Surface texture and some properties of acrylic resins submitted to chemical polishing.
The effects of chemical polishing on dental acrylic resin properties are not well clarified. This study evaluated the effect of chemical and mechanical polishing on the residual monomer release (RM), Knoop hardness (KH), transverse strength (TS) and surface texture (ST) of a heat- and self-cured acrylic resin. Four groups were formed: GI-self-cured resin/mechanical polishing; GII-self-cured resin/chemical polishing; GIII-heat-cured resin/mechanical polishing; GIV-heat-cured resin/chemical polishing. Following the polishing procedures, specimens were stored in distilled water at 37 degrees C. The KH and RM measurements were taken after 1, 2, 8 and 32 days of storage, and TS after 2, 8 and 32 days. Surface texture was observed under SEM evaluation. Results were compared statistically at a confidence level of 95%. The following conclusions were drawn: (1) regardless of the acrylic resin and the period of analysis, chemical polishing increased RM levels, reduced KH, and did not affect TS significantly; (2) water storage increased the surface hardness of GII and GIV; (3) GII and GIV showed a smooth and wavy surface under SEM evaluation.
Braun
K O
KO
Removable Partial Prosthodontic, Santa Maria Dental School, Federal University of Santa Maria (UFSM), Santa Maria, Rio Grande do Sul, Brazil.
Mello
J A N
JA
Rached
R N
RN
Del Bel Cury
A A
AA
D000180:Acrylic Resins; D003775:Dental Polishing / Q000379:methods*; D006801:Humans; D008854:Microscopy, Electron; D013499:Surface Properties
D000180:Acrylic Resins