Scanning electron microscopy observation of the substructural evolution of aluminium alloys during cold rolling and partial annealing.
Classical etching techniques for revealing cold deformation and partial recrystallisation in metals have been optimised for optical microscopy, which is limited by its resolution. Detailed studies of the mechanisms involved in recovery and recrystallisation during heat treatment are generally made by transmission electron microscopy. The limitation of this technique, with a few exceptions, is its small field of view and the small fraction of the sample available for inspection. The present article departs from the statement that etching, which is a surface alteration technique, must have effects that are detectable by scanning electron microscope (SEM). It was found that carefully adapted polishing and etching procedures allow for substructural investigations by SEM, resulting in various advantages compared with both optical microscopy and TEM.
Schouwenaars
Rafael
R
Department of Mechanical Engineering, National Autonomous University of México, México City, DF. raf_schouwenaars@yahoo.com
Cerrud
Sara
S
Ortiz
Armando
A