Nifedipine loaded chitosan microspheres: characterization of internal structure.
In the present investigation, a simple technique was employed to obtain cross-sections of unloaded and nifedipine loaded chitosan microspheres. Microspheres, adhering to a polymerized resin block, were cut with an ultramicrotome and viewed with a scanning electron microscope. Unloaded microspheres exhibited a uniform dense matrix structure while crystals of nifedipine were clearly visible in the drug-loaded microspheres. At 2% drug loading, however, no crystals could be seen in the microspheres indicating that either the drug was molecularly dispersed or dissolved in the matrix at this concentration. This was confirmed by powder X-ray diffractometry studies where no peak due to crystalline nifedipine was observed. At high Span 85 concentration (1.5% w/v), the external surface of the microspheres collapsed, but the internal structure remained dense. When the drug was dispersed in the chitosan solution with stirring during preparation, the entrapment was good and the shape of the crystals was changed. The internal structure of the microspheres following dissolution exhibited the presence of pores.
Singla
A K
AK
Department of Pharmaceutics, University Institute of Pharmaceutical Sciences Chandigarh, Panjab University, India. singlaak2000@yahoo.com
Sharma
M L
ML
Dhawan
S
S
D002686:Chitin / Q000031:analogs & derivatives; D048271:Chitosan; D003460:Crystallization; D003692:Delayed-Action Preparations; D004337:Drug Carriers; D016503:Drug Delivery Systems; D008855:Microscopy, Electron, Scanning; D008863:Microspheres; D009543:Nifedipine / Q000008:administration & dosage*; D014961:X-Ray Diffraction
D003692:Delayed-Action Preparations; D004337:Drug Carriers; D002686:Chitin; D048271:Chitosan; D009543:Nifedipine