Strength comparison of allogenic bone screws, bioabsorbable screws, and stainless steel screw fixation.
Allogenic bone screws are new to the fixation market and have yet to be tested against current fixation materials. An in vitro comparison of the same sizes of stainless steel, bioabsorbable, and allogenic bone screws was undertaken to assess screw resistance to the forces of bending, pullout, and shear. Using aluminum plates to support the screws, forces up to 1000 Newtons were applied to six to eight samples of each type of screw. During each test, stainless steel screws withstood the maximum force that could be exerted by the testing apparatus without failing (bending, 113.9 +/- 11.8 N mean +/- SE; pullout 999.1 +/- 33.7 N; and shear, 997.5 +/- 108.8 N). In each test, compared to bioabsorbable screws, allogenic bone screws failed faster (pullout, allogenic: 12.4 +/- 1.1 seconds vs. bioabsorbable, 120.6 +/- 13.8 seconds; p = .001; bending, allogenic: 53.4 +/- 4.8 seconds vs. bioabsorbable, 201.9 +/- 11.1 seconds; p = .001; shear, allogenic 13.5 +/- 1.4 seconds vs. bioabsorbable, 43.8 +/- 0.9 seconds; p = .001) under equivalent (pullout: bioabsorbable, 385.0 +/- 18.4 N vs. allogenic, 401.0 +/- 35.9 N; p = .001) or lower (bending, allogenic: 4.7 +/- 0.2 N vs. bioabsorbable, 11.0 +/- 0.9 N; p = .675; shear, allogenic: 312.1 +/- 15.5 N vs. bioabsorbable 680.9 +/- 8.5 N; p = .001) loads, and in a highly variable fashion. Overall, the bioabsorbable screws withstood the forces of bending, pullout, and shear better than the allogenic screws, and stainless steel screws outperformed both bioabsorbable and allogenic screws. Despite these results, allogenic screws could still be useful in compliant patients who would benefit from their osteoconductive properties.
Rano
James A
JA
Oakwood Healthcare System, Dearborn, MI, USA.
Savoy-Moore
Ruth T
RT
Fallat
Lawrence M
LM
D020341:Absorbable Implants; D000704:Analysis of Variance; D001672:Biocompatible Materials; D001863:Bone Screws; D019544:Equipment Failure Analysis; D005593:Fracture Fixation, Internal / Q000295:instrumentation*; D017102:Fracture Healing; D006801:Humans; D008422:Materials Testing; D011108:Polymers; D013193:Stainless Steel; D013718:Tensile Strength
D001672:Biocompatible Materials; D011108:Polymers; D013193:Stainless Steel