Efficacy of dentin bonding to cervical defects.
The bonding efficacy of sclerotic dentin was determined by measuring the polymerization contraction gap width of a commercial light-activated resin composite in a cervical defect and by measuring the micro-Vicker's hardness at the dentin adhesive surface; morphological characteristics were observed using a scanning electron microscope in extracted human incisors and premolars. Contraction gap formation was completely prevented when the cavity wall was primed with 35 vol% glyceryl mono-methacrylate solution after 0.5 mol/L EDTA conditioning. The contraction gap width was significantly decreased when the resin composite was filled into the sclerotic dentin cavity even when priming was omitted. These results suggest that the sclerotic dentin, which is frequently observed in cervical defects, should be preserved as a substrate because it exhibits an effect of dentin priming and is suitable for bonding.
Tani
C
C
Department of the Operative Dentistry, Showa University School of Dentistry, 2-1-1 Kitasenzoku, Ohta-ward, Tokyo 145-8515, Japan.
Itoh
K
K
Hisamitsu
H
H
Wakumoto
S
S
D000134:Acid Etching, Dental; D001641:Bicuspid; D002114:Calcinosis / Q000473:pathology*; D002614:Chelating Agents / Q000737:chemistry; D003188:Composite Resins / Q000737:chemistry*; D001840:Dental Bonding; D003737:Dental Cavity Preparation; D018772:Dental Marginal Adaptation; D003804:Dentin / Q000648:ultrastructure*; D003809:Dentin, Secondary / Q000648:ultrastructure*; D017220:Dentin-Bonding Agents / Q000737:chemistry*; D004492:Edetic Acid / Q000737:chemistry; D005989:Glycerides / Q000737:chemistry; D006244:Hardness; D006801:Humans; D007180:Incisor; D008689:Methacrylates / Q000737:chemistry; D008855:Microscopy, Electron, Scanning; D011108:Polymers / Q000737:chemistry; D013223:Statistics as Topic; D013499:Surface Properties; D019237:Tooth Cervix / Q000648:ultrastructure*
D002614:Chelating Agents; D003188:Composite Resins; D017220:Dentin-Bonding Agents; D005989:Glycerides; D008689:Methacrylates; D011108:Polymers; C069750:glyceryl methacrylate; D004492:Edetic Acid