A comparative study of retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements with stainless steel crowns--an in vitro study.
This study was conducted on 30 extracted human primary molars to assess the retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements. The teeth were embedded in resin blocks and were randomly divided into 3 groups of 10 each. The occlusal surfaces of all teeth were reduced uniformly by 1.0 to 1.5 mm. All mesial, distal undercuts were removed and sharp angles rounded. This was followed by cementing pretrimmed and precontoured stainless steel crowns on each tooth with hand pressure and storing in artificial saliva at 37 degrees C for 24 hours. Retentive strength was tested using Instron Universal Testing Machine. The load was applied starting from a zero reading and gradually increased until the cemented stainless steel crowns showed signs of movement and then the readings were recorded. It was found that retentive strengths of zinc phosphate and glass ionomer cements were statistically better (P < 0.05) when compared to the polycarboxylate cement. Negligible difference (0. 59 kg/cm2) was however observed between zinc phosphate and glass ionomer cements.
Reddy
R
R
Bapuji Dental College & Hospital, Davangere, Karnataka, India.
Basappa
N
N
Reddy
V V
VV
D000704:Analysis of Variance; D002484:Cementation; D003442:Crowns; D001840:Dental Bonding; D017268:Dental Prosthesis Retention; D003799:Dental Stress Analysis / Q000295:instrumentation; D005899:Glass Ionomer Cements / Q000737:chemistry*; D006801:Humans; D008422:Materials Testing; D008963:Molar; D011076:Polycarboxylate Cement / Q000737:chemistry*; D012464:Saliva, Artificial / Q000737:chemistry; D013193:Stainless Steel / Q000737:chemistry*; D018709:Statistics, Nonparametric; D013314:Stress, Mechanical; D014094:Tooth, Deciduous; D015036:Zinc Phosphate Cement / Q000737:chemistry*
D005899:Glass Ionomer Cements; D011076:Polycarboxylate Cement; D012464:Saliva, Artificial; D013193:Stainless Steel; D015036:Zinc Phosphate Cement