Histologic evaluation of a human immediately loaded titanium implant with a porous anodized surface.
BACKGROUND
Several researchers have demonstrated, in the past decade, in clinical and histologic studies, that immediate loading can be successfully used in implant dentistry. Many factors are thought to be of importance in obtaining mineralized tissues at the interface. One of these factors is the implant surface characteristics. Recently, an implant with a new porous anodized surface has been introduced in the market.


OBJECTIVE
The goal of this study was to histologically evaluate a clinically retrieved immediately loaded implant with a porous anodized surface.


METHODS
After a 6-month loading period, an immediately loaded implant with a porous anodized surface that had been inserted in the posterior maxilla was retrieved.


RESULTS
Histology showed that mineralized tissue was present at the interface and the bone-implant contact percentage was about 60%. No gaps or fibrous tissue or inflammatory infiltrate were present at the interface.


CONCLUSIONS
Results show that immediate loading of dental implants has no untoward effects on the formation of mineralized tissues at the interface. Immediate loading is a possible alternative in implant dentistry. key words: dental implants, histology, immediate loading, oxide coating, porous surface
Dental School, University of Chieti, Italy.
Marco
M
Degidi
Giovanna
G
Petrone
Giovanna
G
Iezzi
Adriano
A
Piattelli
D001557:Benzenesulfonates; D016723:Bone Remodeling / Q000502:physiology; D002113:Calcification, Physiologic / Q000502:physiology; D004396:Coloring Agents; D000044:Dental Abutments; D015921:Dental Implants; D017267:Dental Prosthesis Design; D004563:Electrochemistry; D006801:Humans; D008297:Male; D008437:Maxilla / Q000601:surgery / Q000648:ultrastructure; D008875:Middle Aged; D016348:Osseointegration; D016613:Plastic Embedding; D016062:Porosity; D016622:Silver Staining; D013499:Surface Properties; D014025:Titanium / Q000737:chemistry*; D014048:Tolonium Chloride; D016474:Weight-Bearing
D001557:Benzenesulfonates; D004396:Coloring Agents; D015921:Dental Implants; D014048:Tolonium Chloride; C086337:acid fuchsin; D014025:Titanium