title: Effect of tooth brushing and thermal cycling on a surface change of ceromers finished with different methods.
abstract: This in vitro study evaluated the effect of tooth brushing and thermal cycling on the surface lustre and surface roughness of three ceromer systems treated with different surface finishing methods. The ceromers studied were: (1). Artglass, (2). Targis, (3). Sculpture and (4). the control group, Z 100. Half of the Targis and Sculpture groups were polished and the rest were coated with staining and glazing solution, respectively. All specimens were subjected to thermocycling 10000 times. Tooth brushing abrasion tests were performed in a customized tooth-brushing machine with 500 g weight applied on a back-and-forth cycle for 20000 repetitions. The lustre determined by measuring the light reflection area and the average roughness was compared between groups and between pre- and post-test values. All materials showed a lower lustre and rougher surface after thermocycling and tooth brushing (P < 0.05). All ceromer specimens, except glazed Sculpture, showed a higher lustre and similar roughness to the control group. The post-brushing results revealed that glazed Sculpture presented discretely fallen out glaze coatings and had maximum change. However, stained Targis showed minimum change (P < 0.05) and polished Targis presented more changes than that of the staining treatment. It is therefore concluded that the glaze coatings for Sculpture don't exhibit long-term durability, while stain coatings for Targis acted like a protective layer.
mesh_terms: D000704:Analysis of Variance; D002516:Ceramics; D003188:Composite Resins; D003775:Dental Polishing; D005899:Glass Ionomer Cements; D006358:Hot Temperature; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D012823:Silicate Cement; D012822:Silicon Dioxide; D013499:Surface Properties; D014099:Toothbrushing; D015040:Zirconium
chemical_list: D003188:Composite Resins; C113550:FiberKor, sculpture; D005899:Glass Ionomer Cements; C083568:Z100 composite resin; C111841:ceromer; C111282:dental polyglass; D012823:Silicate Cement; D012822:Silicon Dioxide; D015040:Zirconium