Characterization of ciclosporin A loaded poly (D,L lactide-co-glycolide) microspheres using modulated temperature differential scanning calorimetry.
The aim of this study was to investigate the physical structure of poly (D,L lactide-co-glycolide) (PLGA) microspheres loaded with ciclosporin A in terms of the amorphous properties of the individual components and the phase separation characteristics of the binary systems. Microspheres were prepared using a standard oil-in-water emulsion technique. The thermal properties of the PLGA, ciclosporin A and loaded spheres were investigated using modulated temperature differential scanning calorimetry (MTDSC) using a TA Instruments MTDSC 2920, with scanning electron microscopy (SEM), X-ray powder diffraction (XRD) and high-performance liquid chromatography used as supportive techniques. MTDSC indicated a glass transition for ciclosporin A in the reversing heat flow signal at 107 degrees C, supported by temperature cycling studies, while XRD showed clear evidence for diffraction peaks, thereby indicating that the material as received is semi-crystalline. The unloaded PLGA spheres showed a glass transition (Tg) at 43 degrees C, with no reduction in Tg being observed on loading the peptide up to 50%, w/w. Similarly, no evidence for diffraction peaks were seen for the drug-loaded systems, although the glass transition corresponding to the peptide was observed for the loaded microspheres, suggesting that the drug is present as a separate amorphous phase. Similarly, SEM studies showed the appearance of distinct "islands" on the surface of the spheres that are suggested to correspond to the drug phase, with the size of the islands increasing with drug loading. Evidence is therefore presented that ciclosporin A may exist in a range of solid states, with the degree of crystallinity being altered by processing. In addition, there appears to be little or no miscibility between the drug and PLGA using the manufacturing protocol employed here. These findings may have implications for the choice of manufacturing protocol, the release of peptide drugs from PLGA microspheres and the chemical and physical stability of such drugs.
Passerini
N
N
Dip Scienze Farmaceutiche, Università degli Studi di Bologna, Italy.
Craig
D Q M
DQ
D001672:Biocompatible Materials / Q000737:chemistry*; D055598:Chemical Phenomena; D002626:Chemistry, Pharmaceutical; D002627:Chemistry, Physical; D016572:Cyclosporine / Q000008:administration & dosage* / Q000737:chemistry; D003692:Delayed-Action Preparations; D004337:Drug Carriers / Q000737:chemistry*; D004355:Drug Stability; D007166:Immunosuppressive Agents / Q000008:administration & dosage* / Q000737:chemistry; D019344:Lactic Acid / Q000737:chemistry*; D008855:Microscopy, Electron, Scanning; D008863:Microspheres; D011100:Polyglycolic Acid / Q000737:chemistry*; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011108:Polymers / Q000737:chemistry*; D013696:Temperature
D001672:Biocompatible Materials; D003692:Delayed-Action Preparations; D004337:Drug Carriers; D007166:Immunosuppressive Agents; D011108:Polymers; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011100:Polyglycolic Acid; D019344:Lactic Acid; D016572:Cyclosporine