Alumina-alumina artificial hip joints. Part II: characterisation of the wear debris from in vitro hip joint simulations.
Until recently it was not possible to reproduce clinically relevant wear rates and wear patterns in in vitro hip joint simulators for alumina ceramic-on-ceramic hip prostheses. The introduction of microseparation of the prosthesis components into in vitro wear simulations produced clinically relevant wear rates and wear patterns for the first time. The aim of this study was to characterise the wear particles generated from standard simulator testing and microseparation simulator testing of hot isostatically pressed (HIPed) and non-HIPed alumina ceramic-on-ceramic hip prostheses, and compare these particles to those generated in vivo. Standard simulation conditions produced wear rates of approximately 0.1 mm3 per million cycles for both material types. No change in surface roughness was detected and very few wear features were observed. In contrast, when microseparation was introduced into the wear simulation, wear rates of between 1.24 (HIPed) and 1.74 mm3 per million cycles (non-HIPed) were produced. Surface roughness increased and a wear stripe often observed clinically on retrieved femoral heads was also reproduced. Under standard simulation conditions only nanometre-sized wear particles (2-27.5 nm) were observed by TEM, and it was thought likely that these particles resulted from relief polishing of the alumina ceramic. However, when microseparation of the prosthesis components was introduced into the simulation, a bi-modal distribution of particle sizes was observed. The nanometre-sized particles produced by relief polishing were present (1-35nm). however, larger micrometre-sized particles were also observed by both transmission electron microscopy (TEM) (0.021 microm) and scanning electron microscopy (SEM) (0.05-->10 microm). These larger particles were thought to originate from the wear stripe and were produced by trans-granular fracture of the alumina ceramic. In Part I of this study, alumina ceramic wear particles were isolated from the periprosthetic tissues from around Mittelmeier ceramic-on-ceramic hip prostheses. Characterisation of the particles by TEM and SEM revealed a bi-modal size distribution. SEM analysis revealed particles in the 0.05-3.2 microm size range. and TEM revealed particles in the 5-90 nm size range, indicating that microseparation of the prosthesis components may be a common event in vivo. This study (Part II) has revealed that the introduction of microseparation of the prosthesis components during the swing phase of the wear simulation reproduced clinically relevant wear rates, wear patterns and wear particles in in vitro hip joint simulators.
Tipper
J L
JL
Medical & Biological Engineering, School of Molecular Biology and Biochemistry, University of Leeds, UK.
Hatton
A
A
Nevelos
J E
JE
Ingham
E
E
Doyle
C
C
Streicher
R
R
Nevelos
A B
AB
Fisher
J
J
D000537:Aluminum Oxide; D018786:Bone Substitutes / Q000737:chemistry*; D003198:Computer Simulation; D006622:Hip Prosthesis; D006801:Humans; D008855:Microscopy, Electron, Scanning; D011475:Prosthesis Failure; D013314:Stress, Mechanical
D018786:Bone Substitutes; D000537:Aluminum Oxide