Supramolecular cation assemblies of hydrogen-bonded (NH4+/NH2NH3+)(crown ether) in [Ni(dmit)2]-based molecular conductors and magnets.
Hydrogen-bonded supramolecular cation assemblies of (NH4+/NH2-NH3+)(crown ether), where the crown ether is [12]crown-4, [15]crown-5, or [18]crown-6, were incorporated into electrically conducting [Ni(dmit)2] salts (dmit2- = 2-thioxo-1,3-dithiole-4,5-dithiolate). (NH4+)([12]crown-4)[Ni(dmit)2]3(CH3CN)2 had a pyramidal shape, while ionic channels were observed in (NH4+)(0.88)([15]crown-5)[Ni(dmit)(2)]2 and (NH4+)(0.70)([18]crown-6)[Ni(dmit)(2)]2. Both (NH4+)(0.88)([15]crown-5) and (NH4+)(0.70)([18]crown-6) contained regularly spaced [Ni(dmit)(2)] stacks formed by N-H.O hydrogen bonding between the oxygen atoms in crown ethers and the NH4+ ion. NH4+ occurred nonstoichiometrically; there were vacant ionic sites in the ionic channels. The ionic radius of NH4+ is larger than the cavity radius of [15]crown-5 and [18]crown-6. Therefore, NH4+ ions could not pass through the cavity and were distributed randomly in the ionic channels. The static disorder caused the conduction electrons to be randomly localized to the [Ni(dmit)2] stacks. Hydrazinium (NH2-NH3+) formed the supramolecular cations in (NH2-NH3+)([12]crown-4)2[Ni(dmit)2]4 and (NH2-NH3+)2([15]crown-5)3[Ni(dmit)2]6, possessing a sandwich and club-sandwich structure, respectively. To the best of our knowledge, these represent the first hydrazinium-crown ether assemblies to be identified in the solid. In the supramolecular cations, hydrogen bonding was detected between the ammonium or the amino protons of NH2-NH3+ and the oxygen atoms of crown ethers. The sandwich-type cations coexisted with the [Ni(dmit)2] dimer stacks. Although the assemblies were typically semiconducting, ferromagnetic interaction (Weiss temperature = +1 K) was detected in the case of (NH2-NH3+)2([15]crown-5)3[Ni(dmit)2]6. The (NH2-NH3+)0.8([18]crown-6)[Ni(dmit)2]2 and (NH4+)0.76([18]crown-6)[Ni(dmit)2]2 crystals were isomorphous. The large and flexible [18]crown-6 allowed for maintaining the same ionic channel structure through replacement of the NH4+ cation by NH2-NH3+.
Akutagawa
Tomoyuki
T
Research Institute for Electronic Science, Hokkaido University, Sapporo 060-0812, Japan. takuta@imd.es.hokudai.ac.jp
Hasegawa
Tatsuo
T
Nakamura
Takayoshi
T
Inabe
Tamotsu
T