Characterization of the structures of poly(urea-urethane) microcapsules.
A series of poly(urea-urethane) microcapsules containing phthalate derivatives as a core material were prepared by an interfacial polymerization process in order to investigate the structural formation mechanism. Scanning electron microscopy (SEM) analysis for the cross sections of microcapsules revealed the systematic formations of porous structures followed by the formation of core/shell structures. Critical values of the core oil content for the formation of porous and core/shell structures were obtained from SEM results and the critical values were found to be proportional to the solubility parameters of core materials. Dynamic mechanical measurements indicated an amorphous structure of wall membrane and the glass transition temperature was found to decrease with increasing the core oil content suggesting a plasticizing effect. The surface amount of the core oils absorbed in the wall membrane was estimated using time of flight secondary ion spectroscopy analysis and found to increase with increasing the oil content before reaching constant. This tendency was interpreted in terms of the structural formation of the microcapsules. The results obtained in the present investigation were reasonably understood on the basis of swelling theory of wall membrane and the Flory-Huggins interaction parameters of the systems were discussed.
Matsunami
Yuki
Y
Fujinomiya Laboratory, Fuji Photo Film Co. Ltd, 200 Onakazato, Fujinomiya, 418-8666, Shizuoka, Japan.
Ichikawa
Kimio
K
D000465:Algorithms; D002214:Capsules; D004055:Differential Thermal Analysis; D004339:Drug Compounding; D013058:Mass Spectrometry; D008567:Membranes, Artificial; D008855:Microscopy, Electron, Scanning; D009821:Oils; D010795:Phthalic Acids / Q000737:chemistry; D011140:Polyurethanes / Q000737:chemistry*; D013696:Temperature; D013816:Thermodynamics
D002214:Capsules; D008567:Membranes, Artificial; D009821:Oils; D010795:Phthalic Acids; D011140:Polyurethanes; C044690:polyetherurethane urea