title: [Preparation of calcium phosphate coatings on surfaces of commercially pure titanium induced by simulated body fluid].
abstract: All samples were divided into three groups and subjected to three different surface treatments, i.e. untreated group, group etched with mixed acid of 1:1 HCl and H2SO4 followed by immersion in 6N NaOH solution at 60 degrees C for 24 h and group etched with mixed acid of 1:1 HCl and H2SO4 followed by immersion in 6N NaOH solution at 60 degrees C for 24 h then heated at 600 degrees C for 1 h. After soaked in simulated body fluid for two weeks, a thin calcium phosphate coatings was precipitated on the surfaces of the two treated samples. Results of SEM and EDX showed that calcium phosphate coatings on the surfaces of the titanium samples etched and heated were more even than the titanium samples etched without heating. The analysis of XRD demonstrated the main component of calcium phosphate coating was hydroxyapatite.
authors.affiliation: Department of Prosthodontics, College & Hospital of Stomatology, Wuhan University, Wuhan 430079.
authors.forename: Wei
authors.initials: W
authors.lastname: Deng
authors.forename: Yining
authors.initials: Y
authors.lastname: Wang
authors.forename: Tao
authors.initials: T
authors.lastname: Jiang
authors.forename: Qun
authors.initials: Q
authors.lastname: Chen
authors.forename: Bin
authors.initials: B
authors.lastname: Zhou
authors.forename: Xiangrong
authors.initials: X
authors.lastname: Cheng
mesh_terms: D001826:Body Fluids / Q000737:chemistry*; D002130:Calcium Phosphates / Q000737:chemistry*; D020099:Coated Materials, Biocompatible / Q000737:chemistry*; D066298:In Vitro Techniques; D008422:Materials Testing; D014025:Titanium
chemical_list: D002130:Calcium Phosphates; D020099:Coated Materials, Biocompatible; C485828:alpha-tricalcium phosphate; C485830:tetracalcium phosphate; C485838:calcium phosphate, monobasic, anhydrous; C020243:calcium phosphate; D014025:Titanium; C485829:calcium phosphate, dibasic, anhydrous