Nucleation and growth of germanium nanowires seeded by organic monolayer-coated gold nanocrystals.
Germanium nanowires, ranging from 10 to 150 nm in diameter, were grown several micrometers in length in cyclohexane heated and pressurized above its critical point. Alkanethiol-protected gold nanocrystals, either 2.5 or 6.5 nm in diameter, were used to seed wire formation. Growth proceeded through a solution-liquid-solid mechanism at growth temperatures ranging from 300 to 450 degrees C. At temperatures exceeding 500 degrees C, large Ge particulates formed due to unfavorable growth kinetics. Temperature, the nature of the precursor, precursor concentration, and the Au:Ge ratio were determining factors in nanowire morphology. The Ge nanowires were characterized using a range of techniques, including XPS, XRD, high-resolution TEM and SEM, nanometer-scale EDS mapping, and DTA.
Hanrath
Tobias
T
Department of Chemical Engineering, Texas Materials Institute, Center for Nano- and Molecular Science and Technology, The University of Texas at Austin, Austin, Texas 78712-1062, USA.
Korgel
Brian A
BA