Hydroxyapatite deposition by alternating soaking technique on poly(vinyl alcohol)-coated polyethylene films.
A poly(vinyl alcohol) (PVA)-coating on polyethylene films, prepared by repetitive adsorption/drying in an aqueous PVA solution, accelerated hydroxyapatite (HAp) deposition by an altemate soaking in aqueous solutions containing Ca2+ and PO4(3-) ions. X-ray photoelectron spectra of the surface of the HAp-deposited film showed the presence of calcium and phosphorus of a suitable peak ratio for HAp formation. X-ray diffraction analyses also revealed peaks corresponding to HAp. Scanning electron microscopic observation showed the surface of the HAp layer to be smooth, with nano-ordered dotted threads in networks. A simple PVA coating on a surface will serve as a novel system for accelerated HAp formation via alternating soaking.
Serizawa
T
T
Department of Applied Chemistry and Chemical Engineering, Faculty of Engineering, Kagoshima University, Japan.
Kawanishi
N
N
Akashi
M
M
D002130:Calcium Phosphates; D020099:Coated Materials, Biocompatible / Q000138:chemical synthesis* / Q000737:chemistry; D017886:Durapatite / Q000737:chemistry*; D008722:Methods; D008855:Microscopy, Electron, Scanning; D020959:Polyethylene / Q000737:chemistry; D011142:Polyvinyl Alcohol / Q000737:chemistry; D012996:Solutions; D013499:Surface Properties; D014961:X-Ray Diffraction
D002130:Calcium Phosphates; D020099:Coated Materials, Biocompatible; D012996:Solutions; C485828:alpha-tricalcium phosphate; C485830:tetracalcium phosphate; C485838:calcium phosphate, monobasic, anhydrous; D020959:Polyethylene; D011142:Polyvinyl Alcohol; D017886:Durapatite; C020243:calcium phosphate; C485829:calcium phosphate, dibasic, anhydrous