[Mechanical studies of lumbar interbody fusion implants].
In addition to autogenous or allogeneic bone grafts, fusion cages composed of metal or plastic are being used increasingly as spacers for interbody fusion of spinal segments. The goal of this study was the mechanical testing of carbon fiber reinforced plastic (CFRP) fusion cages used for anterior lumbar interbody fusion. With a special testing device according to American Society for Testing and Materials (ASTM) standards, the mechanical properties of the implants were determined under four different loading conditions. The implants (UNION cages, Medtronic Sofamor Danek) provide sufficient axial compression, shear, and torsional strength of the implant body. Ultimate axial compression load of the fins is less than the physiological compression loads at the lumbar spine. Therefore by means of an appropriate surgical technique parallel grooves have to be reamed into the endplates of the vertebral bodies according to the fin geometry. Thereby axial compression forces affect the implants body and the fins are protected from damaging loading. Using a supplementary anterior or posterior instrumentation, in vivo failure of the fins as a result of physiological shear and torsional spinal loads is unlikely. Due to specific complications related to autogenous or allogeneic bone grafts, fusion cages made of metal or carbon fiber reinforced plastic are an important alternative implant in interbody fusion.
Bader
R J
RJ
Abteilung Biomechanik, Klinik für Orthopädie und Sportorthopädie, Technische Universität, Connollystrasse 32, 80809 München. rainer.bader@lrz.tum.de
Steinhauser
E
E
Rechl
H
H
Mittelmeier
W
W
Bertagnoli
R
R
Gradinger
R
R
D001696:Biomechanical Phenomena; D002244:Carbon; D000077482:Carbon Fiber; D006801:Humans; D008422:Materials Testing; D008670:Metals; D010969:Plastics; D019736:Prostheses and Implants; D013123:Spinal Fusion / Q000295:instrumentation*; D016474:Weight-Bearing
D000077482:Carbon Fiber; D008670:Metals; D010969:Plastics; D002244:Carbon