Effect of refrigeration on tensile bond strength of three adhesive systems.
The purpose of this study was to investigate the tensile bond strengths of three adhesive systems applied to dentin at refrigerated and room temperatures. Ninety bovine incisor teeth were obtained, embedded in self-cured acrylic resin, abraded on a lathe under water spray and polished to 400 and 600 grit to form standardized dentin surfaces before randomly assigning to six groups (n = 15). The adhesive systems Scotchbond Multi-Purpose, Single Bond and Prime & Bond NT were applied to dentin according to the manufacturers' instructions at refrigerated temperature (4 degrees C) and at room temperature (23 degrees C), before bonding resin-based composite (Z 100). The specimens were stored in distilled water at 37 degrees C for 24 hours and submitted to tensile bond strength tests on a universal testing machine (EMIC DL-2000) at a crosshead speed of 0.5 mm/min. The resulting data were statistically analyzed using analysis of variance and Tukey's test. No statistical differences were found when the adhesive systems were applied at refrigerated and room temperatures. Scotchbond Multi-Purpose and Single Bond had significantly stronger tensile bond strengths than Prime & Bond NT at room and refrigerated temperatures (p < 0.01). Scotchbond Multi-Purpose and Single Bond were statistically similar. No adverse effects upon tensile bond strength were observed when adhesive systems were taken directly from refrigerated storage.
Spohr
A M
AM
Faculty of Dentistry of Piracicaba, UNICAMP, Piracicaba, SP, Brazil.
Correr Sobrinho
L
L
Consani
S
S
Sinhoreti
M A
MA
Borges
G A
GA
D000818:Animals; D017438:Bisphenol A-Glycidyl Methacrylate / Q000737:chemistry; D002417:Cattle; D003188:Composite Resins; D001840:Dental Bonding; D017220:Dentin-Bonding Agents / Q000737:chemistry; D011109:Polymethacrylic Acids / Q000737:chemistry; D011897:Random Allocation; D012034:Refrigeration; D019279:Resin Cements / Q000737:chemistry; D012822:Silicon Dioxide; D015040:Zirconium
D003188:Composite Resins; D017220:Dentin-Bonding Agents; D011109:Polymethacrylic Acids; C425843:Prime and Bond NT; D019279:Resin Cements; C084018:Scotchbond Multi-Purpose; C083568:Z100 composite resin; C115612:single bond; D017438:Bisphenol A-Glycidyl Methacrylate; D012822:Silicon Dioxide; D015040:Zirconium