Loop memory of haptic materials in posterior chamber intraocular lenses.
OBJECTIVE
To compare the shape recovery ratios after compression of haptic materials used in the manufacture of intraocular lenses (IOLs).


METHODS
Center for Research on Ocular Therapeutics and Biodevices, Storm Eye Institute, Medical University of South Carolina, Charleston, South Carolina, USA.


METHODS
The loop memory of 40 silicone-optic posterior chamber IOLs was studied. All the IOLs had modified-C haptics made of poly(methyl methacrylate) (PMMA; n = 10), polyimide (n = 10), polyvinylidene fluoride (PVDF; n = 10), and polypropylene (PP; n = 10). After the overall diameter of each lens was measured (day 0), the lenses were inserted into plastic wells (9.5 mm in diameter) and immersed in water (37 degrees C) for 1 month. They were then placed on an open plate and allowed to reexpand for 2 months. Overall diameter measurements were performed within 5 minutes of the IOLs' removal from the wells and at subsequent time points (days 14, 28, 30, 60, 74, 88, and 95).


RESULTS
The loop memory of each lens was expressed as the difference between the initial overall diameter measurement (pretest) and the measurement at each time point; the lower the value, the higher the memory. The overall difference among the 4 groups was statistically significant at each time point (P < or = .001). From days 30 to 95, silicone-PMMA, silicone-elastimide, and silicone-PVDF IOLs had similar loop memory mean values, which were significantly lower than the mean value of silicone-PP IOLs (P <.05). The latter design tended to be deformed after removal from the wells, with increased optic-haptic angulation.


CONCLUSIONS
Studying the loop memory of haptic materials (PMMA, polyimide, PVDF, and PP) used in the manufacture of posterior chamber IOLs can help surgeons choose an appropriate IOL for each patient.
Izak
Andrea M
AM
Center for Research on Ocular Therapeutics and Biodevices, Storm Eye Institute, Medical University of South Carolina, Charleston, South Carolina 29425-5536, USA.
Werner
Liliana
L
Apple
David J
DJ
Macky
Tamer A
TA
Trivedi
Rupal H
RH
Pandey
Suresh K
SK
D007910:Lenses, Intraocular; D009757:Nylons / Q000737:chemistry*; D019904:Polymethyl Methacrylate / Q000737:chemistry*; D011126:Polypropylenes / Q000737:chemistry*; D011145:Polyvinyls / Q000737:chemistry*; D011474:Prosthesis Design; D012826:Silicone Elastomers; D013314:Stress, Mechanical; D005465:Fluorocarbon Polymers
D009757:Nylons; D019904:Polymethyl Methacrylate; D011126:Polypropylenes; D011145:Polyvinyls; D012826:Silicone Elastomers; C024865:polyvinylidene fluoride; D005465:Fluorocarbon Polymers