title: [A surface reacted layer study of titanium-zirconium alloy after dental casting].
abstract: OBJECTIVE
  To investigate the influence of the mold temperature on the surface reacted layer of Ti-Zr alloy castings.
  
  
  METHODS
  Ti-Zr alloy was casted into a mold which was made of a zircon (ZrO2.SiO2) for inner coating and a phosphate-bonded material for outer investing with a casting machine (China) designed as vacuum, pressure and centrifuge. At three mold temperatures (room temperature, 300 degrees C, 600 degrees C) the Ti-Zr alloy was casted separately. The surface roughness of the castings was calculated by instrument of smooth finish (China). From the surface to the inner part the Knoop hardness and thickness in reacted layer of Ti-Zr alloy casting was measured. The structure of the surface reacted layer was analysed by SEM. Elemental analyses of the interfacial zone of the casting was made by element line scanning observation.
  
  
  RESULTS
  The surface roughness of the castings was increased significantly with the mold temperature increasing. At a higher mold temperature the Knoop hardness of the reactive layer was increased. At the three mold temperature the outmost surface was very hard, and microhardness data decreased rapidly where they reached constant values. The thickness was about 85 microns for castings at room temperature and 300 degrees C, 105 microns for castings at 600 degrees C. From the SEM micrograph of the Ti-Zr alloy casting, the surface reacted layer could be divided into three different layers. The first layer was called non-structure layer, which thickness was about 10 microns for room temperature group, 20 microns for 300 degrees C and 25 microns for 600 degrees C. The second layer was characterized by coarse-grained acicular crystal, which thickness was about 50 microns for three mold temperatures. The third layer was Ti-Zr alloy. The element line scanning showed non-structure layer with higher level of element of O, Al, Si and Zr, The higher the mold temperature during casting, the deeper the Si permeating and in the second layer the element Si could also be found.
  
  
  CONCLUSIONS
  The mold temperature is one of the major factors influencing to casting quality. In order to reduce the surface reacted layer of Ti-Zr alloy castings, the lower mold temperature and the investment without Si should be chosen.
authors.affiliation: Fourth Military Medical University.
authors.forename: Y
authors.initials: Y
authors.lastname: Zhang
authors.forename: T
authors.initials: T
authors.lastname: Guo
authors.forename: Z
authors.initials: Z
authors.lastname: Li
authors.forename: C
authors.initials: C
authors.lastname: Li
mesh_terms: D003722:Dental Alloys / Q000737:chemistry*; D003735:Dental Casting Technique; D013499:Surface Properties; D013696:Temperature; D014025:Titanium / Q000737:chemistry*; D015040:Zirconium / Q000737:chemistry*
chemical_list: D003722:Dental Alloys; D015040:Zirconium; D014025:Titanium