Effect of stair descent loading on ultra-high molecular weight polyethylene wear in a force-controlled knee simulator.
A loading protocol approximating forces, torques and motions at the knee during stair descent was developed from previously published data for input into a force-controlled knee simulator. A set of total knee replacements (TKRs) was subjected to standard walking cycles and stair descent cycles at a ratio of 70: 1 for 5 million cycles. Another set of implants with similar articular geometry and the same ultra-high molecular weight polyethylene (UHMWPE) resin (GUR 415), sterilization and packaging was tested with standard walking cycles only. Implant kinematics, gravimetric wear and surface roughness of the UHMWPE inserts were analysed for both sets of implants. Contact stresses were calculated for both loading protocols using a Hertzian line contact model. Significantly greater weight loss (p < 0.05) and more severe surface damage of UHMWPE inserts resulted with the walking + stair descent loading protocol compared to walking cycles only. Anterior-posterior (AP) tibiofemoral contact point displacements were lower during stair descent than walking, but not significantly different (p = 0.05). Contact stresses were significantly higher during stair descent than walking, owing to higher axial loads and the smaller radius of curvature of the femoral components at higher flexion angles. High contact stresses on UHMWPE components are likely to accelerate the fatigue of the material, resulting in more severe wear, similar to what is observed in retrieved implants. Thus the inclusion of loading protocols for activities of daily living in addition to walking is warranted for more realistic in vitro testing of TKRs.
Benson
L C
LC
Department of Bioengineering, Clemson University, Clemson, South Carolina 29634-0905, USA
DesJardins
J D
JD
Harman
M K
MK
LaBerge
M
M
D000203:Activities of Daily Living; D019544:Equipment Failure Analysis / Q000295:instrumentation* / Q000379:methods* / Q000592:standards; D007717:Knee / Q000503:physiopathology*; D007720:Knee Prosthesis; D008124:Locomotion / Q000502:physiology*; D008422:Materials Testing; D009068:Movement / Q000502:physiology; D011095:Polyethylenes; D015203:Reproducibility of Results; D012680:Sensitivity and Specificity; D013314:Stress, Mechanical; D013499:Surface Properties; D019415:Torque
D011095:Polyethylenes; C111601:ultra-high molecular weight polyethylene