Voids and porosities in class I micropreparations filled with various resin composites.
In this in vitro study, voids inside a minimal occlusal restoration using different consistencies of resin composite and various application techniques were investigated. One hundred and fifty-two simulated, minimally invasive preparations, including a prepared fissure and an excavated carious dentin lesion, were ground in perspex blocks. After applying an acrylic primer (Artglass Connector, Kulzer), the preparations were restored with the adhesive PhotoBond (Kuraray) and one of three resin composites: a packable composite (Prodigy Condensable-Kerr), a syringable composite (Clearfil Photo Posterior, Kuraray) and a flowable composite (Revolution, Kerr). The restorations were inserted according to eight protocols (n = 19). In three groups, the composite was placed in bulk. In another three groups, a layer of flowable composite was placed first, then cured, followed by a second layer of one of the three composites. In two groups, the first layer of flowable composite was left uncured before a second layer of a packable or syringable composite was inserted. The perspex blocks were sectioned and inspected for the presence of voids. Statistical analysis was conducted using Fischer's exact tests at p < 0.05. The results showed that restoring minimal preparations in the absence of porosities and voids was very difficult to achieve. Placing a layer of flowable composite that was left uncured, directly followed by injecting a medium-viscous composite, was the technique that resulted in the most homogeneous restoration.
Opdam
Niek J M
NJ
University of Nijmegen, Department of Cariology and Endodontology, PO Box 9101, NL 6500 HB Nijmegen, The Netherlands. N.Opdam@dent.kun.nl
Roeters
Joost J M
JJ
de Boer
Tim
T
Pesschier
Dennis
D
Bronkhorst
Ewald
E
D003188:Composite Resins / Q000737:chemistry*; D003731:Dental Caries / Q000628:therapy; D003737:Dental Cavity Preparation / Q000145:classification*; D003743:Dental Enamel / Q000648:ultrastructure; D003750:Dental Fissures / Q000628:therapy; D018772:Dental Marginal Adaptation; D003793:Dental Restoration, Permanent; D003804:Dentin / Q000648:ultrastructure; D017220:Dentin-Bonding Agents / Q000737:chemistry; D005899:Glass Ionomer Cements / Q000737:chemistry; D006801:Humans; D016062:Porosity; D019279:Resin Cements / Q000737:chemistry; D012823:Silicate Cement / Q000737:chemistry; D013223:Statistics as Topic; D013499:Surface Properties; D014783:Viscosity
D003188:Composite Resins; D017220:Dentin-Bonding Agents; D005899:Glass Ionomer Cements; C099128:Prodigy; D019279:Resin Cements; C102735:Revolution (composite resin); C111282:dental polyglass; C074669:Clearfil Photo Bond; C092420:Clearfil Photo Posterior; D012823:Silicate Cement