Controlled synthesis and magnetic properties of 2D and 3D iron azide networks infinity2[Fe(N3)2(4,4'-bpy)] and infinity3[Fe(N3)2(4,4'-bpy)].
Controlled synthesis of transition metal complexes with mixed ligands has led to two new compounds with the same empirical formula [Fe(N3)2(4,4'-bpy)] (4,4'-bpy=4,4'- bipyridine). The compound 2D-[Fe(N3)2(4,4'-bpy)] (I) contains end-on (EO) bridging azido ligands. It crystallizes in the orthorhombic crystal system, space group Cmmm (No. 65): a=11.444(2) A, b=15.181(3) A, c=3.458(1) A, V=600.8(2) A(3), and Z=2. The compound 3D-[Fe(N3)2(4,4'-bpy)] (II) contains end-to-end (EE) azido bridges. It belongs to the tetragonal crystal system, space group P4(1)2(1)2 (No. 92): a=8.132(1) A, b=8.132(1) A, c=16.708(3) A, V=1104.9(5) A(3), and Z=4. Crystals of I and II have been grown by the diffusion method. Phase-pure samples of both compounds have been obtained by means of an optimal solution synthesis. Spontaneous long-range magnetic ordering was found in both I and II, with I being a metamagnet, and II being a ferromagnet. For I, in the low-field region, multiple transitions at TN1=20 K and TN2=5 K were observed, and these indicated the existence of Fe moment reorientation. Heat capacity measurements on II confirmed ferromagnetic transition at TC=20 K.
Fu
Aihua
A
Department of Chemistry, Rutgers University, Camden New Jersey 08102, USA.
Huang
Xiaoying
X
Li
Jing
J
Yuen
Tan
T
Lin
Chyan Long
CL