Extended creep behavior of dental composites using time-temperature superposition principle.
OBJECTIVE
The purpose of the study was to characterize long-term creep deformation behavior of selected dental composite resins.


METHODS
Two hybrid composite resins (one midifill type Clearfill and the other minifill type Charisma) and one microfill type (Durafill) were evaluated. 25 mm x 10 mm x 2 mm rectangular bar specimens were subjected to single cantilever mode of flexural loading and their creep compliance changes determined over 10 min durations in the temperature range of 32-120 degrees C at 5 degrees C intervals. The reference temperature selected was the body temperature of 37 degrees C for the oral environment. All creep compliance curves at other temperatures were shifted along the log time axis to superimpose them on the reference temperature (37 degrees C) curve to generate an extended isothermal master curve over eight decades of time (seconds). The shift factors were determined as a function of temperature and fitted by the least square method to the William-Landel-Ferry model.


RESULTS
The data showed excellent fit to the model, indicating the validity of the model to characterize the long-term behavior using the time-temperature superposition principle. The creep compliance changed from initial mean values of 76, 245 and 605 microm(2)/N to 3 year mean values of 217, 880 and 1653 microm(2)/N for Clearfill, Charisma and Durafill systems, respectively. These means were significantly different both as a function of composites and time (p<0.05).


CONCLUSIONS
The results indicate that resin volume fraction and filler parameters may play a critical role in the long-term deformation and energy release processes, and these processes may be an important influence on the long-term clinical durability of composite restorations.
Vaidyanathan
Tritala K
TK
Department of Restorative Dentistry, NJ Dental School, UMDNJ, 110 Bergen Street, Newark, NJ 07103, USA. vaidyatk@umdnj.edu
Vaidyanathan
Jayalakshmi
J
Cherian
Zena
Z
D003187:Compliance; D003188:Composite Resins / Q000737:chemistry*; D019232:Dental Restoration Failure; D003799:Dental Stress Analysis; D004548:Elasticity; D016018:Least-Squares Analysis; D008422:Materials Testing; D008689:Methacrylates / Q000737:chemistry; D008956:Models, Chemical; D010316:Particle Size; D018583:Pliability; D012212:Rheology; D013314:Stress, Mechanical; D013696:Temperature; D013997:Time Factors; D014783:Viscosity
C084111:Charisma composite resin; C112828:Clearfil AP-X; D003188:Composite Resins; D008689:Methacrylates; C039734:Durafill