Composite restorations: influence of flowable and self-curing resin composite linings on microleakage in vitro.
This in vitro study evaluated the microleakage at enamel (occlusal) and dentin (gingival) margins of MOD resin composite restorations made with different incremental insertion techniques. MOD cavities were prepared on 60 extracted human molars with the proximal margins placed 1 mm below the cemento-enamel junction. All teeth were acid-etched and treated with One-Step adhesive, then restored with a hybrid resin composite (Renew) with and without a flowable composite (AEliteflo) or a self-curing composite (Bisfil 2B) as the first increment in the proximal boxes. The time of placement of the second increment in relation to curing of the first increment was also varied. After polishing, the teeth were soaked in 0.5% basic fuchsin for 24 hours, sectioned and evaluated for dye penetration. None of the restorative techniques prevented microleakage at the enamel and dentin margins. However, microleakage at dentin margins were significantly reduced by the use of a flowable composite as the first increment in the proximal boxes. Time of placement in relation to curing had no influence on microleakage. Microleakage was lower at enamel margins than at dentin margins; however, besides microleakage at the enamel-restoration interface, 37 of the 60 restored teeth (62%) displayed at least one white line in enamel adjacent to the composite restoration.
Peutzfeldt
Anne
A
Department of Dental Materials, School of Dentistry, University of Copenhagen, Denmark. apz@odont.ku.dk
Asmussen
Erik
E
D017609:Barium Compounds; D017438:Bisphenol A-Glycidyl Methacrylate; D002126:Calcium Hydroxide; D003188:Composite Resins; D003763:Dental Leakage / Q000517:prevention & control*; D003764:Dental Materials; D003793:Dental Restoration, Permanent / Q000379:methods*; D006801:Humans; D008963:Molar; D012822:Silicon Dioxide
C121035:Aeliteflo; D017609:Barium Compounds; D003188:Composite Resins; D003764:Dental Materials; C078905:Bisfil; D017438:Bisphenol A-Glycidyl Methacrylate; D012822:Silicon Dioxide; C040409:Renew (dental material); D002126:Calcium Hydroxide