Oxidative pyrolysis of organic ion exchange resins in the presence of metal oxide catalysts.
Pretreatment of the organic ion exchange resins by oxidative pyrolysis is effective for volume reduction before vitrification. In this work, pyrolysis of two nuclear-grade resins, Purolite NRW100 (cationic) and NRW400 (anionic), was examined using a laboratory-scale theromgravimetric analyzer (TGA) in air. It was shown that the cationic resin was harder to degrade and was less volatile compared to anionic resin. Off-gas data revealed the presence of SO2, CO2, CO, and H2O during oxidative pyrolysis of cationic resin from 30 to 800 degrees C. Trimethylamine, CO2, CO, and ethyl formate were found in the case of anionic resin. In addition, oxidative pyrolysis of the mixed resins (50/50 wt.%) showed the existence of the gases nearly at the temperatures where the gases would evolve if the results of two different resins were superimposed. Several metal salts including CuSO4*5H2O, CuO, and FeSO4*7H2O, as well as the ions Cu2+ pre-loaded on the resins had a catalytic effect on the oxidative pyrolysis of cationic resins, in which the decomposition of functional groups and polymer matrices was enhanced. Such catalytic effect was highlighted by a large decrease in activation energy calculated according to a degradation mechanism involving four consecutive reactions.
Juang
Ruey-Shin
RS
Department of Chemical Engineering, Yuan Ze University, 320, Chung-Li, Taiwan, ROC.
Lee
Tsye-Shing
TS
D002384:Catalysis; D007475:Ion Exchange Resins / Q000737:chemistry; D007700:Kinetics; D008670:Metals / Q000737:chemistry; D010084:Oxidation-Reduction; D010087:Oxides / Q000737:chemistry; D011108:Polymers; D011850:Radioactive Waste; D012037:Refuse Disposal / Q000379:methods; D012116:Resins, Plant / Q000737:chemistry*
D007475:Ion Exchange Resins; D008670:Metals; D010087:Oxides; D011108:Polymers; D011850:Radioactive Waste; D012116:Resins, Plant