title: Attachment, proliferation and differentiation of periodontal ligament cells on various guided tissue regeneration membranes.
abstract: The purpose of this study was to evaluate the biological effects of guided tissue regeneration (GTR) membrane materials, per se, on the periodontal tissue regeneration. Rat periodontal ligament (PDL)-derived cells were used to study the attachment, proliferation and differentiation, in vitro, on various GTR membranes. Five commercially available membranes bovine type I collagen (BioMend; BM), bovine type I atelocollagen (Tissue Guide; TG), polylactic acid (Epi-Guide; EG), co-polymer of polylactic acid and polyglycolic acid (Resolute; RL) and expanded polytetrafluoroethylene: e-PTFE (Gore Tex; GT)-were examined. A 3 x 3 mm section of the membrane was fixed to the bottom of a 35 x 10 mm style culture dish and plated with 2 ml of cell suspension at an initial density of 5 x 10(4) cells/ml in culture medium with 10% fetal bovine serum. For cell growth analysis, the specimens were fixed with 10% buffered formalin and stained with hematoxylin at 1.5 hours and 1, 3 and 5 days after cell seeding. The number of cells included in a unit area of 0.25 mm2 were counted under light microscopy. As a comparative scaffold of cell proliferation, a plastic cover for cell culture slip (Celldesk; CD) was used. For analysis of cell differentiation, activity of alkaline phosphatase (ALP) and calcification were histochemically revealed after 2-week cultivation. The initial number of PDL cells attached to the membrane at 1.5 hours after cell seeding was different among membranes. RL, TG and EG had the same level of attached cell numbers as that on CD, while the cell numbers on GT and BM were significantly lower than that on CD (p < 0.01). The rate of cell proliferation with time also differed among the membranes examined. RL and BM demonstrated a significantly higher number of cells at 5 days than at 1.5 hours (p < 0.01). TG had increased numbers of cells at 3 and 5 days after cell seeding. However, there was no statistical difference between the cell numbers at 1.5 hours and 5 days after cell seeding (p > 0.1). EG had a similar number of cell attachments to that at 1.5 hours throughout the experimental period. There was almost no cell proliferation on GT. Cell clusters of ALP positive cells and foci of calcification were seen on all membranes except for GT, where a scant number of cells were seen. Results from this study implied that GTR membrane materials, per se, may influence cell proliferation and differentiation in the process of periodontal tissue regeneration.
authors.affiliation: Department of Oral Pathology, Hiroshima University Faculty of Dentistry, Japan. ttakata@hiroshima-u.ac.jp
authors.forename: T
authors.initials: T
authors.lastname: Takata
authors.forename: H L
authors.initials: HL
authors.lastname: Wang
authors.forename: M
authors.initials: M
authors.lastname: Miyauchi
mesh_terms: D000469:Alkaline Phosphatase / Q000096:biosynthesis; D000818:Animals; D001672:Biocompatible Materials; D002113:Calcification, Physiologic; D002417:Cattle; D002448:Cell Adhesion; D002454:Cell Differentiation; D002455:Cell Division; D002478:Cells, Cultured; D003094:Collagen; D024042:Collagen Type I; D016557:Guided Tissue Regeneration, Periodontal; D019344:Lactic Acid; D008297:Male; D008567:Membranes, Artificial; D010513:Periodontal Ligament / Q000166:cytology* / Q000502:physiology*; D011091:Polyesters; D011098:Polyglactin 910; D011108:Polymers; D011138:Polytetrafluoroethylene; D051381:Rats; D011917:Rats, Inbred Lew; D018709:Statistics, Nonparametric
chemical_list: D001672:Biocompatible Materials; D024042:Collagen Type I; D008567:Membranes, Artificial; D011091:Polyesters; D011108:Polymers; C094810:Resolut; C059821:atelocollagen; D019344:Lactic Acid; D011098:Polyglactin 910; C033616:poly(lactide); D011138:Polytetrafluoroethylene; D003094:Collagen; D000469:Alkaline Phosphatase