The effect of malalignment on stresses in polyethylene component of total knee prostheses--a finite element analysis.
OBJECTIVE
To investigate the effects of malalignment on stresses in tibial polyethylene component of total knee prostheses.


METHODS
A three-dimensional finite element analysis was used to calculate the contact stress and von Mises stress in the tibial polyethylene component subjected to a compressive load, and the malalignment situations were simulated.


BACKGROUND
Many biomechanical studies to investigate the stresses in tibial polyethylene component were assumed at the ideal contact alignment. The effect of malalignment on stresses in tibial polyethylene component was not investigated extensively.


METHODS
Three-dimensional finite element models of the tibiofemoral joint of knee prostheses for three different designs were constructed. Three malalignment conditions including the medial translation (0.25, 0.5 and 1.0 mm), internal rotation (1 degree, 3 degree and 5 degree), and varus tilt (1 degree, 3 degree and 5 degree) of the femoral component relative to the tibial component were simulated. A compression load of 3000 N was applied to the tibiofemoral joint at 0 degree of flexion. The maximum contact stress and von Mises stress in the tibial component were compared to investigate the effects of malalignment.


RESULTS
In comparing with the neutral position, the greatest increase of maximum contact stress were 67.6%, 14.3% and 145.9% and the greatest increase of maximum von Mises stress were 92.5%, 22.7% and 120.6% in maltranslation, internal rotation and varus tilt simulations, respectively.


CONCLUSIONS
The greatest increase of contact stress and von Mises stress was occurred in the high conformity flat-on-flat design of knee prosthesis under the severest malalignment condition. The high conformity curve-on-curve design of knee prosthesis has the minimal risk of polyethylene wear under the malalignment conditions.


CONCLUSIONS
This study revealed the importance of malalignment effect on stresses in tibial polyethylene component. Polyethylene wear in surface replacement total knees will be minimal when a high conformity curve-on-curve knee design is used and the rotational line between the femoral and tibial components has the least effect on polyethylene wear but varus/valgus malalignment, even with the best designed prosthesis will still accelerate wear.
Liau
Jiann Jong
JJ
Orthopaedic Biomechanics Laboratory, Institute of Biomedical Engineering, National Yang Ming University, No. 155, Sec. 2, Li-Nung St., Shih-Pai, 11221, ROC, Taipei, Taiwan.
Cheng
Cheng Kung
CK
Huang
Chun Hsiung
CH
Lo
Wai Hee
WH
D017760:Bone Malalignment / Q000503:physiopathology*; D020342:Finite Element Analysis; D006801:Humans; D021621:Imaging, Three-Dimensional; D007719:Knee Joint / Q000503:physiopathology*; D007720:Knee Prosthesis; D011095:Polyethylenes; D012399:Rotation; D013314:Stress, Mechanical
D011095:Polyethylenes