Compositional stability and marginal accuracy of complete cast crowns made with as-received and recast type III gold alloy.
BACKGROUND
The effect of combining new and recast metal on the compositional stability of the alloy used and accuracy of the final restoration is not known.


OBJECTIVE
This study characterized the elemental compositional stability of as-received and recast type III gold alloy. The effect of combining these alloys on the marginal accuracy of complete cast crowns also was evaluated.


METHODS
Sixty standardized type III gold alloy complete crowns were made on epoxy resin dies duplicated from a metal master die with conventional laboratory techniques. Three casting protocols (n = 20 each) were established in relation to the proportion of as-received and recast gold alloys: Group A (100% as-received metal), Group B (50% wt new metal, 50% wt once recast metal), and Group C (100% once recast metal). An elemental analysis was performed at 3 sites along the cast crown (cervical, middle, and occlusal) with x-ray energy-dispersive spectroscopy. Marginal accuracy was measured with a microscope before and after cementation. Results were subjected to 1-way analysis of variance followed by the Ryan-Einot-Gabriel-Welsch multiple-range test at a 1% level of significance.


RESULTS
Elemental composition was significantly different among the casting groups (P<.001). The mean weight percentage values were 72.4% to 75.7% Au, 4.5% to 7.0% Pd, 10.7% to 11.1% Ag, 7.8% to 8.4% Cu, and 1.0% to 1.4% Zn. Statistically but not clinically significant differences also were found for marginal accuracy. The marginal discrepancy was less than 25 microm for all casting conditions, with the lowest value recorded for Group A (7 microm), the highest for Group C (12 microm), and an intermediate value for Group B (9 microm) specimens.


CONCLUSIONS
Recasting type III gold alloys may adversely affect the marginal accuracy of complete cast crowns. In this study, however, such effects were not clinically significant.
Ayad
Mohamed F
MF
Section of Restorative Dentistry, Prosthodontics, and Endodontics, College of Dentistry, University of Tanta, Tanta, Egypt. ayadmf@hotmail.com
D000704:Analysis of Variance; D002484:Cementation; D003442:Crowns; D003735:Dental Casting Technique; D004577:Electron Probe Microanalysis; D017743:Equipment Reuse; D006047:Gold Alloys / Q000737:chemistry*; D008422:Materials Testing; D003765:Models, Dental; D017755:Prosthesis Fitting; D015203:Reproducibility of Results
D006047:Gold Alloys