Use of municipal incinerator bottom ash as sintering promoter in industrial ceramics.
The use of glassy frits obtained from municipal incinerator bottom ash and glass cullet, as sintering promoters in the production process of porcelainized stoneware, was investigated. The emphasis was on studying the similarities and differences with respect to the standard body. The characterization involved the application of several techniques: chemical analysis, X-ray powder diffraction, linear shrinkage during firing, water absorption, bending strength and spot resistance test. The results show that, the addition of these glassy frits in the body improve the characteristics of water absorption and spot resistance which is related to the absence of surface porosity originated by the glassy phase. Moreover, addition of glassy frits to the porcelanized stoneware body does not change significantly its bending strength. In the firing conditions used there is a slight worsening in the tiles planarity, while there is a significant modification of the color, which becomes darker with respect to the base body.
Barbieri
L
L
Dipartimento di Ingegneria dei Materiali e dell'Ambiente, Facoltà di Ingegneria, Università di Modena e Reggio Emilia, Italy. barbieri.luisa@unimo.it
Corradi
A
A
Lancellotti
I
I
Manfredini
T
T
D002516:Ceramics; D003247:Conservation of Natural Resources; D005898:Glass; D017745:Incineration; D008420:Manufactured Materials; D008422:Materials Testing; D012037:Refuse Disposal