Diffusion coefficient of water through dental composite resin.
Water sorption of polymer filling materials affects dimensional stability, mechanical properties and bonding strength with tooth structures. To clarify the effect of the degradation on service life and micro-leakage, the diffusion coefficient of water through the resin should be identified. Distributions of time-dependent water concentrations in the resin were computed. Water sorption of composite resin discs with different thicknesses was measured and compared with the solution of Fick's second law. The diffusion coefficient of water through the resin discs was computed to be D=3.9-5.0 x 10(-13)m(2)/s from the measurements of specimens with different thicknesses. Results of water sorption measurements for the discs with different thicknesses were in good agreement with the theoretical results. The relationship among the thickness of the disc, the diffusion coefficient and the water sorption ratio was shown clearly. The testing method for water sorption by International Standard ISO 4049 for resin-based filling materials was discussed.
Asaoka
Kenzo
K
Department of Dental Engineering, School of Dentistry, Tokushima University, 3-18-15 Kuramoto-cho, Tokushima 770-8504, Japan. asaoka@dent.tokushima-u.ac.jp
Hirano
Susumu
S
D003188:Composite Resins / Q000737:chemistry*; D004058:Diffusion; D007700:Kinetics; D013997:Time Factors; D014867:Water
D003188:Composite Resins; D014867:Water