu.edu
Agarwala
V
V
Knobloch
L A
LA
Seghi
R R
RR
D000704:Analysis of Variance; D001672:Biocompatible Materials / Q000737:chemistry; D001732:Bite Force; D017554:Carbon Compounds, Inorganic / Q000737:chemistry; D002516:Ceramics / Q000737:chemistry*; D003188:Composite Resins / Q000737:chemistry; D003743:Dental Enamel / Q000473:pathology*; D003775:Dental Polishing; D003776:Dental Porcelain / Q000737:chemistry*; D019554:Dental Restoration Wear; D003793:Dental Restoration, Permanent; D006244:Hardness; D006801:Humans; D007091:Image Processing, Computer-Assisted; D018020:Lithium Compounds / Q000737:chemistry; D008855:Microscopy, Electron, Scanning; D017655:Silicon Compounds / Q000737:chemistry; D013223:Statistics as Topic; D013314:Stress, Mechanical; D013499:Surface Properties; D014072:Tooth Abrasion / Q000145:classification / Q000473:pathology*; D019217:Tooth Attrition / Q000145:classification / Q000473:pathology*
D001672:Biocompatible Materials; D017554:Carbon Compounds, Inorganic; D003188:Composite Resins; C118557:Empress 2; D018020:Lithium Compounds; D017655:Silicon Compounds; C111131:VMK 68; D003776:Dental Porcelain; C081267:Willceram porcelain; C037884:finesse; C022088:silicon carbide