J-integral fracture toughness and tearing modulus measurement of radiation cross-linked UHMWPE.
Radiation and chemical cross-linking of medical grade ultrahigh molecular weight polyethylene (UHMWPE) has recently been utilized in an effort to improve wear performance of total joint replacement components. However, reductions in mechanical properties with cross-linking are cause for concern regarding the use of cross-linked UHMWPE for high-stress applications such as in total knee replacement prostheses. In this study, the fracture behavior of radiation cross-linked UHMWPE was compared to that of uncross-linked UHMWPE. The Rice and Sorensen model that utilizes mechanical parameters obtained from uniaxial tensile and compact tension tests was used to calculate the steady state J-integral fracture toughness, Jss, for radiation cross-linked UHMWPE. Jss decreased monotonically with increase in radiation dose. UHMWPE exhibited tough, ductile tearing behavior with stable crack growth when it was cross-linked using a gamma radiation dose of 0-50 kGy. However, in cross-linked UHMWPE irradiated to a dose of 100 and 200 kGy, unstable fracture occurred spontaneously upon attaining the initial crack driving force, J1c. This indicates that a high degree of cross-linking is less desirable for high-stress applications in orthopaedic implants. However, a substantial increase in J1c, even at a low degree of cross-linking, suggests that a low degree of cross-linking may be beneficial for resistance to delamination and catastrophic failure, both of which require an initiation step for the fracture to propagate in the material. This mechanical test should, however, be considered along with fatigue tests and joint simulator testing before determination of an appropriate amount of cross-linking for total joint replacement prostheses that experience high stresses.
Gomoll
A
A
Orthopaedic Research Laboratory, Department of Orthopaedic Surgery, Brigham and Women's Hospital, Harvard Medical School, 75 Francis Street, MRB 106, Boston, MA 02135, USA.
Wanich
T
T
Bellare
A
A
D019645:Arthroplasty, Replacement, Knee; D003432:Cross-Linking Reagents; D004307:Dose-Response Relationship, Radiation; D005720:Gamma Rays; D006801:Humans; D008422:Materials Testing; D011095:Polyethylenes / Q000528:radiation effects*; D019736:Prostheses and Implants; D013314:Stress, Mechanical; D013718:Tensile Strength
D003432:Cross-Linking Reagents; D011095:Polyethylenes; C111601:ultra-high molecular weight polyethylene