Bioactive calcium phosphate invert glass-ceramic coating on beta-type Ti-29Nb-13Ta-4.6Zr alloy.
A fine, strong coating consisting of a bioactive calcium phosphate invert glass-ceramic can be prepared easily by reaction of the glassy phase with an oxide layer formed on a new beta-type titanium alloy, Ti-29Nb-13Ta-4.6Zr, when the metal, on which the mother glass powders with a composition of 60CaO-30P(2)O(5)-7Na(2)O-3TiO(2) in mol% are placed, is heated at 800 degrees C in air. A compositionally gradient layer is developed on the titanium alloy during the heating. Tensile bonding strength of the coating to the metal is significantly higher than those of the coatings to conventional metals such as Ti-6Al-4V alloy or pure titanium. The oxidized layer on Ti-29Nb-13Ta-4.6Zr alloy is relatively thinner than that on Ti-6Al-4V alloy even with heat treatment in air; large tensile stresses are not generated in the layer.
Kasuga
Toshihiro
T
Department of Materials Science and Engineering, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, Nagoya 466-8555, Japan. kasugato@mse.nitech.ac.jp
Nogami
Masayuki
M
Niinomi
Mitsuo
M
Hattori
Tomokazu
T
D000497:Alloys / Q000737:chemistry*; D001672:Biocompatible Materials / Q000737:chemistry*; D002130:Calcium Phosphates / Q000737:chemistry*; D002516:Ceramics / Q000737:chemistry*; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning
D000497:Alloys; D001672:Biocompatible Materials; D002130:Calcium Phosphates; C485828:alpha-tricalcium phosphate; C485830:tetracalcium phosphate; C485838:calcium phosphate, monobasic, anhydrous; C023506:Glass ceramics; C020243:calcium phosphate; C485829:calcium phosphate, dibasic, anhydrous