Calibration graphs for steels by IR laser ablation inductively coupled plasma atomic emission spectrometry.
Infrared laser ablation (IRLA) was studied as a sample-introduction technique for the analysis of steels by inductively coupled plasma atomic emission spectrometry (ICP-AES). A comparison of two IRLA-ICP-AES systems based on Q-switched nanosecond Nd: YAG lasers was performed. The beam of the LINA-Spark atomizer (LSA Sarl, Cully, Switzerland) based on the Surelite 1-20 laser (Continuum, USA) was moved along a circle. A Perkin-Elmer Optima 3000 DV ICP system was used both with lateral and axial viewing modes. A laboratory-made ablation system based on the Brilliant laser (Quantel) was coupled to a Jobin-Yvon 170 Ultrace ICP (lateral viewing, polychromator part employed). A sample was rotated along a circle during ablation. Linearity of calibration plots was verified at least up to 19% Cr and 12% Ni without internal standardization for both LA-ICP-AES systems. Other elements examined were Mo up to 3%, Mn up 1.5%, Si up to 1.7%, and Cu up to 0.15%. The reproducibility was in the range 5-1 %RSD for a mass percentage 0.5-20% of steel constituents. The relative uncertainty of the centroids of the calibration lines was in the range from +/- 4% to +/- 12% for Cr, Ni, Mn, Mo, and Si, and from +/- 8% to +/- 19% for Cu. The lowest determinable quantities were calculated for calibration dependencies. Performances of both the IR-LA-ICP-AES were comparable.
Kanický
V
V
Laboratory of Plasma Sources for Chemical Analysis, Faculty of Science, Masaryk University Brno, Czech Republic. viktork@chemi.muni.cz
Otruba
V
V
Novotný
K
K
Musil
P
P
Mermet
J M
JM