title: Improvement in zirconia osseointegration by means of a biological glass coating: An in vitro and in vivo investigation.
abstract: The biocompatibility and osseointegration of zirconia (ZrO(2)), either coated with RKKP bioglazeor uncoated, were evaluated in vitro and in vivo. The in vitro test was performed in human osteoblasts, whereas maximal sensitization was performed in 23 Dunkin Hurtley guinea pigs. RKKP bioglaze-coated and uncoated (controls) ZrO(2) cylinders were implanted in the distal femoral epiphyses of 14 Sprague-Dawley rats under general anesthesia, and animals were sacrificed at 30 and 60 days. Lactate dehydrogenase, alkaline phosphatase, and Thiazolyl Blue (MTT) were tested in vitro. A graded score was used for evaluating the results of the sensitization test. Histomorphometry and microhardness testing were performed to quantify the osseointegration rate, as well as bone quality around the implants. Neither in vitro cytotoxicity nor sensitization were observed. Histomorphometry demonstrated that at 30 days, the affinity index was significantly higher in coated implants than in uncoated ones (p < 0.05); at 60 days, the behavior of coated implants was better than that of uncoated ones, but differences were not significant. Significant increases in bone microhardness were found at 1000 microm from the interface area for both uncoated (p < 0.0005) and RKKP bioglaze-coated (p < 0.0005) ZrO(2), and also within 200 microm from the interface (p = 0.014) but only for coated ZrO(2.) These results suggest that RKKP bioglaze-coated ZrO(2) permits biocompatible devices with improved osseointegration properties to be manufactured.
authors: Experimental Surgery Department, Research Institute Codivilla Putti-Rizzoli Orthopaedic Institute via di Barbiano 1/10, 40136, Bologna, Italy. nicolo.nicolialdini@ior.it
authors: N Nicoli
authors: NN
authors: Aldini
authors: M
authors: M
authors: Fini
authors: G
authors: G
authors: Giavaresi
authors: P
authors: P
authors: Torricelli
authors: L
authors: L
authors: Martini
authors: R
authors: R
authors: Giardino
authors: A
authors: A
authors: Ravaglioli
authors: A
authors: A
authors: Krajewski
authors: M
authors: M
authors: Mazzocchi
authors: B
authors: B
authors: Dubini
authors: M G
authors: MG
authors: Ponzi-Bossi
authors: F
authors: F
authors: Rustichelli
authors: V
authors: V
authors: Stanic
mesh_terms: D000818:Animals; D018786:Bone Substitutes / Q000592:standards; D016923:Cell Death / Q000187:drug effects; D002516:Ceramics; D020099:Coated Materials, Biocompatible / Q000494:pharmacology / Q000592:standards* / Q000633:toxicity; D005260:Female; D006168:Guinea Pigs; D006801:Humans; D007114:Immunization; D020007:Implants, Experimental / Q000592:standards; D008422:Materials Testing; D019563:Mechanics; D016348:Osseointegration; D010006:Osteoblasts / Q000187:drug effects; D051381:Rats; D015996:Survival Rate; D015040:Zirconium / Q000494:pharmacology / Q000592:standards* / Q000633:toxicity
chemical_list: C022107:Bioglass; D018786:Bone Substitutes; D020099:Coated Materials, Biocompatible; D015040:Zirconium; C028541:zirconium oxide