Viscoelastic properties and residual strain in a tensile creep test on bovine temporomandibular articular discs.
This study was designed to evaluate the creep characteristics and residual strain of bovine temporomandibular joint (TMJ) discs in tension. Twenty discs were divided into three specimens each: central, lateral and medial regions. Tension of 1.0 MPa was applied and sustained for 20 min to the specimens from 10 right-side discs, and tension of 1.5 MPa to specimens from 10 left-side discs. After the period of tension for creep, the specimens were removed from the tension devices and restoration observed for 20 min. Time-dependent creep curves showed a marked change in strain during the initial 5s. The essential time delay in strain ceased after 2 min, and strain reached an almost steady level after 3 min. At a tensile stress of 1.5 MPa, a strain of 14.5% on average was produced after 20 min creep in the central specimens; peripheral specimens showed strains of 12.4% on average. There were significant differences in strain between the central and peripheral specimens. The residual strain after 20 min restoration was 0.93% on average and there were no significant regional differences. This creep feature could be well represented by a generalized linear viscoelastic model. It was concluded that the regional differences in viscoelasticity might be caused by the complicated articulating functions of the TMJ, and that the residual strain caused by sustained stress could be an important factor in disc deformation.
Tanaka
E
E
Department of Orthodontics, Hiroshima University, Faculty of Dentistry, 1-2-3 Kasumi, Minami-ku, 734-8553, Hiroshima, Japan. etanaka@ipc.hiroshima-u.ac.jp
Tanaka
M
M
Aoyama
J
J
Watanabe
M
M
Hattori
Y
Y
Asai
D
D
Iwabe
T
T
Sasaki
A
A
Sugiyama
M
M
Tanne
K
K
D000818:Animals; D001696:Biomechanical Phenomena; D002417:Cattle; D003799:Dental Stress Analysis; D004548:Elasticity; D005260:Female; D016014:Linear Models; D008954:Models, Biological; D019224:Temporomandibular Joint Disc / Q000502:physiology*; D013718:Tensile Strength; D014783:Viscosity