Photoelectrocatalytic degradation of 4-chlorophenol and oxalic acid on titanium dioxide electrodes.
Photocatalytically active thin TiO(2) films were produced by spin-coating or dip-coating an alkoxy precursor onto a transparent conducting electrode substrate and by thermal oxidation of titanium metal. The thin films were used to study the photoelectrocatalytic or photoelectrochemical degradation of oxalic acid and 4-chlorophenol (4-CP) under near UV (monochromatic, 365 nm) light irradiation. Degradation was monitored by a variety of methods. In the course of oxalic acid degradation, CO(2) formation accounted for up to 100% of the total organic carbon degradation for medium starting concentrations; for the degradation of 4-CP, less CO(2) was detected due to the higher number of oxidation steps, i.e. intermediates. Incident-photon-to-current conversion efficiency, educt degradation and product formation as well as Faradaic efficiencies were calculated for the degradation experiments. Quantum yields and Faradaic efficiencies were found to be strongly dependent on concentration, with maximum values (quantum yield) around 1 for the highest concentrations of oxalic acid.
Waldner
G
G
Institute of Materials Chemistry, Vienna University of Technology, Veterinärplatz 1, A-1210 Vienna, Austria. gwaldner@mail.zserv.tuwien.ac.at
Pourmodjib
M
M
Bauer
R
R
Neumann-Spallart
M
M
D002384:Catalysis; D002733:Chlorophenols / Q000737:chemistry*; D004396:Coloring Agents / Q000737:chemistry*; D004563:Electrochemistry; D004566:Electrodes; D008962:Models, Theoretical; D019815:Oxalic Acid / Q000737:chemistry*; D010777:Photochemistry; D019163:Reducing Agents / Q000737:chemistry*; D014025:Titanium / Q000737:chemistry*
D002733:Chlorophenols; D004396:Coloring Agents; D019163:Reducing Agents; C009495:titanium dioxide; C029107:4-chlorophenol; D019815:Oxalic Acid; D014025:Titanium