Evaluation of the biodurability of polyurethane-covered stent using a flow phantom.
OBJECTIVE
To evaluate the biodurability of the covering material in retrievable metallic stents covered with polycarbonate polyurethane.


METHODS
Using a peristaltic pump at a constant rate of 1 ml/min, bile was recirculated from a reservoir through a long tube containing four stents. Each of these was removed from the system every two weeks and a radial tensile strength test and scanning electron microscopy (SEM) were performed. Each stent, removed at 2, 4, 6 and 8 weeks, was compared with a control stent not exposed to bile juice.


RESULTS
Gross examination showed that stents were intact at 2 weeks, but at 4, 6 and 8 weeks cracks were observed. The size of these increased gradually in accordance with the duration of exposure, and at 8 weeks several large holes in the polyurethane membrane were evident. With regard to radial tensile strength, extension and peak load at break were 84.47% and 10.030 N/mm, 54.90% and 6.769 N/mm, 16.55% and 2.452 N/mm, 11.21% and 1.373 N/mm at 0, 2, 4 and 6 weeks, respectively. Scanning electron microscopy at 2 weeks revealed intermittent pitting and cracking, and examination at 4, 6 and 8 weeks showed that the size of these defects was gradually increasing.


CONCLUSIONS
When the polyurethane membrane was exposed to bile, biodegradation was first observed at week two and increased gradually according to the duration of exposure.
Kim
D H
DH
Department of Diagnostic Radiology, Chosun University Hospial, Gwangju, Korea.
Kang
S G
SG
Choi
J R
JR
Byun
J N
JN
Kim
Y C
YC
Ahn
Y M
YM
D001647:Bile Acids and Salts / Q000502:physiology; D001673:Biodegradation, Environmental; D006863:Hydrogen-Ion Concentration; D008855:Microscopy, Electron, Scanning / Q000295:instrumentation*; D019047:Phantoms, Imaging; D011140:Polyurethanes; D015607:Stents; D013718:Tensile Strength; D013997:Time Factors
D001647:Bile Acids and Salts; D011140:Polyurethanes