Room temperature oxidation of Cu(3)Ge films grown on Si and Si(1-x)Ge(x) substrates.
Room temperature oxidation of Cu3Ge films grown on Si, Si(0.85)Ge(0.15) and Si(0.52)Ge(0.48) substrates, respectively, at a temperature of 200-300 degrees C was studied using transmission electron microscopy (TEM) in conjunction with energy dispersive spectrometry (EDS) and scanning electron microscopy (SEM). For Cu(3)Ge films grown at 200 degrees C and subsequently exposed in air for 1 week oxide protrusions and oxide networks appeared in the film surface and grain boundaries of Cu(3)Ge, respectively. At room temperature O from air and Si from the substrate, diffused along the grain boundaries of Cu(3)Ge to react with Cu(3)Ge grains, initiating the Cu(3)Si-catalyzed oxidation. Cu(3)Ge films are superior to Cu(3)(Si(1-x)Gex) films in retarding Cu(3)Si-catalyzed oxidation. Annealing at 300 degrees C allowed Si diffusion from the substrate into the Cu(3)Ge overlayer to form Cu(3)(Si(1-x)Gex), enhancing the Cu(3)Si-catalyzed oxidation rate. In the present study, Cu(3)Ge films grown on Si(0.52)Ge(0.48) at 200 degrees C show the best resistance to room temperature oxidation because higher Ge concentration in the substrate and lower temperature annealing can more effectively retard Si diffusion from the substrate into the Cu(3)Ge overlayer, and hence reduce the Cu(3)Si-catalyzed oxidation rate.
Liang
Hsuan-Han
HH
Department of Materials Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan, ROC.
Luo
Jian-Shing
JS
Lin
Wen-Tai
WT